IFR-2000阻燃聚丙烯热性能研究

研究了用无卤膨胀型阻燃剂IFR-2000作阻燃剂的阻燃聚丙烯的热性能和阻燃性能。     

Correlation of reactivity with chemical structure: Thermal hydrogenation of gas oils

The relationship between chemical structure and reactivity for thermal hydroprocessing was studied for five gas oils derived from Alberta bitumens. Chemical structure was characterized by combining data from ¹ H and ¹³ C nuclear magnetic resonance spectroscopy, class fractionation, and elemental analysis to calculate structural parameters. Thermal hydrotreating was performed in a continuous-flow stirred reactor at 420 and 440°C, 13.9 MPa hydrogen pressure, and 1.5 h¹ LHSV. Conversion of the 343–525°C boiling fraction of the gas oils was correlated with the concentration of naphthenic methylene groups in the feed. Formation of methane and ethane was dependent on the degree of condensation of the aromatic rings in the feed oils. Thermal desulfurization was highly correlated with the amount of saturates in the feed, and the aromaticity of the resin fraction. Hydrogen consumption increased with the aromaticity of the gas oil…     

Characterization of microporous-mesoporous MCM-41 silicates prepared in the presence of octyltrimethylammonium bromide

MCM-41 silicates prepared in the presence of octyltrimethylammonium bromide either by a conventional method or by post-synthesis hydrothermal treatment were characterized by nitrogen adsorption in a wide range of relative pressure from 10^-6 to 1. Hydrothermally restructured samples were found to have lower BET surface areas, lower external surface areas and thicker silica walls than the non-treated sample. More importantly, in addition to their characteristic mesopores (ca. 3 nm), they were shown to have considerable amounts of micropores. The relative amount of micropores and mesopores was shown to be dependent on the treatment conditions. Thus, it is demonstrated that the postsynthesis hydrothermal restructuring is a convenient synthesis route to MCM-41 silicates with bimodal pore size distribution involving controllable amounts of microporosity. This revised version was published online in July 2006 with corrections to the Cover Date.     

一种无线传感器网络链式传输分簇路由协议

由于周围环境对无线传感器网络(WSNs)的影响,在布设到特殊环境下时会产生信号的衰减与损耗,导致通信不畅。针对此问题,提出一种以LEACH路由协议为基础适应特殊环境(长直空间)的新型路由算法。本算法采用链式传输,即从内部逐一将信号传输给距空间最外端且距基站位置较近的簇头,克服了内部节点死亡过快的问题。同时簇内采用链式传输并且改进簇头阈值与成簇半径,减小了能量消耗,提高了稳定性,克服了LEACH算法的不足。     

低密度泡沫玻璃的研究与应用

低密度泡沫玻璃是利用碎玻璃制造的一种气孔率大于90%的隔热保温材料,它具有强度高、导热系数小、吸水率低、不吸湿、耐腐蚀等特性,在潮湿环境下抗冻性能好,是一种优良的低温、超低温隔热保温材料。该产品用途广泛,所用的原材料简单易得,但生产工艺过程比较复杂,生产过程控制精度要求较高,容易产生各种缺陷而影响产品的质量。本文对低密度泡沫玻璃的生产工艺过程进行详细的分析研究,提出相应的措施,确保产品的低密度和高成品率,提高产品的性能,扩大产品的使用范围。     

Preparations and properties of thermosensitive terpolymers of N‐isopropylacrylamide,sodium 2‐acrylamido‐2‐methyl‐propanesuphonate,and N‐tert‐butylacrylamide

Terpolymers based on N‐isopropylacrylamide, sodium 2‐acrylamido‐2‐methyl‐propanesulfonate, and N‐tert‐butylacrylamide were synthesized by free‐radical copolymerization with 2,2′‐azobisisobutyronitrile as an initiator. The lower critical solution temperatures (LCSTs) of the linear polymer aqueous solutions were determined by the measurement of the transmittance on UV at different temperatures. The influence of the polymer concentration, polymer composition, and ionic strength on the LCSTs of the linear polymers was investigated. The LCST decreased with increases in the hydrophobic monomer N‐tert‐butylacrylamide, polymer concentration, and ionic strength. The phase transition became sharp when the polymer concentration and ionic strength increased. Meanwhile, the crosslinked hydrogels were prepared with the same recipe used for the linear terpolymers, but a crosslinker was added to the reaction system. The swelling ratios of the hydrogels at various temperatures and salt solutions were determined. The hydrogels possessed both high swelling ratios and thermosensitivity. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

热处理前后丙烯腈／溴乙烯共聚纤维的热性能和阻燃性能研究

分析了热处理前后丙烯腈／溴乙烯共聚纤维的热性能与溴乙烯含量、升温速率或热处理时间的关系，并对纤维的阻燃性与溴含量或热处理时间关系进行了研究。结果表明，溴含量的增加或热处理时间的延长对热稳定性和阻燃性的提高有较大影响，而且经热处理后纤维的阻燃性与溴无关。