金属注射成形Ti-6Al-4V烧结坯的力学性能与烧结时间关系

研究了在1260℃烧结时,烧结时间对Ti-6Al-4V烧结坯力学性能的影响.结果表明平均晶粒尺寸为45 μm的氢化-脱氢粉末样品在1 260C烧结3 h～6 h,其相对密度为95.6%～96.7%、拉伸强度648 MPa～686 MPa、屈服强度526 MPa～615 MPa,但延伸率仅小于4%.90%气雾化(晶粒尺寸为32.5 μm)和10%氢化-脱氢混合粉末样品在1 260℃烧结2 h～6 h,其相对密度大于95%、拉伸强度800 MPa～848 MPa、屈服强度712 MPa～762 MPa、延伸率7.4%～9.5%.混合粉末样品的力学性能几乎达到美国ASTM粉末冶金的标准.     

W18Cr4V高速钢激光相变强化层的残余应力

利用Ｘ射线衍射法对Ｗ１８Ｃｒ４Ｖ高速钢激光相变强化层的残余应力进行了测定和分析。试验结果表明，相变强化层表面的残余应力为压应力，内部为拉应力，近似按正弦函数分布。其大小和分布状态随工艺参数的变化而改变。当改变工艺参数使表面熔化时，表面为拉应力。     

立轧对中厚板断面形状的影响

基于中厚板在立轧轧边后板坯变形的物理模拟,分析了平辊立轧与倒棱轧制对中厚板断面形状的影响。平辊立轧可显著减小坯料侧面双鼓形及折叠,倒棱轧制可有效消除坯料侧面双鼓形。     

MECHANISM OF Re-B-V CO-PERMEATION

ＭＥＣＨＡＮＩＳＭＯＦＲｅＢＶＣＯＰＥＲＭＥＡＴＩＯＮ①ＬｉＦｅｎｇｚｈｅｎ，ＬｉｕＺｈａｏｊｉｎｇ，ＪｉｎＱｕａｎ，ＸｕＺｈｉｈｕｉＤｅｐａｒｔｍｅｎｔｏｆＭａｔｅｒｉａｌｓＳｃｉｅｎｃｅａｎｄＥｎｇｉｎｅｅｒｉｎｇ，ＨａｒｂｉｎＵｎｉｖｅｒ...     

Amorphous sol-gel SiO2 film for protection of Ti6Al4V alloy against high temperature oxidation

Amorphous SiO₂ thin films were deposited on Ti6Al4V alloy by sol-gel processing. Isothermal and cyclic oxidation tests of the coated and uncoated specimens were performed at 700 and 800 °C. The SiO₂ film exhibited beneficial effects on the oxidation resistance of the alloy. Titania scales formed on the uncoated specimens, and severe spallation and stratification of the scales were observed. The oxidation rates of the silica coated specimens were decreased significantly. The silica film shrunk to about a quarter in thickness, probably by mechanism of crystallization of silica and evaporation of the organic additments. The oxide scales formed on the coated specimens were multilayered. Beneath the silica film, formation of a thick rutile titania layer followed by a thin alumina layer occurred. Above the silica film, alumina plus minor titania layer formed. It is deduced therefore that the growth of the multilayered and mixed oxide scales was dominated by both outward diffusion of metal and inward diffusion of oxygen.     

Effects of temperature and current density on the surface hardness and tribological properties of Ti-6Al-4V alloy by molten salt carburization

Surface hardening of Ti-6Al-4V alloy was achieved by carburization in a molten salt bath containing BaCO₃ as the carbon-yielding agent with electrolysis within the temperature range 790–930°C. The hardness of the total carburizing layer (TCD) is influenced by the bath temperature, the applied current density and the carburizing period. The major hardening effect is considered to be the formation of a solid solution of carbon in -Ti. The oxide film wrapping at the outermost surface of cathodically charged specimens, identified to be mainly BaTiO₃, was formed irrespective of the bath temperature during the quenching process and has no effect on the surface hardening. The optimal carburizing parameters obtained in this study for surface hardening are carburizing at 930±10°C (bath temperature) and 0.3 A/Cm² (applied current density) for 90 min (carburizing period), while those for tribological properties improvement are carburizing at 860±5°C and 0.3 A/Cm² for 90 min.     

Mechanical properties and microstructure of Ti-6Al-4V compacts by metal injection molding

Ti-6Al-4V compacts were fabricated by metal injection molding(MIM). Influence of vacuum sintering time on mechanical properties and microstructure of the sintered compacts at 1 260 ℃ were investigated. The experimental results show that the compacts sintered at 1 260 ℃ for 3 -6 h, which was made from hydrogenation-dehydrogenation(HDH) powder(average particles size is 45 μm), have a relative density of 95.6%- 96.7%, ultimate tensile strength of 648 - 686MPa and 0.2% yield strength of 526 - 615MPa; but a lower elongation(＜4%) and that the compacts sintered at 1 260 ℃ for 2 - 6 h, which was made from 90% gas-atomized powder(average particles size is 32.5 μm) and 10 % HDH powder, have higher relative density(＞95 %), ultimate tensile strength of 800 -848MPa,0.2% yield strength of 712 - 762MPa and high elongation (7.4%- 9.5%). When the sintering time is increased,porosity decreases and microstructure of sintered products changes from equiaxed to typical Widmanstatten, the average sizes of prior β grains, α colonies and α phase thickness in the β grains increase accordingly. After HIP treatment,pores obviously become less, microstructure of alloy is refined and mechanical properties are greatly improved.     

ZTC4筒形件温成形扩口数值模拟

对铸造Ti-6Al-4V筒形件温成形扩口成形工艺进行了数值模拟分析,得出了优化的工艺参数,并对凸模锥角进行了优化模拟,得出了合适的锥角。     

Observations on the oxidation behavior of Ni-Cr alloys containing minor additions of group III,IV, or V elements

The corrosion of a number of experimental ternary Ni-15 wt. % Cr-0.5wt. %X alloys (where X= Y, La, Ce, Sm, Th, U, Zr, or V) has been assessed in pure oxygen at 900° C for periods of exposure up to 450 hr, and compared with the behavior of an Ni-15% Cr control alloy. It has been established that while all of the alloys oxidize in accordance with a protective, approximately parabolic regime, considerable differences in oxidation rates are exhibited. In particular, additions of La, Ce, and Th bring about progressively enhanced rates of oxidation relative to the binary alloy, whereas Y, Sm, V, U, and Zr effect increasingly reduced rates of oxidation in the order given. The rate constant for the Th-bearing alloy is about two orders of magnitude larger than that for the alloy containing Zr. Such differences in behavior seem to be associated with subtle variations in the morphology/composition of the corrosion products from alloy to alloy. The observations are considered in the light of earlier published literature concerning the effects of rare-earth and other reactive elements on the oxidation behavior of Ni/Cr alloys.This work has been carried out with the support of Procurement Executive, Ministry of Defence.     

螺帽热镦凹模的选材与复合渗强化处理研究

螺帽热镦凹模选用近年研究成功的新型3Cr3Mo3W2V(简称HM1)热作模具电渣钢制造,采用锻热固溶调质预处理、优化热处理工艺与复合渗强化处理新工艺,消除了原HM1电炉钢制常规热处理时该模具的中期失效。