Two-step flotation recovery of iron concentrate from Donganshan carbonaceous iron ore

The flotation of pure and natural carbonaceous iron ore samples in the oleate flotation system was investigated. Starch can depress hematite effectively in a wide pH range, but cannot depress siderite efficiently in neutral conditions. The flotation recovery of pure hematite, siderite, and quartz in the oleate-starch-CaCl₂ system is significantly different when the slurry pH varies from 4 to 12. A novel two-step flotation process was developed for the separation of iron concentrate from Donganshan carbonaceous iron ore through which the siderite concentrate is first recovered and the high quality hematite concentrates with relative high iron recovery can be obtained in the second step flotation. The siderite concentrate may be utilized directly or undergo further concentration steps to increase iron grade.     

Effects of yttrium on the formation and magnetic properties of bulk metallic glassy （Fe, Co）-B-Si-Nb alloys

The bulk metallic glassy (BMG) rods of [(Fe0.5Co0.5)0.72B0.192Si0.048Nb0.04]100-xYx (x=0-6) and [(FexCo1-x)0.72B0.192Si0.04]Nb0.04]96Y4 (x=0.5-0.8) were prepared by copper mold casting. The structure, thermal stability,and magnetic properties of the samples were studied by X-ray diffraction (XRD), differential scanning calorimetry (DSC), and vibrating sample magnetometer (VSM). Adding lat% to 6at% of yt-trium, the bulk glassy alloy rods of [(Fe0.5Co0.5)0.72B0.192Si0.048Nb0.04]100-xYx (x=0-6) with the diameter of 3 mm were not formed, and the sample with 4at% of yttrium showed less crystalline phase than others. When the Fe/Co atomic ratio was between 5:5 and 7:3, the bulk glassy alloy rods of [(Fe1-xCox)B0.192Si0.048Nb0.04]96Y4 (x=0.5-0.8) with the diameter of 2 mm were fabricated. In the (Fe, Co)-B-Si-Nb-Y BMGs, when the Fe content increased, the thermal stability, the supercooled liquid region, and the glass-forming ability (GFA) decreased, but the saturation magnetization (Ms) increased.     

Dependence of domain wall structures on repetition n in[Pt（0.5 nm）/Co（0.4 nm）]n/NiO（1.1 nm）/[Co（0.4 nm）/Pt（0.5 nm）]n multilayers

The magnetic force microscopy and a sample vibrating magnetometer have been used to investigate the domain structure in two antiferromagnetically coupled Co/Pt multilayers.In the antiferromagnetic coupled[Pt(0.5 nm)/Co(0.4 nm)]_n/NiO(1.1 nm)/[Co(0.4 nm)/Pt(0.5 nm)]_n multilayers with perpendicular anisotropy,the antiferromagnetic interlayer coupling strength increases linearly with the repetition number n in Co/Pt multilayers.In demagnetized states,relatively shifted domain walls in the two Co/Pt multila...     

邻苯三酚红-溴化十六烷基吡啶分光光度法测定农业样品中铁

对铁 ( )与邻苯三酚红的显色反应条件进行了研究。在溴化十六烷基吡啶存在下 ,于 p H 5 .0的乙酸-乙酸钠缓冲介质中 ,铁 ( )与邻苯三酚红形成绿色配合物 ,其最大吸收波长为 64 8nm,表观摩尔吸光系数为 3 .2 0× 10 4L· (mol·cm) -1 ,铁 ( )浓度在 0～ 2 5 μg· (2 5 m L) -1范围内符合比耳定律。在酒石酸钾钠和氟化钠的存在下 ,方法具有良好的选择性 ,应用于粮食、植株样品和环境水样中微量铁的测定 ,结果满意     

