Catalytic properties and electronic structure of copper ions in Cu-ZSM-5

The effect of ion exchange conditions, such as Si/Al ratio, precursor copper salt, pH and concentration of the solution, on the catalytic activity in SCR of NO by propane and on the electronic state of copper ions in Cu-ZSM-5 has been studied. The NO conversion in NO SCR by C₃H₈ has been found to reach a maximum value at Cu/Al ratio about 0.37–0.4 and remain constant at higher Cu/Al.

ESR and UV–vis DR spectroscopy have been used to elucidate stabilization conditions of copper ions in Cu-ZSM-5 zeolites as isolated Cu²⁺ ions, chain copper oxide structures and square-plain oxide clusters. The ability of copper ions for reduction and reoxidation in the chain structures may be responsible for the catalytic activity of Cu-ZSM-5. These transformations of copper ions are accompanied by the observation of intervalence transitions Cu²⁺–Cu⁺ and CTLM of the chain structures in the UV–vis spectra.     

Epoxy paint failure in B-52 fuel tanks: Part II. Influence of DIEGME concentration in the fuel on the failure process

A model has been proposed to explain the failure of the original BMS10-39 epoxy paint on upper vertical surfaces in B-52 fuel tanks. The model involves interaction of the paint with DIEGME, a fuel system ice inhibitor (FSII) in jet fuel, that is distilled from the liquid fuel. In this communication, distillation experiments used to support the model are refined to better match the mass transfer of vapor from fuel in a B-52 fuel tank at close to room temperature. The interaction of these lower temperature distillates with the paint affirms the earlier model. On the basis of these experiments it is proposed that paint failure may be controlled or eliminated by reducing the level of DIEGME in the fuel. Proposed changes in military jet fuel composition are detailed.     

Selectivity Enhancement to the Exclusive Formation of Ethyltoluenes and Hydrogen During Dehydroalkylation of Toluene with Ethane

The dehydroalkylation of toluene with ethane to the isomeric ethyltoluenes was studied on 0.4Pt/H-ZSM-5 at varying contact times (1/WHSV). At a high contact time of 1.0 h, toluene disproportionation and hydrogenolysis reactions dominate, resulting in low selectivity to the desired ethyltoluenes via the alkylation reaction. However, at a low contact time of 0.12 h side reactions are eliminated, resulting in maximum selectivities to the kinetically favored ethyltoluenes and hydrogen. Results at high selectivities to ethyltoluenes provide significant insight into reaction pathways.     

Active sites of Cu-ZSM-5 for the decomposition of acrylonitrile

The catalytic decomposition of acrylonitrile (AN) over Cu-ZSM-5 prepared with various Cu loadings was investigated. AN conversion, during which the nitrogen atoms in AN were mainly converted to N₂, increased as Cu loading increased. N₂ selectivities as high as 90–95% were attained. X-ray diffraction measurements (XRD) and temperature-programmed reduction by H₂ (H₂-TPR) showed the existence of bulk CuO in Cu-ZSM-5 with a Cu loading of 6.4 wt% and the existence of highly dispersed CuO in Cu-ZSM-5 with a Cu loading of 3.3 wt%. Electron spin resonance measurements revealed that Cu-ZSM-5 contains three forms of isolated Cu²⁺ ions (square-planar, square-pyramidal, and distorted square-pyramidal). The H₂-TPR results suggested that in Cu-ZSM-5 with a Cu loading of 2.9 wt% and below, Cu⁺ existed even after oxidizing pretreatment. The activity of AN decomposition over Cu/SiO₂ suggested that CuO could form N₂, but, independent of the CuO dispersion, nitrogen oxides (NO_x) were formed above 350 °C. Cu⁺ and the square-pyramidal and distorted square-pyramidal forms of Cu²⁺ showed low activity for AN decomposition. Temperature-programmed desorption of NH₃ suggested that N₂ formation from NH₃ proceeded on Cu²⁺, resulting in the formation of Cu⁺. The Cu⁺ ions were oxidized to Cu²⁺ at around 300 °C. Thus, high N₂ selectivity over Cu-ZSM-5 with a wide range of temperature was probably attained by the reaction over the square-planar Cu²⁺, which can be reversibly reduced and oxidized.     

