玻璃微珠的表面化学镀银及红外辐射性能研究

采用化学镀方法在玻璃微珠表面镀银,考察了预处理条件、反应温度和反应时间等因素对玻璃微珠表面镀银的影响,并通过扫描电镜和X-射线衍射分析仪,对镀银后玻璃微珠的表面形貌和结构进行了观察和表征。将镀银玻璃微珠用于涂料中,考察了玻璃微珠在涂料中的应用及其红外辐射率的变化,探讨了化学镀条件对涂料红外辐射率的影响,结果表明,在控制反应温度和浓度的条件下,可使镀银玻璃微珠的红外辐射率由原来的1.02降为0.70,将其应用于涂料后,涂层的红外辐射率为0.80。     

玻璃纤维布内中空纤维丝的检测

介绍了玻璃纤维布内中空纤维丝的检测方法。     

石墨炉原子吸收光谱(GFAAS)法测定石英玻璃中硼的研究

试样经氢氟酸分解，通过加入化学改进剂和多次注射浓缩样品及低温、长时间灰化的方法，在硝酸介质中用石墨炉原子吸收光谱法(GFAAS)测定石英玻璃中硼的含量。该方法解决了GFAAS法分析石英玻璃中硼灵敏度低和准确度低的问题。     

粉煤灰超细玻珠复配轻集料在固井低密度水泥浆中的作用

阐述了粉煤灰超细玻珠复配轻集料在固井低密度水泥浆中对其流变性能、强度、质量均匀性以及密度的影响和作用机理。表明该复配轻集料可以明显改善水泥浆的流动性、保水性以及水泥与高效外加剂的相容性,水泥石抗压和抗折强度有显著改善,水泥浆具有良好的质量均匀性,用该集料配制的超低密度水泥浆能满足固井要求,并由此提高固井的经济性。     

大块非晶合金的性能、制备及应用

综述了大块非晶合金的性能、制备方法及应用，对比了吸铸法制备的棒状Zr41.2Ti13.8Cu12.5Ni10Be22.5,Zr57Cu20Al10Ni8Ti5,Zr52.5Ti5Cu17.9Ni14.6Al10(原子分数)大块非晶样品的过冷温度区间宽度(△Tx)，给出了3种大块非晶合金系列的热稳定性参数Tg、Tx及△Tx，提出了大块非晶合金领域存在的问题及发展方向．     

玻璃碳电极的激光改性处理

玻璃碳电极（ＧＣＥ）用激光脉冲照射处理后，电化学反应行为发生很大变化。背景电流减小，Ｆｅ３＋／Ｆｅ２＋氧化还原电对的电极反应速率显著提高，抗坏血酸（ＡＡ）在电极上呈现明显的吸附作用。     

低温腐蚀及其防护技术

为了加热炉和锅炉的安全经济运行 ,分析了烟气余热回收中低温腐蚀的机理 ,提出了行之有效地解决和防止低温腐蚀的几种技术方法     

BaFe12O19/SiO2-B2O3微晶玻璃陶瓷的制备和微波性能

采用柠檬酸sol-gel工艺合成了BaFe12O19/SiO2-B2O3微晶玻璃陶瓷，研究了SiO2-B2O3玻璃的含量，Ba/Fe原子比和热处理温度对体系析出晶相的影响，以及介电常数和磁异率在1MHz-6GHz频率范围的变化规律，结果表明，休系中SiO2-B2O3玻璃的含量和Ba/Fe比越高，BaF312O19相的析出越困难，前驱体合适的热处理温度为1000℃，介电常数和磁导率基本上随测试频率的增而加下降；介电损耗的最大值为0．43，磁损耗较小。     

Effects of solvent and temperature on the coupling agent/epoxy resin interface

Increased wetting of the coupling agent/epoxy resin interface was observed when γ-glycidoxypropyltrimethoxysilane, polyfunctional aminosilane and γ-aminopropyltriethoxysilane were applied respectively from methyllethylketone, dimethylformamide and water on woven glass cloths which had been cleaned at 300°C. However, when factory-applied coupling agents were burnt off the woven cloths and fresh coupling agents re-applied, it was found that the nature of the factory-applied coupling agent influenced subsequent wetting. Thinner glass fibres showed a greater improvement in wetting rate than thicker fibres in those solvents identified to be good for improved wettability, irrespective of the heat-cleaning temperature.     

Physical Aging of Amorphous Fructose

ABSTRACT: Physical aging of amorphous anhydrous fructose at temperature 5 °C and at 22 °C was studied using differential scanning calorimetry (DSC). The dynamic glass transition temperature, T_g0 for unaged samples was 16 °C and 13.3 °C for heating rate of 10 °C/min and 1 °C/min, respectively. The fictive temperature, T_f0 for unaged samples calculated by Richardson and Savill method was 12 °C, which is close to the dynamic value obtained from the lower DSC heating rate. The fictive temperature T_f of the aged fructose glasses at temperatures both below and above the transition region was fitted well by a non-exponential decay function (Williams-Watts form). Aging above the transition region (22 °C) for 18 d increased both the dynamic glass transition temperature T_g and the fictive temperature T_f. However, aging below the transition region (5 °C) for 1 d increased the dynamic glass transition temperature T_g but decreased the fictive temperature T_f.