轴齿轮断齿失效分析

通过对轴齿轮断口形貌、硬度测试及金相组织等试验进行分析表明，齿根处没有进行硬化处理造成齿根处抗疲劳性能不足是导致轴齿轮疲劳断裂的主要原因，另外齿根过渡处倒角过小，且存在纵向刀痕引起了较大应力集中也是导致轴齿轮疲劳断裂的原因。     

“Technically Unavoidable” in Terms of Genetically Modified Organisms – an Approach for Food Control

In case of findings of authorized genetically modified (gm) plant ingredients below the 0.9 per cent threshold, exceptions from labelling requirements according to regulation (EC) No. 1829/2003 can only be made, “provided that this presence is adventitious or technically unavoidable”. The authors describe factors that should be considered regarding contaminations by gm plant ingredients as technically unavoidable or not. A practical approach for interpretation, taking into account quality control measures and documentation as well as present findings in comparable products is proposed. Received: February 23, 2007     

Calculation of fatigue limits of case-hardened specimens with consideration of mean stresses and residual stresses

 The strength of case-hardened parts under cyclic loading can be determined in an experimental manner, but this can produce a large amount of costs due to the expenditure of material and testing time. Therefore, a calculation method is developed, that strongly reduces the number of experiments. The presented model is based on Weibull's weakest-link concept and allows to compute the survival probability of a case-hardened part which is loaded close to the fatigue limit. The essential quantities in this model are the distribution of Vicker's hardness of the material, the exponents of the Weibull distribution of the volume and the surface, the residual stress state, the surface roughness and the surface oxidation depth. By integrating the survival probabilities of the surface and the volume, the survival probability of the entire specimen or part can be calculated, which allows to compute the fatigue limit. The necessary parameters have to be determined from reference specimens. The model is successfully examined by comparing experimental and calculated results of smooth and notched case-hardened specimens under alternating torsion, rotating bending, repeated tension and tension-compression. Received 20 August 2001 / Accepted 11 November 2001     

推进波作用下的底泥起动

在介绍推进波作用下底泥起动特点的基础上，将上层水体作为粘性流体，底泥作为粘弹性体，推导了推进波作用下泥床面剪应力的表达式，并根据试验结果，给出了推进波作用下底泥起动时的床面剪应力与底泥流变参数的关系。     

全双极WTA模型的改进及其实现

提出了一种相似度的新定义，使双极ＷＡＴ模型的实现更加简洁明了。增加一个阈值使系统能判别非存储模式或因其信息量过低而无法鉴定的输入模式，阈值的大小与要求的容错能力有关。双极相似度及阈值通过光学方法实现。阈值的光学实现使系统仍具有照明不变性。通过电路实现取及ＷＴＡ网络的迭代运算。     

Determination of gust action stress cycle counts for fatigue checking of line-like steel structures

The classical spectral analysis of structural response to a gusty wind is applied to the prediction of fatigue damage as expressed by the rate of accumulation of Miner's quotient, using the rainflow algorithm to establish stress-range cycle counts. A general solution in chart form is given for the effect of the broad-band (quasi-static) part of the response spectrum, together with an algebraic formulation for its combination with the effect of narrow-band (quasi-resonant) response.A procedure for integration of the long-term expectation of Miner's quotient is indicated. It is concluded that quasi-static response alone is unlikely to pose a serious fatigue problem. With generally anticipated levels of dynamic response, fatigue damage is greatly increased, but can be controlled at acceptable levels by care to avoid features especially sensitive to fatigue.     

The Research of ST-OFDM in Physical Layer of IEEE 802.16a

This paper briefly introduces one of the three physical layer implementations of IEEE 802.16a~[1],WirelessMAN-OFDM PHY.Based on the implementation,the combination of Orthogonal Frequency Division Multiplexing(OFDM)and Space-Time Coding(STC)which is briefly called ST-OFDM in IEEE 802.16a,is investigated under thechannel provided in Ref.[2].Especially,this paper is focused on the influence of the optimal decision threshold on the sys-tern Bit-Error-Rate(BER)performance based on unequal probabilities of sources.The simulations show that when Signal-Noise-Ratio(SNR)is low the optimal decision threshold is obviously superior to the usual one;when SNR is high to someextent,such as 10 dB for 4QAM and 16 dB for 16QAM,we can use the usual decision threshold instead of the optimal     

一个新的具有指定接收者(t,n)门限签名加密方案

提出了一个具有指定接收考验证的签名加密方案。该方案是数字签名与公钥密码体制的有机集成。与普通数字签名方案相比，除了具有认证性、数据完整性外还具有保密性和接收方的隐私性。然后又利用门限方案首次构造了一个（t,n)门限签名加密方案。该(t,n)门限签名方案具有数据传输安全、顽健性、通信代价更小、执行效率更高等特点。     

基于模糊度测度和改进遗传算法的图像分割

为了利用模糊集理论进行图像分割,本文提出了一种模糊度测度函数,它衡量了背景模糊集和某一个二值图像的相似性:模糊度越小,这种相似程度越大;并且对模糊度的计算只需要进行简单的比较运算和加法运算,便于硬件实现。本文利用遗传算法求取最佳阈值,针对遗传算法的某些不足之处.我们利用精英策略和模拟退火的思想,对其做了一些修正。实验结果表明:相对于Shannon熵方法和模糊熵方法,本文方法取得了较好的分割结果,并且具有较强的抗噪声能力。     

Effects of the cryogenic cooling on the fatigue strength of the AISI 304 stainless steel ground components

For environmental considerations, the substitution of the conventionally used oil-based grinding fluids has nowadays become strongly recommended. Although several alternatives have been proposed, cryogenic cooling by liquid nitrogen is the non-polluting coolant that has been given relatively more attention because of its very low temperature. In this investigation, in order to contribute to developing this promising cooling mode, its beneficial effects on the ground surface integrity of the AISI 304 stainless steel and their consequences on the fatigue lifetime are explored. Results of this investigation show that grinding under cryogenic cooling mode generates surfaces with lower roughness, less defects, higher work hardening and less tensile residual stresses than those obtained on surfaces ground under oil-based grinding fluid. These surface enhancements result into substantial improvements in the fatigue behaviour of components ground under this cooling mode. An increasing rate of almost 15% of the endurance limit at 2 × 10⁶ cycles could be realized. SEM analyses of the fatigue fracture surfaces have shown that the fatigue cracks observed on the specimens ground under cryogenic cooling are shorter (i.e., 30-50 μm) than those generated under oil-based cooling mode (i.e., 150-200 μm). The realized improvements in the surface integrity and in the fatigue behaviour are thought to be related to the reduction of the grinding zone temperature observed under cryogenic cooling, as no significant differences between the grinding force components for both cooling modes have been observed.