国家标准样品 标准参比 荧黑3#（SRB3#）的研制

从标准参比炭黑3#(SRB3#)的定义、生产、混兑、分样、测试、数据统计等几方面介绍了标准参比炭黑3#(SRB3#)的研制及定值过程。     

Fe-Al合金薄膜的磁致伸缩特性

一般稀土金属-过渡金属系磁致伸缩材料都有脆和容易氧化等问题。而具有体心立方结构（bcc）的铁系磁致伸缩材料，较之稀土-铁系材料具有较高的韧性和耐蚀性。Fe-17％（原子）Ga单晶合金在室温下显示很高的磁致伸缩敏感度，但这一合金有价格高昂且难处理等问题，然而Fe-Al合金显然有其更多的优越性。因此，采用离子镀装置制备了Fe-Al合金薄膜，研究了结晶结构和磁特性及其磁致伸缩特性。研究时所用的薄膜试样是在三电极配置离子镀装置上制备的。首先在电弧炉中用纯铁（99．9％）和铝（99．5％）制得Fe-Al合金锭，通过电子束加热熔融蒸发形成Fe-Al合金蒸发源。在此蒸发源-基片Si（100）间设置的探针电极上施加正电位（50V），使之发生放电，由此所蒸发的金属蒸汽等离子化并沉积于硅基片上，通过改变Fe-Al合金蒸发物的成分来控制所形成的合金薄膜的成分。依靠基片托架背面的加热器来控制基片温度，于523K基片温度下进行镀膜。用能散X射线光谱法分析Fe-Al合金膜的成分,用触针法测定膜厚，用X射线衍射装置进行结构分析，用振动样品磁强计测定试样磁性，用光杠杆法测定试样的磁致伸缩。     

2×××系含Zr铝合金中Zn、Ni分析曲线的建立

2×××系铝合金由于加入Zr,使Zn、Ni光电分析时成分超差 ,这样给控制 2 2 19等含Zr元素的铝合金成分带来困难。对 2×××系含Zr铝合金中的Zn、Ni重新制作分析曲线 ,以消除由于Zr的加入对Zn、Ni测定的影响。从而保证其分析精度 ,确保分析数据的准确。     

金刚石(膜)的拉曼光谱表征技术进展

本文较全面地介绍了金刚石(膜)拉曼光谱中各主要拉曼峰的位置、特点及光致发光现象,重点对1150 cm-1附近拉曼峰产生的原因进行了讨论.通过对前人数据、结论的分析,指出1150 cm-1附近的散射峰和紫外拉曼光谱中T峰出现的机理应是一致的,都源于有序尺寸的减少.根据共振尺寸选择效应,1150 cm-1附近的拉曼峰,可能是紫外拉曼光谱中的T峰在可见光谱中向高波数移动的结果;而不同方法制备的金刚石膜样品其晶粒尺寸差异造成的振动模禁止,是不同研究者对1150 cm-1附近拉曼峰作为纳米晶金刚石的特征峰争论的原因所在.     

38CrSi钢表面纳米结构层力学性能的研究

采用超音速微粒轰击技术在38CrSi合金钢表面制备了厚度约为25μm纳米晶层.利用X射线衍射、扫描电镜和透射电镜对表面结构进行分析.纳米结构层的最表面层的晶粒尺寸约为16nm,晶粒尺寸随着距表面距离的增加而增大.利用纳米压痕仪对表面纳米结构层的力学性能进行研究,结果表明,当表面晶粒尺寸降低到纳米量级时力学性能明显改善,最表面纳米结构层的硬度是基体的2倍左右,并服从Hall-Petch关系;表面纳米结构层的弹性恢复系数明显提高;利用该方法制备的纳米晶对弹性模量的影响较小;对表面纳米化样品进行低温退火处理可使纳米结构层的性能更加稳定.分析表明表面纳米结构层力学性能的改善主要是表面晶粒细化的结果.     

基于近红外光谱的煤粉样品定量检测研究

针对煤质快速在线检测的需求,采用傅里叶变换近红外光谱结合不同的光谱预处理方法,即平滑处理方法、微分方法、多元散射校正方法、标准归一化处理方法分别建立了煤粉样品的水分、灰分和挥发分的偏最小二乘模型,并对模型的检测结果进行了十字交叉验证。结果表明,基于25点平滑处理方法建立的水分偏最小二乘模型较优,基于标准归一化处理方法建立的灰分偏最小二乘模型最佳,基于5点平滑处理方法建立的挥发分偏最小二乘模型精度最高,验证了应用傅里叶变换近红外光谱技术定量分析煤粉指标的可行性。