Sol-gel Preparation and Preliminary in vitro Evaluation of Fluorapatite／Hydroxyapatite Solid Solution Films

Fluorapatite/hydroxyapatite solid solution has better biological properties than other apatites, especially used as films or coatings. In this work, sol-gel preparation and in vitro behavior of fluorapatite/hydroxyapatite solid solution films on titanium alloy were investigated. Ca(NO3)2-4H20 and PO(OH)x(OEt)3-x were selected as precursors, and hexafluorophosphoric acid (HPFo) was used as a fluorine containing reagent. The Ca and P precursors were mixed with HPFo to keep the Ca/P molar ratio 1.67. The mixtures refluxed for 12 h were used as dipping sols for the preparation of the films. The phase of the films obtained at 600℃ was apatite. The F contents in the films increased with the concentrations of HPF6 in the dipping sols. The solid solution films were shown to have better stability than hydroxyapatite films, and a reasonably good bioactivity in the in vitro evaluation.     

抗热震抗强腐蚀坩埚的研制

本研究以氧化铝为基相,采用复相技术,加入磷酸锆低膨胀相及中间过渡相,提高材料的抗热震性,使氧化铝—磷酸锆复相材料坩埚不仅稳定抗腐蚀性好,同时具有良好的抗热震性,提高了使用寿命。     

预应力混凝土肋加气块复合屋面板制作与屋面施工

1 概况预应力混凝土肋加气块复合屋面板(以下简称复合屋面板)是集承重、隔热、保温为一体的一种新型屋面板。上海地区自1986年始初次设计复合屋面板时采用的是高200mm的预应力混凝土肋、在肋间填充加气块的方式。该板面分有盖与无盖两种(即板面加与不加钢筋网片细石混凝土),经过试点工程实践均取得成功,于1988年通过上海市级技术鉴定。     

丙烯酸酯聚氨酯紫外固化凝胶生成动力学研究

采用丙烯酸酯聚氨酯和二苯甲酮/安息香乙醚复合光敏剂,对该体系紫外光固化反应的凝胶生成动力学进行分析。用红外光谱定量测定光聚合过程的变化,发现光聚合反应主要是以双键打开,交联为特征的,并得出1408cm~(-1)双键吸收峰随光照时间而变化的关系式:P_(c=c)=0.325 t~(0.135)。临界凝胶点可由双键反应程度与凝胶分数之间关系外推得到,凝胶点后,体系中存在一个凝胶与溶胶之间分配关系,此时凝胶与溶胶共存,凝胶中双键反应程度P_(A(g))>总双键反应程度P_A>溶胶中双键反应程度P_(A(S))。随着凝胶增加,P_A和P_(A(g))逐渐上升,而P_(A(s))下降。此体系的紫外固化实验工作曲线与理论值基本一致。     

溶胶—凝胶法莫来石被覆SiC复合微粒子的制备

本文采用溶胶－凝胶法以组成为３Ａｌ２Ｏ３．２ＳｉＯ２的混合溶胶分别于和压力条件下，对ＳｉＣ微细粉进行包覆处理，该涂覆层在低于１０００℃下经１ｈ热处理可结晶成莫来石层，研究了涂覆溶胶浓度、涂覆压力对涂层厚度、结晶化温度等的影响，涂覆后的ＳｉＣ微粉在中高温的表面抗氧化性明显提高。     

溶胶－凝胶法制备Pb（Zr，Ti）O_3玻璃陶瓷过程中的结构变化

本文介绍溶胶－凝胶法制备均匀ＰｂＺｒ－Ｔｉ－Ｂ－Ｓｉ凝胶玻璃，并通过适当热处理在凝胶玻璃中原位生长Ｐｂ（Ｚｒ；Ｔｉ）Ｏ３微晶的新工艺·利用ＩＲ谱考察了凝胶玻璃中的元素键合结构随温度的变化．结合热分析和ＸＲＤ；ＳＥＭ技术，研究了Ｐｂ（Ｚｒ，Ｔｉ）Ｏ３微晶在凝胶玻璃中的生长过程及该材料的结构特点．发现Ｐｂ２（Ｚｒ，Ｔｉ）２Ｏ６＋ｘ立方焦绿石介稳过渡相的纳米微晶首先出现于该体系中，并在更高的温度下先后完全转变成三方和四方Ｐｂ（Ｚｒ，Ｔｉ）Ｏ３钙钛矿相．电子显微观察结果表明，该工艺制备的Ｐｈ（Ｚｒ；Ｔｉ）Ｏ３玻璃陶瓷具有均匀的细晶结构．     

膨润土凝胶调剖剂XJF的研制及应用

介绍了调剖剂XJF的配方,讨论了影响调剖剂性能的配方因素(膨润土含量、HPAM溶液浓度、XJ用量及添加剂Fc的浓度),考察了封堵能力和应用范围,简介了在火烧山油田现场试验的结果。     

在聚合物驱和水驱中窜流与层间渗透率差异对凝胶处理效果的影响

本文对用凝胶封堵高渗层效果做了模拟研究，所选模型是由两个独立的均质层组成，每层渗透率在纵向上均是各向同性。层间水平渗透率比为０．００３３－０．５，两层的垂直／水平渗透率比相同且为０．００１－０．１。先将凝胶注入到高渗透的深层中，再在每层中注入聚合物和水，每层流度不同，注入到各层中的量亦不同，由于改善了注入剖面，从而降低了垂直／水平渗透率比，所以在井筒附近用凝胶封堵高渗层可提高原油采收率。相同条件下