烧结与冷镦过程中铝硅共晶合金显微结构与密度的演变

采用烧结及后续的镦粗工艺制备了铝硅共晶合金块体材料,研究了烧结温度对烧结体显微结构、抗压强度及相对密度的影响。结果表明：烧结温度显著影响烧结体的显微结构和抗压强度,以临近铝硅共晶合金液相线的温度烧结时,发生了局部熔化,产生的熔融液体破坏了颗粒表面的氧化膜,颗粒之间相互黏结,形成了烧结骨架。以优化的555℃烧结,Si颗粒呈球状,抗压强度达到最佳,但相对密度未发生变化。在后续的冷镦过程中,烧结骨架及粉末颗粒均产生变形,孔隙减小,颗粒呈扁平状,相对密度达到了98%。     

储氢与合金材料

介绍了储氢合金材料和开发应用动态。     

塑料瓶贴标用乳液胶的研究

本文分析了塑料瓶的表面结构特性及其对贴标胶的要求，简介乳液胶的合成过程，讨论了聚会温度、搅拌速度、增粘剂和改性剂对贴标胶的影响。     

塑料模具材料选用原则及应用

对塑料模具材料的选用原则和新型模具材料进行了简要的介绍，在此基础上，以成型手机外壳塑料模具为例，对其关键零部件的选材应用进行了主要说明。     

Room temperature oxidation of lead-indium alloy films

The kinetics of growth of thin (14 to 40Å) oxide layers on lead-indium alloys was investigated ellipsometrically, using: 3000Å thick films at 23°C; and oxygen exposures at 760 torr for times ranging from five minutes to five days. Assuming that the oxide layer is comprised of a two-phase mixture of PbO and In₂O₃ having a negligible extinction coefficient made it possible to estimate the oxide composition from the ellipsometrically-obtained oxide refractive index. Under these oxidizing conditions, the volume fraction of PbO in the oxide mixture decreases from a value of unity for pure lead to zero for alloys containing more than 30 at. percent In, in agreement with the Auger Electron Spectroscopy results of Chou and coworkers. The oxidation rate equals a exp (X₁/X), where α and X₁ will be seen to vary complexly with alloy composition. A theoretical explanation of these results is also presented.     

Micro- and nano-scale deformation behavior of nylon 66-based binary and ternary nanocomposites

The primary aim of this paper is to provide an insight on the effect of the location of organoclay on the micro- and nano-scale deformation processes in melt-compounded nylon 66/organoclay/SEBS-g-MA ternary nanocomposites prepared by different blending sequences. In addition, the deformation processes of the ternary nanocomposites were compared to the binary nanocomposites (nylon 66/organoclay and nylon 66/SEBS-g-MA) and neat nylon 66. The incorporation of SEBS-g-MA particles toughened nylon 66 markedly; but the flexural modulus and strength were both reduced. Conversely, the use of organoclay increased the modulus but decreased the fracture toughness of nylon 66. Nylon 66/SEBS-g-MA/organoclay ternary nanocomposites exhibited balanced elastic stiffness and toughness. Stress-whitening studies of the fracture surfaces in terms of gray level were also performed and an attempt was made to correlate the optical reflectivity characteristics with fracture toughness. It was concluded that the capability of SEBS-g-MA particles to cavitate was decreased by the presence of organoclay in the SEBS-g-MA phase, resulting in reduced toughening efficiency. The best micro-structure for toughness and other mechanical properties is thus to maximize the amount of exfoliated organoclay in the nylon 66 matrix rather than to have it embedded in the finely dispersed SEBS-g-MA particles.     

合金钢中白点缺陷超声反射波辨析

通过对进口合金钢中白点缺陷超声反射波形的分析研究，为白点缺陷的判定提供借鉴，保证工程材料的使用安全。     

电炉还原熔炼氧化钴矿的生产实践

介绍了刚果(金)钴铜冶炼厂电炉还原熔炼处理钴铜氧化矿工艺的设计特点及生产实践。     

The Effects of Aging Precipitation on the Recrystallization of CuNiSiCr Alloy

The interaction between precipitation and recrystallization and its effect on the properties of the Cu-Ni-Si-Cr alloy during aging were discussed. The results show that the deformation results in much more dispersed precipitation of the phases. The precipitations have accelerating or retarding effects on the recrys allization. On the formation and growth of recrystallization, the precipitated phases are coarsed or dissolved in front of grain boundaries following a re-precipitation in the recrystallization area.