热压变形对灰口铸铁石墨形态的影响

研究了灰口铸铁(HTl50)在900℃大压下量塑性变形后石墨的分布形态，结果表明：随着压下量的增加，石墨片逐渐趋于平行分布；变形过程中发生了碳的回溶，同时伴随着石墨片的断裂；石墨片体积分数及片间距随压下量的增加而逐渐减少。     

提高高铬白口铸铁磨球冲击抗力的技术关键

当高铬白口铸铁含铬量为18%～28%,Cr/C值是8￣9,铸铁的显微组织是回火马氏体 少量残余奥氏体(<5%) M7C3碳化物,则磨球具有高的冲击韧性和断裂韧性K1C,具有高的冲击抗力,表现出低的冲击剥落量。     

纳米TiO2复合铁钛防锈颜料的研制及产业化进展

介绍了纳米TiO2复合铁钛防锈颜料的制备原理、工艺、技术指标;描述了铁钛防锈涂料的配方、性能检验和产业化进展情况.     

Coking kinetics of a Cr2O3/Al2O3 catalyst during 1-butene dehydrogenation: Effect of H2 partial pressure

The influence has been studied of the partial pressure of hydrogen (0–30 kPa) upon the coking rate of a Cr₂O₃/Al₂O₃ commercial catalyst during 1-butene dehydrogenation. Coke deposition has been analysed using a monolayer-multilayer reversible coke growth model (MMRC model). This model provides good fits to the experimental data, within the range of partial pressure of H₂ studied, and allows us to estimate the main kinetic parameters involved in the coking-deactivation process. The results obtained reveal a dual effect of hydrogen: competition against 1-butene for the active sites and the removal of coke precursors from the catalyst surface. Bom effects diminish the coking rate as the H₂ partial pressure is increased.     

Chemical Reaction Engineering and Research and development of gas solid systems

A general procedure is proposed for innovative research and development of gas-solid reactor systems, with a brief explanation of the significance of each step in the procedureBased upon the contacting mode between gas and solid phases, as well as the ways of supplying thermal energy to the reacting regions, various types of gas-solid reactor systems are classified by using tables of so called “matrix” form, for thermal cracking and gasification of heavy oils, gasification of coal, gasification of solid waste, calcination of limestone, clinkering of cement and reduction of iron ore.The importance of fundamental concepts is emphasized for successful research and development by presenting several examples; namely, calcination of limestone, thermal cracking of heavy oils and gasification of solid waste materials.In connection with the direction in which fundamental research should be oriented, four primary ways of thinking are proposed, which can be applied to obtain innovative ideas for further research and development in this field.One example of the author's practical experience was selected to show the role of the fundamental research in the course of large scale development. Finally the author outlines the role of chemical reaction engineering to innovate the novel gas-solid reactor systems which may be inevitable for simultaneous solution of the three big E's; namely, Energy, Environment and Economy.     

用含Pb、As、Sn地方生铁砂型铸造生产D型石墨铸铁的研究

基于Ph、As、Sn等元素有增大铁液过冷倾向的作用，利用含Ph、As、Sn的地方生铁，采用合金化和砂型铸造可以获得D型石墨铸铁，对其工艺方案进行了研究。用正交试验法设计试验方案，得到最佳工艺方案为：在亚共晶成分（WB％：3．2C，2．1si）的铁液中加入适量的铝（0．6％）和钛（0．8％），可以得到含有100％D型石墨的铸铁，其抗拉强度最高可达276MPa。     

大剂量Si-Mn复合孕育剂在铸铁中的应用

从例证和机理两方面来说明通过大剂量Si Mn复合孕育在铸铁中的应用 ,使Mn的作用得到充分发挥 ;Mn13是提高铸铁组织中珠光体量和性能的理想元素 ;通过调节大剂量Si Mn复合孕育剂中Mn的比例来稳定和提高基体组织中的珠光体量 ,达到稳定和提高铸铁性能的目的 ,它的可操作性比通过控制化学成分来稳定和提高铸铁的性能更好更容易 ,冲天炉熔炼效果更明显。     

Ni-Cr-Fe-Si-B合金涂层及铝青铜基体熔合区组织的研究

采用钨极氩弧焊方法在铝青铜基体上施焊了Ni—Cr-Fe-Si—B合金涂层，并运用金相显微镜、扫描电子显微镜及能谱分析了喷涂层、熔合区及热影响区的组织形貌和成分分布。结果表明，喷焊时，在涂层与基体界面两侧各组元均发生了明显的扩散，Cu、Ni组元间可相互取代，基体融合区组织的基本组成仍为α (α γ2)，但同时也形成了Cu2FeAl7、NiAl3等新相，且融合区组织细小，涂层与基体间为冶金态结合。     

离心铸造CrMoWVNb白口铸铁轧辊的研究

应用离心铸造方法：以Cr,Mo,V,Nb为主要合金元素，研制成功了CrMoWVNb白口铸铁轧辊，分析了合金元素在轧辊中的作用，指出在轧辊中加入适量稀土和钛可细化轧辊组织，改善轧辊性能，同时还分析了轧辊生产中裂纹产生的原因，提出了消除裂纹的措施，并应用于高速线材轧机预精轧机架，使用寿命达到高镍铬无限冷硬铁轧辊的4－5倍。     

离心铸造大口径球铁管用复合功能型脱硫剂的研制

为使硫量波动的高炉铁液能适应大型离心铸造球铁铸管生产,研制了一种成本较低廉、添加操作简单的复合功能型脱硫剂。其主要组分包括强脱[S]去[O]材料钝化镁粒、碳化钙,增加石墨核心元素Zn和膨胀集渣材料珍珠岩,以及能抑制反球化作用和净化铁液的材料等。采用冲入法进行球化处理,这种脱硫剂覆盖在球化剂和孕育剂上,使用方法简单,效果良好。