Amtshaftung bei Bauführung im Hochwassergebiet; fehlerhafter Flächenwidmungsplan; Nachforschungspflichten der Gemeinde

Bestehen ausreichende Anhaltspunkte für die Hochwassergef?hrdung, ist die Gemeinde verpflichtet, sich durch Nachforschungen Gewissheit über das Vorliegen oder Nichtvorliegen eines Hochwasserabflussgebietes gem § 38 Abs 3 WRG zu verschaffen. Liegt ein solches vor, hat sie gem § 12 Abs 1 Z 2 krnt GplG dieses im Fl?chenwidmungsplan ersichtlich zu machen. Erteilt die Gemeinde eine Baubewilligung ohne diese von der Erteilung einer wasserrechtlichen Bewilligung abh?ngig zu machen, haftet sie für die Kosten der Bauführung, die bei gesetzes-konformer Vorgangsweise unterlassen worden w?re.     

介孔氧化铁对正辛醇乙氧基化反应的催化性能

以十二烷基磺酸钠为模板剂、乙二胺为碱性介质,将水热法合成的氧化铁/十二烷基磺酸钠复合中孔材料在550℃、空气气氛中煅烧10h,除去模板剂,得到介孔氧化铁。通过X射线衍射、氮气吸附-脱附方法对介孔氧化铁的晶体结构和表面物性进行表征。表征结果显示,煅烧后的介孔氧化铁具有典型的六方介孔的结构特征,平均孔径为5.4nm。将介孔氧化铁用于催化正辛醇乙氧基化反应,研究结果表明,升高反应温度和初始压力、增加催化剂用量,可加快环氧乙烷的反应速率,同时产物的相对分子质量分布较窄。当平均聚合度为6.5时,正辛醇聚氧乙烯醚相对分子质量分布的选择性系数达到21.1。     

快速色谱分析技术在油气勘探中的应用

文章通过对五口井的现场应用介绍，阐述了快速色谱分析技术在油气层识别和解释方面的准确性，探讨了该技术在薄油气层的发现和评价、快速钻进条件下油气层的发现、对油气层全烃组份变化的统一、水平井的地质导向以及排除钻井液添加荆对油气显示的影响五个方面的优势，从而论证了快速色谱分析技术在油气勘探中的应用价值。     

Übergangene Nachbarn; Erlangung der Parteistellung; Sachlichkeitsgebot

Die Regelung über die Erlangung der Parteistellung übergangener Nachbarn durch Geltendmachung von Einwendungen bis l?ngstens drei Monate nach dem angezeigten Baubeginn ist wegen der Anknüpfung an einen untauglichen Zeitpunkt verfassungswidrig.     

单微乳液中制备Ag/TS-1及丙烯气相环氧化

采用N2H4还原含AgNO3的单微乳液制备了Ag／TS-1催化剂。TEM表征结果表明，Ag高度分散于TS-1之上。以H2、O2存在下的丙烯气相环氧化为探针反应，考察了Ag／TS-1的催化性能。结果表明，采用Ag／TS-1为催化剂，Ag的负载量为1％（质量分数，下同），823 K焙烧后，373 K下反应30 min时，丙烯转化率为1．69％，环氧丙烷（Propylene oxide，PO）选择性为93．2％。当Ag的负载量超过2％时，反应过程中生成大量的热，造成PO的选择性下降。采用Ag的负载量为8％的Ag／TS-1催化剂，消除热效应后，丙烯的转化率为2．46％．PO的选择性为79．2％。     

VSC8150在波分复用系统开销提取中的应用

波分复用系统将不同波长的光复用在一起进行传输,以满足对传输容量和传输距离的各种需求。介绍了一种开销监视与提取的设计方法,使用VSC8150提取承载在波分复用系统相应波长上SDH信号的开销。分析了VSC8150的工作原理,管脚和外部接口,以及与FPGA、单片机共同完成B1重新计算,开销提取,B1,J0提取。此外,还提出将帧丢失,帧失步等错误状态传送给单片机和网管的方法。本设计增强了波分复用系统网管管理参数,功能和灵活性,这会在系统维护时带来较大的方便。该设计已经成熟应用在实际的波分复用系统中。