An approach to measure infill matric suction of irregular infilled rock joints under constant normal stiffness shearing

Rock joints infilled with sediments can strongly influence the strength of rock mass. As infilled joints often exist under unsaturated condition, this study investigated the influence of matric suction of infill on the overall joint shear strength. A novel technique that allows direct measurement of matric suction of infill using high capacity tensiometers (HCTs) during direct shear of infilled joints under constant normal stiffness (CNS) is described. The CNS apparatus was modified to accommodate the HCT and the procedure is explained in detail. Joint specimens were simulated by gypsum plaster using three-dimensional (3D) printed surface moulds, and filled with kaolin and sand mixture prepared at different water contents. Shear behaviours of both planar infilled joints and rough joints having joint roughness coefficients (JRCs) of 8–10 and 18–20 with the ratios of infill thickness to asperity height (t/a) equal to 0.5 were investigated. Matric suction shows predominantly unimodal behaviour during shearing of both planar and rough joints, which is closely associated with the variation of unloading rate and volumetric changes of the infill material. As expected, two-peak behaviour was observed for the rough joints and both peaks increased with the increase of infill matric suction. The results suggest that the contribution of matric suction of infill on the joint peak normalised shear stress is relatively independent of the joint roughness.     

Solid state reactions between SiC and Ir

Reactivity between SiC and Ir as a function of SiC-crystallinity was investigated by diffusion bonding technique under a vacuum and over the temperature range of 1200–1450 °C. As reaction products, various Ir-silicides and free unreacted-C were detected. Reactivity is strongly affected by the temperature and SiC-crystallinity involving a series of interactions, from “no reaction” to “massive exothermic reactions”. In particular, interfacial phenomena are more pronounced by the presence of defects and grain boundaries.Solid state reactions result in formation of fine C-precipitates rearranged in a quasi-periodic microstructure. On the contrary, clustering of highly ordered C-precipitates (C-graphitized) occurs after “massive reactions” take place.A relationship between the degree of graphitization (from 1 to multi-layers of graphene), temperature and SiC crystallinity was found by Raman spectroscopy. 2D-layering phenomenon is enhanced in polycrystalline SiC at high temperature.     

Study on the hydrogen storage properties of a TiZrNbTa high entropy alloy

High-entropy alloys (HEAs), as a new class of metallic materials, have received more and more attention due to its excellent mechanical properties. In this study, the hydrogen absorption properties, such as hydrogen absorption capacity, thermodynamics, kinetics and cyclic properties, as well as the hydride structure of a newly designed TiZrNbTa HEA were investigated. The results showed that multiple hydrides including ε-ZrH₂, ε-TiH₂ and β-(Nb,Ta)H were found in the TiZrNbTa HEA after hydrogenation. With the increase of temperature from 293 K to 493 K, the maximum hydrogen absorption capacity decreased from 1.67 wt% to 1.25 wt% and the plateau pressure related with β-(Nb,Ta)H hydrides increased from 1.6 kPa to 14.8 kPa. The formation enthalpy of β-(Nb,Ta)H hydride was determined to be −6.4 kJ/mol, which was less stable than that of NbH and TaH hydrides. The results also showed that the TiZrNbTa HEA exhibited a rapid hydrogen absorption kinetic even at the room temperature with a short incubation time, and the hydrogen absorption mechanism was determined to be the nucleation and growth mechanism. Moreover, the hydrogen absorption capacity at 293 K decreased slowly with the cycle numbers, and remained 86% capacity after 10 cycles. Cracking occurred after hydrogen absorption and became worse with cycles.     

Effects of sintering in a high magnetic field on properties of vitrified bond and vitrified CBN composites

Vitrified bond CBN grinding wheels are being widely used due to their superior performance. Also, advantages of vitrified grinding wheels are high elastic modulus, stable chemical property, and low thermal expansion coefficient. Brittleness and low strength are key factors restricting the development of vitrified bond CBN grinding wheels. In this paper, the sintering in a high magnetic field was innovatively introduced into the manufacturing of vitrified bond CBN grinding wheels, and the effects of sintering in a high magnetic field on properties on vitrified bond and vitrified CBN composites were systematically investigated. Vitrified bond was characterized using three-point bending, scanning electron microscopy, X-ray diffraction. It was observed that microstructure of vitrified bond could be changed, grain orientation could be controlled and average grain size could be decreased in a high magnetic field, while vitrified bond strength could be simultaneously improved. High quality vitrified bond could be obtained by appropriately adjusting the strength and direction of high magnetic field. Results demonstrated that vitrified bond properties were improved when the magnetic field strength was 6?T. In order to highlight the high magnetic field effect on the vitrified CBN composites, the ordinary CBN abrasives and nickel plated CBN abrasives were used respectively. Microstructures, bending strengths of vitrified CBN composites were compared in different high magnetic fields. When the magnetic field strength was appropriate (less than 6?T), the binding characteristic of vitrified bond CBN composites with nickel plated CBN abrasives was greatly improved. The highest bending strength value of vitrified CBN composites was 79.5?MPa in 6?T high magnetic field.     

