Cu含量对Sm2Co17型烧结磁体工作温度的影响

采用粉末冶金法制备烧结Sm(Co1-u-v-wFeuCuvZrw)7.5(v=0.05~0.08)材料,研究了Cu含量对材料内禀矫顽力及其温度系数的影响,进而探讨了Cu含量对材料工作温度的影响。结果表明,Cu的添加对材料的内禀矫顽力有显著影响,而对材料Hcj温度系数无明显影响(-0.2~-0.3%/℃)。提高Cu含量有利于提高材料的Hcj,但将降低其剩磁Br。v=0.08的材料350℃下B-H退磁曲线仍保持直线,性能达到Br=0.92T,Hcb=620kA/m,Hcj=856kA/m,(BH)max=143kJ/m3,可满足350℃工作温度的特定使用要求。     

Sm2Co17稀土永磁材料的研究概况

随着现代工业的发展,对永磁体的要求也越来越高,既要求磁性能优良,又要求稳定性好,可靠性高.目前,对Sm2Co17稀土永磁材料的研究主要体现在高温永磁体、高稳定性永磁体和成型工艺等方面.影响Sm2Co17磁体性能的因素较多,其中比较重要的因素是磁体的显微组织、时效处理及合金的化学成分等.     

无槽永磁直线同步电动机永磁体对电磁推力的影响

建立无槽式永磁直线同步电动机分层解析模型,以矢量磁位作为求解变量得到励磁磁场和电枢反应磁场的二维解。分析该电机永磁体结构对电磁推力的影响。用有限元法验证解析结果,两种方法所得结果吻合较好,表明方法可行。     

超强大型永磁除铁器的开发及应用

探讨了超强大型永磁除铁器的开发应用,论述了永磁材料的性能和应用,介绍了RCYA-20超强除铁器的工作原理、产品特点、主要参数、综合评价。     

几种常见介质对NdFeB磁体的腐蚀研究

采用失重法,分别在空气、自来水、氯化钠溶液、硫酸溶液及氢氧化钠溶液等几种常见介质中,对NdFeB磁体不同温度下的腐蚀情况进行了研究。结果表明:在同种介质中,NdFeB磁体的腐蚀速率随温度的升高而加快;pH值较小时,腐蚀严重;而当溶液的pH值增加时,样品的腐蚀速率减缓;当pH>10时,样品的质量基本不减少;pH>12,θ>25℃时,样品表面会形成碱式化合物,总质量增加,样品几乎不再受到腐蚀。     

铝薄膜对烧结NdFeB磁体耐蚀性能的影响

采用直流磁控溅射的方法在烧结NdFeB磁体表面沉积Al薄膜提高磁体的耐蚀性能。研究膜厚及溅射功率对薄膜结构和耐蚀性能的影响。利用SEM对Al薄膜的微观结构进行分析,并采用动态极化曲线和中性盐雾实验分析Al薄膜耐蚀性能。均匀致密的Al薄膜的形成是获得良好耐蚀性能的必要条件。在51-82 W溅射功率下制备的6.69μm的Al薄膜具有良好的耐蚀性能。     

前处理工艺对NdFeB表面真空蒸镀Al薄膜结构及性能的影响

为了开发烧结钕铁硼磁体表面低损伤、环境友好型镀膜前处理工艺,在分别采用抛光、酸洗(50 s)、吹砂、吹砂+酸洗(5 s)4种不同工艺处理的烧结NdFeB磁体表面真空蒸镀Al薄膜。经不同工艺前处理的NdFeB基体和涂层的形貌采用扫描电子显微镜进行观察;采用拉伸试验对Al涂层和基体之间的结合力进行测试;NdFeB基体的自腐蚀行为采用电化学极化曲线进行表征。结果表明:吹砂前处理后NdFeB基体表面存在一层晶粒损伤层,导致镀Al薄膜试样镀层与基体之间的结合力(9.54 MPa)最差。而采用吹砂+酸洗(5 s)前处理后NdFeB表面镀Al试样镀层与基体之间结合力可达13.58 MPa。酸洗(50 s)及喷砂+酸洗(5 s)前处理后基体试样的自腐蚀电流密度基本相同(21μA·cm~(-2)),仅为抛光及喷砂前处理基体试样的20%。在4种工艺当中,吹砂+酸洗(5 s)前处理工艺获得最高的结合力和优异的耐腐蚀性能。     

