Experimental and numerical investigation of fracture in double-edge notched steel plates

Double-edge notched (DENT) steel plates were pulled until complete fracture and several experimental observations were made (using profilometry and scanning electron microscopy). The essential work of fracture (EWF) model was found to be well verified. Numerical simulations—up to the maximum load only—of some experiments were performed using the finite element method (FEM), and incorporating geometric and material non-linearities (large deformation elasto-plasticity). Some experimental measurements were compared with the corresponding numerical computations and excellent agreement was found.     

氧化铝/锌合金复合材料界面的SEM观察

利用挤压铸造制备氧化铝／锌合金复合材料，在扫描电镜（ＳＥＭ）上观察复合材料的界面。结果表明，在复合材料中纤维与基体间存在致密界面层，合金元素通过适当的化学反应可改善纤维与基体间的结合；在凝固过程中，纤维／基体界面上的硅在共晶体的共生生长过程中起了领先相作用，导致复合材料的共晶转变是由铝硅共晶转变和锌铝共晶转变两者组成。     

PVDF中空纤维滤膜的形态结构

用Ｌ－Ｓ相转换法制备了聚偏氟乙烯（ＰＶＤＦ）中空纤维不对称滤膜。铸膜液由聚合物、溶剂和添加剂组成。用电子显微镜（ＳＥＭ）考察了聚合物浓度、添加剂用量及种类对膜形态结构的影响。实验结果表明，聚合物浓度对膜形态结构有显著影响，当铸膜液中聚合物浓度较低时，无论用什么种类添加剂，都能形成大、且多的孔，但孔的形状随添加剂不同而异。当恒定聚合物浓度时，添加剂的用量对膜形态结构有很大的影响，但孔的大小及多少与添加剂含量的多少不成正比。     

Theoretical Analysis of Critical period in Microbend Fiberoptic Sensor

1IntrodctionThesdV8fltsg6Sofffi1CY0bCfldf山CY0ptlCS6fiS0f8f6lflt6llSltyffiDdU18tlflgsliddCtCCtlflg，simpletechnique，highrellabllltyandlowprice，thereformlcrobendfiberoptlcsensorIswidelyusedtomeasurementofstrain，stressandv比rationetc．Inpractice，thesensltlvltyofsensorIsaveryimportantparameter，andthesensltlvltyofmlcrobendf山eroptlcsensorIsmainlyrelat-6dtofoil0WlflgthY66f8CtofS［‘-：ffilCfob6fldsffiplltlld6：fillffib6yofthlCY0b6fldS6Ct10llSsfldffil-crobendperiod，andmlcrobendperio…     

简易炉外处理在电炉钢生产中的应用

阐述了小电炉采用投资少，见较快，简单易行的炉外处理措施，提高了钢质量和生产率，生产实践和应用结果表明，本措施可为同类型企业的炼钢工艺完善和技术进步提供参考。     

THE FRACTURE MECHANISM OF 475°C EMBRITTLEMENT IN A DUPLEX STAINLESS STEEL

The mechanism of “475°C embrittlement” of a duplex stainless steel was investigated using finite element modelling of the stress distribution at brittle fracture initiation. Brittle fracture initiated at a critical shear stress, which increased with ferrite hardness. The fracture stress was affected by the duplex microstructure. Fracture was nucleated by deformation twins, which were identified using electron back-scatter diffraction. The ductile-to-brittle fracture transition was sensitive to age-hardening and could be described simply by the effect of age-hardening and test temperature on the yield stress.     

Failure analysis of a wire rope

Wire ropes, pulleys, counterweights, and connecting systems are used for auto tensioning of contact wires of electric railways. A wire rope in one such auto tensioning system suffered premature failure. Failure investigation revealed fatigue cracks initiating at nonmetallic inclusions near the surface of individual wire strands in the rope. The inclusions were identified as Al-Ca-Ti silicates in a large number of stringers, and some oxide and nitride inclusions were also found. The wire used in the rope did not conform to the composition specified for AISI 316 grade steel, nor did it satisfy the minimum tensile strength requirements. Failure of the wire rope was found to be due to fatigue; however, the ultimate fracture of the rope was the result of overload that occurred after fatigue failure had reduced the number of wire strands supporting the load.     

单模光纤最小群速度色散波长附近的调制不稳定性

利用修正的非线性Ｓｃｈｒｏｄｉｎｇｅｒ方程研究了单模光纤最小群速度色散波长附近的调制不稳定性，发现了一个新的由光纤四色散导致的调制不稳定性区域，该区域的调制范围与初始入射脉冲的功率和四阶色散有关。     

广州中城广场主体工程施工技术

广州中城广场工程结构形式复杂，平面曲折多角。施工中在应用多种模板体系、泵送混凝土、无粘结预应力楼板及核心筒部分小平台滑模等方面，采用了多项新技术，保证了工程质量，加快了工程进度。     

含羧基的聚乙烯醇胺肟螯合纤维吸附钯的研究

研究了含羧基的聚乙烯醇胺肟（ＰＶＡＡＯ－ＡＡｃ）螯合纤维对钯的吸附，讨论了ｐＨ、温度、浓度、吸附时间对吸附率及回收率的影响。确定了最佳吸附条件，吸附钯的纤维用５％硫脲＋０．１０ｍｏｌ／Ｌ硝酸溶液可以解吸。