Effect of in-situ formation of columnar mullite and pore structure refinement on high temperature properties of corundum casatbles

The effects of in-situ synthesis columnar mullite and pore structure on the hot modulus of rupture (HMOR), thermal shock resistance and corrosion resistance of corundum castables have been investigated in this paper. When 2% nano silica was added, the pore diameters of castables could be decreased to 15 nm (at 110 °C), 1 μm (1100 °C) and 6 μm (1500 °C), respectively. The corresponding reducing magnitude of pore size is 98.5%, 83.3% and 33.3%. The HMOR of castables fired at 1500 °C increased by 110% to 3.64 MPa. Furthermore, after three thermal shock cycles, the residual strength ratio of castables increased from 5.2% to 15.3%. A large amount of cross-distributed columnar mullite was formed between nano silica and α-Al₂O₃ by the two-dimensional nucleation mechanism, which remarkably enhanced the high temperature properties. The penetration index reduced from 30.86% to 19.88%, suggesting that smaller pore size and higher viscosity had a great influence to the penetration process.     

Road Extraction from High Resolution Remote Sensing Image based on Shape Analysis with Gestalt Theory

Simulating the psychological experience of human vision，a road extraction model based on the format tower is proposed to extract the road in the high resolution remote sensing image from the perspective of morphology.Firstly，based on the spectral and texture information，the suspected road targets are extracted by using segmentation technology.Then these targets are classified according to their reliability and extract the road targets for each category.Finally，three types of identified road information are verified and merged，and the continuous smooth road extraction results are obtained.Experiments on real high resolution images show that the results are consistent with the visual perception of the human eye，and the overall classification accuracy is higher，indicating that the algorithm is effective and feasible and has good use value.     

Formation and properties of high entropy oxides in Co-Cr-Fe-Mg-Mn-Ni-O system: Novel (Cr,Fe,Mg,Mn,Ni)3O4 and (Co,Cr,Fe,Mg,Mn)3O4 high entropy spinels

Possibility of formation of quinary and senary equimolar high entropy oxides from the Co-Cr-Fe-Mg-Mn-Ni-O system is presented. Different proposed compositions are synthesized using the solid-state reaction route at high temperatures (900−1100 °C) and quenched to room temperature. Phase composition of the samples is studied, showing tendency toward formation of two main phases: rock salt-structured Fm-3 m and spinel-structured Fd-3 m. It is documented that the annealing temperature has a profound effect on stability of both structures, and at 1100 °C usually the highest content of Fm-3 m phase is usually observed. Three different oxides, namely, (Co,Cr,Fe,Mn,Ni)₃O₄, (Co,Cr,Fe,Mg,Mn)₃O₄ and (Cr,Fe,Mg,Mn,Ni)₃O₄ are obtained as single-phase materials, which structure can be described as the high entropy Fd-3 m spinel one. The latter two compounds have not been previously reported in the literature. Activated character of the electrical conductivity dependence on temperature is observed, with relatively high total conductivity at high temperatures and corresponding high absolute values of Seebeck coefficient.     

FeOOH–CoS composite catalyst with high catalytic performances for oxygen evolution reaction at high current density

Water electrolysis is an efficient approach for high-purity hydrogen production. However, the anodic sluggish oxygen evolution reaction (OER) always needs high overpotential and thus brings about superfluous electricity cost of water electrolysis. Therefore, exploiting highly efficient OER electrocatalysts with small overpotential especially at high current density will undoubtedly boost the development of industrial water electrolysis. Herein, we used a simple hydrothermal method to prepare a novel FeOOH–CoS nanocomposite on nickel foam (NF). The as-prepared FeOOH–CoS/NF catalyst displays an excellent OER performance with extremely low overpotentials of 306 and 329 mV at 500 and 1000 mA cm⁻² in 1.0 M KOH, respectively. In addition, the FeOOH–CoS/NF catalyst can maintain excellent catalytic stability for more than 50 h, and the OER catalytic activity shows almost no attenuation no matter after 1000 repeated CV cycles or 50 h of stability test. The high catalytic activity and stability have exceeded most non-noble metal electrocatalysts reported in literature, which makes the FeOOH–CoS/NF composite catalyst have promising applications in the industrial water electrolysis.     

A first-principles investigation on mechanical and metallic properties of titanium carbides under pressure

The titanium carbides are potential candidates to achieve both high hardness and refractory property. We carried out a structural search for titanium carbides at three pressures of 0 GPa, 30 GPa and 50 GPa. A phase diagram of the Ti-C system at 0 K was obtained by elucidating formation enthalpies as a function of compositions, and their mechanical and metallic properties of titanium carbides were investigated systematically. We also discussed the relation of titanium concentration to the both mechanical and metallic properties of titanium carbides. It has been found that the average valence electron density and tractility improved at higher concentrations of titanium, while the degree of covalent bonding directionality decreased. To this effect, the hardness of titanium carbide decreases as the content of titanium increases. Our results indicated that the titanium content significantly affected the metallic properties of the Ti-C system.     

Stability and thermophysical properties of fly ash nanofluid for heat transfer applications

Improving the performance of heat transfer fluids is altogether significant. The best approach for improving the thermal conductivity is the addition of nanoparticles to the base fluid. In the present study, specific heat, dynamic viscosity, and thermal conductivity of water-based Indian coal fly ash stable nanofluid for 0.1% to 0.5% volume concentration in the temperature range of 30 to 60°C has been investigated. To evaluate an average particle diameter of 11.5 nm, the fly ash nanoparticles were characterized with scanning electron microscopy and dynamic light scattering. Using zeta potential, the stability of nanofluid in the presence of surfactant Triton X-100 was tested. Thermal conductivity and viscosity of fly ash nanofluid increased, while specific heat decreased as volume concentration increased. The effect of temperature on the fly ash nanofluid was directly proportional to its thermal conductivity and specific heat and inversely proportional to viscosity.