Characterization and application of polypropylene films modified with stimuli‐sensitive copolymers with an Ar‐plasma postpolymerization technique

Surface‐modified polypropylene (PP) films with thermally and photochemically sensitive copolymers consisting of N‐(2‐hydroxypropyl)methacrylamide (HPMA) and 4‐(4‐methoxyphenylazo)phenyl methacrylate (MPAP), poly(HPMA‐co‐MPAP)‐g‐PP (abbreviated g‐PP) film, were prepared by graft copolymerization with an Ar‐plasma postpolymerization technique. The surfaces of the g‐PP films were characterized by means of X‐ray photoelectron spectroscopy; the percentage grafting of poly(HPMA‐co‐MPAP) with a number‐average molecular weight of 3.28 × 10⁴ was 7.12%, and the molar ratio of HPMA–MPAH in the copolymer was 0.75:0.25. The stimuli‐sensitive adsorption of albumin and polystyrene microspheres on the g‐PP film was also measured. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 143–148, 2003     

Effect of crystallization and interface formation mechanism on mechanical properties of film‐insert injection‐molded poly(propylene) (PP) film/PP substrate

A previous study has shown that the adhesion between the film and substrate of film‐insert injection‐molded poly(propylene) (PP) film/PP substrate was evident with the increases in barrel temperature and injection holding pressure. In this second part of the research work, the crystallinity at the interfacial region (i.e., region between the film and the injected substrate) was extensively studied using FTIR imaging, polarized light microscopy, and DSC in an attempt to determine the level of influence that crystallinity has on the interface and bulk mechanical properties. Consequently, a more thorough and clearer picture of the influence of the inserted film on the interfacial crystallinity and subsequently the substrate mechanical properties, such as peel strength and impact strength, has been revealed. The initial proposition that crystallinity could enhance film–substrate interfacial bonding has been confirmed, judging from the higher peel strength with increasing crystallinity at the interfacial region. Nevertheless, the change in crystallinity was not only confined to the interfacial region. With the film acting as heat‐transfer inhibitor between the injected resin and the mold wall, the total crystal structure of the substrate was substantially altered, which subsequently affected the bulk mechanical properties. The lower impact strength of film‐insert injection‐molded samples compared to that of samples without film inserts provided evidence of how the film could impart inferior properties to the substrate. The difference in cooling rate between the substrate and film might also cause other defects such as warpage and/or residual stress build‐up within the product. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 294–301, 2005     

Cyclic oxidation processes during anodizing of Al-Cu alloys

The influence of copper on the morphologies of porous anodic alumina has been investigated under current and voltage control using a sputtering-deposited Al-2.7 at.% Cu alloy and a commercial AA 2024-T3 aluminium alloy anodized in either sulphuric acid electrolyte or the same electrolyte but with addition of tartaric acid. The findings indicate that film development involves repeated formation of embryo cells of anodic alumina at the metal/film interface. During the initial stages of anodizing at constant voltage, cell formation is accompanied by current peaks in the current-time response. The porosity of the resultant films has a lateral aspect due to the layering of embryo cells. The thickness of individual layers is proportional to the formation voltage, with a ratio of the order 1 nm V⁻¹. The cell formation is accompanied by enrichment of copper in the alloy, incorporation of copper species into the anodic film, in low amounts relative to the alloy, and evolution of oxygen. These processes disrupt the formation of the classical pore morphology, characteristic of high purity aluminium, due to continuous formation of fresh embryo cells and re-direction of pores. The main effect of the tartaric acid addition to the sulphuric acid was to reduce the rate of anodizing of the alloys at constant voltage by about 10-20%.     

Protecting biodegradable coatings releasing antimicrobial agents

This article describes the synthesis and in vitro analysis of poly(ester anhydride) antimicrobial protection coatings. Poly(ester anhydride)s composed of ricinoleic acid, sebacic acid, terephthalic acid, and isophthalic acid were used in this study. The polymers were compatible with various fillers commonly used in paint preparation. The in vitro experiments showed that the polymers are able to release diuron, an antimicrobial agent, for months. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Conjugate heat transfer in turbulent falling liquid films

Heat transfer characteristics for a falling turbulent liquid film flow over a fin are analyzed using the conjugate convection-conduction theory. Numerical results are obtained from a simultaneous solution of the energy equations of the fluid and the fin. Results are presented for the fin temperature distribution, dimensionless heat transfer coefficients, local heat fluxes, and fin efficiencies.     

Fundamental Optical Absorption Edge of Sputter-Deposited Zirconia and Yttria

Zirconia and yttria films were sputter deposited onto unheated fused silica substrates using a metal target and rare gas-oxygen discharges. Double-beam spectrophotometry was used to measure the transmission and reflection as a function of incident photon energy, E , from which the absorption coefficient, α( E ), was calculated. An indirect interband transition at E _i= 4.70 eV and two direct interband transitions at E _g1= 5.17 eV and E _g2= 5.93 eV occur in monoclinic zirconia. Two direct interband transitions at E _g1= 5.07 eV and E _g2= 5.73 eV occur in cubic yttria. The absorption edge structure is modified when unusual phases, such as tetragonal zirconia, and zirconia and yttria with no longrange crystallographic order, are present.     

微波铁氧体器件薄膜的制备及性能研究

该文采用RF磁控溅射工艺制备了射频薄膜电感用的铁氧体薄膜。为了降低铁氧体薄膜在高频下的涡流损耗、剩余损耗等,通过对铁氧体材料的磁特性分析,研究了不同的温度、成分掺杂对铁氧体磁性能的影响,获得了矫顽力为5.619 6Guss的铁氧体薄膜,并采用SEM、XRD对铁氧体薄膜表面结构进行了表征,采用VSM对薄膜磁性能进行了测试。     

Additive-aided electrochemical deposition of bismuth telluride in a basic electrolyte

A new basic electrolyte with two cationic plating additives,polydiaminourea and polyaminosulfone,was investigated for the electrochemical deposition of the bismuth telluride film on a nickel-plated copper foil.Tellurium starts to deposit at a higher potential(-0.35 V) than bismuth(-0.5 V) in this electrolyte.The tellurium-to-bismuth ratio increases while the deposition potential declines from-1 to-1.25 V, indicating a kinetically quicker bismuth deposition at higher potentials.The as-deposited film featu...     

反应性乳化剂在乳液保护膜压敏胶中的应用

选择阴-非离子反应性乳化体系,通过乳液聚合,制备了丙烯酸酯乳液保护膜压敏胶．对压敏胶的物理性能、粘合性能、保护膜胶层的抗转移能力以及胶膜的耐水性能进行了测试,并与采用非反应性乳化体系制得的具有相同单体组成的保护膜压敏胶进行了对比分析．结果表明：使用反应性乳化剂能明显改善胶膜的耐水性、提高胶层的抗转移能力,并能获得综合性能良好的保护膜乳液压敏胶．     

Investigations of ZnO thin films deposited by a reactive pulsed laser ablation

Highly transparent ZnO thin films were deposited at different substrate temperatures by pulsed laser deposition in an oxygen atmosphere. The thin films were characterized by various techniques including X-ray diffraction, scanning electron microscopy, optical absorption, and photoluminescence. We demonstrated that oriented wurtzite ZnO thin films could be deposited at room temperature using a high purity zinc target. Variable temperature photoluminescence revealed new characteristics in the band edge emission. The underlying mechanism for the observed phenomena was also discussed.