Possible methods of recycling NdFeB-type sintered magnets using the HD/degassing process

With the rapid growth in the use of NdFeB-type magnets and with the growing environmental need to conserve both energy and raw materials, the recycling of these magnets is becoming an ever important issue. In this paper it is demonstrated that hydrogen could play a vital role in this process. Fully dense sintered NdFeB-type magnets have been subjected to the hydrogen decrepitation (HD) process. The resultant powder has been subsequently processed in one of two ways in order to produce permanent magnets. Firstly, the powder was subjected to a vacuum degassing treatment over a range of temperatures up to 1000 °C in order to produce powder that would be suitable for the production of anisotropic bonded or hot pressed magnets. Secondly, the HD-powder has been used to produce fully dense sintered magnets; in which case optimisation of the milling time, sintering temperature and time was carried out. The optimum degassing temperature for coercive powder was found to be 700 °C, giving powder with a remanence (Br) of 1350 mT (±50 mT) and an intrinsic coercivity (Hcj) of 750 kA m⁻¹ (±50 kA m⁻¹). The best sintered magnet was produced by very lightly milling the powder (30 min, roller ball mill), aligning, pressing and vacuum sintering at 1080 °C for 1 h. The magnetic properties of this magnet were: (BH)_max = 290 kJ m⁻³ (±5 kJ m⁻³), Br = 1240 mT (±50 mT) and Hcj = 830 kA m⁻¹ (±50 kA m⁻¹); representing decreases of 15%, 10% and 20%, respectively, from the properties of the initial magnet.     

熔体温度对快淬法制备纳米晶复合Nd_(8.5)Fe_(77)Co_5Zr_3B_(6.5)合金微观结构和磁性能的影响

将Nd_(8.5)Fe_(77)Co_5Zr_3B_(6.5)(at%)合金熔化至不同温度后,以18 m/s的甩带速度快淬,对淬态条带进行了退火处理,分析了其微观结构和磁性能的变化。结果表明,熔体温度对淬态及其退火态合金的微观结构和磁性能可以产生重要影响,熔体温度为1210℃时制备的快淬条带由Nd_2Fe_(14)B相和部分非晶相组成,具有一定的硬磁性;随着快淬时熔体温度的升高,淬态条带中非晶相的质量分数逐渐增加,其磁性逐渐转变为软磁性。几种合金经退火处理后均由大量Nd_2Fe_(14)B相与少量软磁相组成,熔体温度较低的合金退火后其晶粒尺寸较小,磁性能较好。熔体温度为1210℃时制备的合金退火后磁性能最佳,内禀矫顽力Hci为559.2 kA/m,剩余磁化强度Br为0.98 T,最大磁能积(BH)_(max)为127.8 kJ/m~3。     

菱镁矿浮选尾矿直接合成同时制备镁橄榄石和镁砂研究

为了有效利用菱镁矿浮选尾矿废弃物,提出以其为原料,在不添加任何物质、不经过高压压制成型的条件下直接烧制同时制备优质镁橄榄石和烧结镁砂的技术路线,并在高温管式炉中对其可行性进行了实验研究。通过对不同反应温度和时间条件下制备的样品进行XRD和SEM-EDS表征和分析,确认新技术路线不仅可行,并且还具有反应速度快、产品质量优等优势。当反应温度为1400℃及以上时,原料中的SiO₂在数分钟之内全部转化,产物镁橄榄石和烧结镁砂晶体发育良好。研究结果对进一步开发菱镁矿浮选尾矿废弃物高效利用新技术提供有力支持。