Effects of Cerium on Microalloying in Low Sulfur Nb-Ti-Bearing Steel

The overcooling austenite CCT curves were investigated by using THERMECMASTOR-Z simula-tion machine, the test samples refining from 50kg vacuum induction furnace and two-stage controlled rolling in laboratorial condition. Test results show that addition cerium (Ce) in low sulfur Nb-Ti-bearing steel affects as follows: Ce can. increase the transformation point t Ar3 and t Ar1, enlarge the intervals of temperature (tAr1-tAr3).Ce can make the CCT curves to move upper and right, reduce the hardenability. Ce can increase the transformation temperature of bainite and enlarge intervals of bainite. The martensites become from coarse strip to fine strip by Ce in higher cooling rates. Ce can decrease MS and enhance the trend of lath martensitic structure and limit the formation of lamellar crystal.     

Y—PSZ的马氏体相变

(一)试验方法 由上海工业大学提供纯ZrO_2和Y-PSZ(氧化钇稳定的部分稳定氧化锆)粉末,平均粒径为0.05～0.1μm。在医用压片机上将混有成型剂的粉末压制成19×14×2mm的薄片,经脱除成型剂后,在箱式硅化钼炉中于1450～1500℃保温2h烧结成约13.5×10 ×1.5mm的瓷片作为X射线衍射试样。常温X射线衍射在菲利浦APD-10全自动X射线衍射仪上进行。高、低温X射线衍射在日本理学     

用获得板条状马氏体提高模具寿命

<正> 热作模具在工作时承受着复杂应力和多变温度的联合作用,模具中各部分应力状态很复杂,工作时反复受热和冷却,因而要求热作模具应有高的强度、韧性及良好的抗氧化性、耐热疲劳性等。板条状马氏体具有较好的综合性能,既有高的强度和硬度,又有     

403回火马氏体不锈钢的颗粒冲蚀

SUS403马氏体不锈钢的金相结构为马氏体和铁素体混合组织，有非常好的韧性、强度、耐热性和耐腐蚀性。这种钢广泛用于应力大、形状复杂的零部件，如：阀门或泵体，管道材料和涡轮叶片。这种钢在工业应用中都要经过淬火和回火处理。[第一段]     

超高压下CsBr的结构与相变

采用金刚石对顶压砧高压装置（DAC）、同步辐射X光源和能散法，对CsBr粉末样品进行了原位高压X光衍射实验，最高压力115GPa。观测到在53GPa左右压力下，CsBr的最强衍射峰（110）劈裂成两个峰，标志简单立方结构向四方结构的转变；在0至最高压力范围内（相应于V／V0为1至0.463)测量了晶轴比c/a；在115GPa内未观测到样品的金属化现象。