选用不同结构的多元醇作骨架，合成一系列高性能的聚氨酯丙烯酸树脂，并通过对聚氨酯丙烯酸树脂性能的对比研究，发现以聚丁二烯二元醇为骨架的聚氨酯丙烯酸酯树脂具有极佳的柔韧性和优异的低温耐曲折性。     

低密度泡沫玻璃的研究与应用

低密度泡沫玻璃是利用碎玻璃制造的一种气孔率大于90%的隔热保温材料,它具有强度高、导热系数小、吸水率低、不吸湿、耐腐蚀等特性,在潮湿环境下抗冻性能好,是一种优良的低温、超低温隔热保温材料。该产品用途广泛,所用的原材料简单易得,但生产工艺过程比较复杂,生产过程控制精度要求较高,容易产生各种缺陷而影响产品的质量。本文对低密度泡沫玻璃的生产工艺过程进行详细的分析研究,提出相应的措施,确保产品的低密度和高成品率,提高产品的性能,扩大产品的使用范围。     

近十年常温干法精脱硫专利技术发展动态

收集了近十年来国内的常温干法精脱硫专利，并分类列举出各种脱硫剂的物化性质和几种常温精脱硫工艺，重点阐述了该技术的优缺点及其未来发展方向。     

High temperature polymerization of propylene catalyzed by MgCl2‐supported Ziegler–Natta catalyst with various cocatalysts

Four cocatalysts, referred to as ethylaluminoxanes, were synthesized by the reaction between triethylaluminium (AIEt₃) and water under various molar ratios of H₂O/Al at ?78°C. Aluminoxanes were used as cocatalysts for a MgCl₂‐supported Ziegler–Natta catalyst for propylene polymerization at temperatures ranging from 70 to 100°C. When the polymerization was activated by AlEt₃, the activity as well as the molecular weight and isotacticity of the resulting polymer gradually dropped as the temperature varied from 70 to 100°C. When ethylaluminoxane was employed as the cocatalyst, good activity and high molecular weight and isotacticity were obtained at 100°C. Furthermore, when the cocatalyst varied from AlEt₃ to ethylaluminoxane, the atactic fraction and polymer fraction with moderate isotacticity decreased and the high isotactic fraction slightly increased, which indicated that the variation of the cocatalyst significantly affects the isospecificity of active sites. It was suggested that the reactivity of the Al‐Et group and the size of the cocatalyst were correlated to the performance of the Ziegler–Natta catalyst at different temperatures. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 1978–1982, 2006     

Effect of Twin-Plane Reentrant Edge on the Coarsening Behavior of Barium Titanate Grains

When BaTiO₃ ceramics were sintered at relatively low temperatures (≤1250°C), the grains with reentrant edges caused by a (111) double twin grew exclusively. As a result, a microstructure with a bimodal grain-size distribution composed of platelike large grains and fine matrix grains was obtained. In contrast, at the usual sintering temperature between 1250° and 1350°C, grains containing a (111) double twin did not exhibit any growth advantage. In this case, a coarse and uniform microstructure was obtained. When this coarse-grained specimen was further heat-treated at 1365°C, the grains possessing a double twin were observed to grow exclusively again. The results were explained in terms of a coarsening process controlled by two-dimensional nucleation.     

A203型低温氨合成催化剂使用小结

对Ａ２０３型低温氨合成催化剂的使用进行总结，介绍了该催化剂的装填，升温还原情况及使用效果。     

高效防腐中温磷化液LC-1的制备及性能

制备了一种含Zn2+、Mn2+、N i2+三系离子的LC-1磷化液,通过硫酸铜点滴、氯化钠浸蚀、SEM等手段对磷化膜进行了测试,测定了磷化温度、磷化时间对膜层耐蚀性的影响。结果表明,在磷化温度大于65℃,磷化时间大于10 m in的条件下,所形成的磷化膜结晶均匀、致密、黑褐色,耐蚀性良好。LC-1三系磷化液可适用于大批量钢铁工件的磷化生产。     

Bubble temperature data for phenol-alcohol systems: Phenol-I-Amyl alcohol and phenol-n-Amyl alcohol systems

In order to supplement the literature data on VLE, isobaric bubble temperature data were collected for the binary systems phenol-i-amyl alcohol and phenol-n-amyl alcohol over the entire composition range by indirect method using a standard Swietoslawski type ebulliometer. The measurements were made at three sub-atmospheric pressures. The experimental t-x data were correlated with both equation of state method and gamma-phi methods. In the former approach, the Soave equation of state is used, whereas in the latter case Wilson, NRTL and UNIQUAC equations are used.     

混合物MH-81状态方程的研究——从无限稀释活度系数预测混合物汽液平衡

本文由无限稀释活度系数求取混合物MH-81状态方程的二元相互作用参数,预测了二元混合物的汽液平衡,获得了较满意的结果。     

电子陶瓷和器件的低温共烧技术

较系统地介绍了电子器件用低温共烧陶瓷(low temperature cofired ceramics,LTCCs)材料,探讨了其工艺中的若干问题。电子器件用低温共烧陶瓷材料包括:玻璃/陶瓷复合材料、结晶化玻璃、晶化玻璃/陶瓷复合材料以及液相烧结陶瓷,其中典型的和最为常用的LTCCs为玻璃/陶瓷(特别是氧化铝)复合材料。正在研究的一些陶瓷介质材料中,Bi基介质材料引起了人们的关注。玻璃/陶瓷复合材料的制备工艺中,应当着重关注和加深了解玻璃的流动性和结晶性、玻璃的起泡、玻璃和陶瓷颗粒间的反应、共烧材料的匹配等问题,从优选材料配方和优化工艺着手,从而获得优质可靠的材质和器件。