铝电解多功能天车轨道接头磨损的机理分析

分析铝电解多功能天车轨道接头的受力情况、轮轨磨损机理和现场采集的数据照片,指出轨道经过碾压后的硬度变化以及氧化铝灰对天车轨道接头磨损的影响,提出相应措施.     

降低氧化铝生产中熟料折合比的探讨

在氧化铝生产过程中，熟料折合比是烧结法一项重要的综合性指标，本文通过对熟料折合比的定义、计算公式的剖析，分析了生产过程中影响熟料折合比的主要因素，对有效降低熟料折合比的措施进行了探讨。     

棕刚玉粉中Al2O3含量分析方法的探讨

对耐火材料——棕刚玉粉的质量分析控制，提出了用实用性的检测方法测定其Al2O3含量。通过与国家标准分析方法的对比试验，证实快速实用分析方法测定棕刚玉粉中Al2O3含量是可行的。     

碳酸化分解工艺的改进与实践

本文针对烧结法生产氧化铝过程中,铝酸钠溶液的碳酸化分解工艺,由间断分解到连续分解的改进进行了论述,指出连续分解是碳酸化分解的发展方向。     

Slip and Twinning in Polycrystalline Alumina (α-Al2O3) Deformed under Hydrostatic Pressure between 600° and 1000°C

The microstructure of polycrystalline alumina deformed under hydrostatic pressure and at low temperature is investigated by transmission electron microscopy. Deformation occurs mainly by prism plane slip and rhombohedral twinning. Introduction of hydrogen leads to a significant decrease in the yield stress. In large grain size alumina deformed with hydrogen, accommodation of twinning involves dislocation reactions in the twin boundary and in the grains rather than by cracking. Prism plane dislocations decompose into basal dislocations by cross slip probably due to a decrease of Peierls stress for basal slip in the presence of hydrogen.     

宽流道板式换热器在氧化铝生产种子分解过程中的应用

介绍了宽流道板式换热器的结构、特点及在氧化铝生产种子分解过程中的应用。     

The interfacial microstructure of joined single crystal and polycrystalline alumina

The interfacial microstructures of 96 and 98% polycrystalline alumina joined with single crystal sapphire have been investigated in relation to the joining parameters. Joining has been evaluated based on either using a thin spin-on silica interlayer or by placing the alumina and sapphire in direct contact. The materials were joined by placing the coated or uncoated surfaces in contact and heating in the range of 1340–1475 °C with minimum external load. With the aid of a silica interlayer, sapphire and 98% polycrystalline alumina were successfully joined in 180 min at 1400 °C and above, while samples without a silica interlayer failed to join under these conditions. However, sapphire and 96% polycrystalline alumina were joined both with and without the use of silica interlayer. A variety of interfacial morphologies have been observed, including amorphous regions, fine crystalline alumina, and intimate contact between the sapphire and polycrystalline alumina.     

浸入式水口MgAlON质内衬材料的抗Al2O3附着性研究

浸入式水口在连铸过程中，特别是多炉连铸铝镇静钢时，由于Al2O3在水口内壁附着引起堵塞问题。研究了无碳无二氧化硅的MgAlON质耐火材料，考察了MgAlON—Al2TiO5、MgAlON—BN、Al2O3-C、CaO-ZrO2-C材料的抗Al2O3附着性。结果表明，MgAlON-AT复合材料的抗舢203附着性和抗钢水侵蚀性均优于其它材料．     

Thermoreversible Gelcasting: A Novel Ceramic Processing Technique

A new ceramic processing method, thermoreversible gelcasting (TRG), has been developed. The method uses a gelation process that can be reversed multiple times. Two Al₂O₃ systems have been explored with the use of a specific triblock copolymer to form a binding gel network. The mixture becomes a free-flowing liquid on heating above 60°C. However, on cooling below 60°C, the slurry instantaneously transforms to a physical gel. This process can be reversed easily (essentially with an infinite processing time window) while the solvent is present in the system, which is advantageous when trying to produce high-quality dense pieces if initial casting irregularities occur. Near-theoretically dense specimens have been produced with properties consistent with reported values of high-density Al₂O₃.     

Asymmetric alumina membranes electrochemically formed in oxalic acid solution

Alumina membranes were fabricated by anodizing aluminium metal in 0.15 M oxalic acid. The growth kinetics of the porous layer were investigated in the temperature range –1 to 16 °C using linear potential scans up to 70 V. The faradaic efficiencies of metal oxidation and of porous layer formation, determined by applying Faraday's law, were found to be independent of both temperature and electrical charge. SEM analysis of the metal-side and solution-side surfaces revealed different morphologies. After dissolution of the barrier layer in phosphoric acid, the metal-side surface showed circular pores whose size of about 90 nm was found to be uniform and independent of temperature. The pore population was also practically independent of temperature and a value of about 4 × 10¹³ pores m^–2 was determined. On the solution-side surface the presence of a deposit partially occluding the mouths of pores was observed. This coating could be removed by chemical etching in NaOH or thermal treatment at 870 °C, where decomposition of oxalate occurs. This supports the hypothesis that the deposit consists of an aluminium salt containing oxalate anions precipitated from the solution. The results show that it is possible to control the morphological characteristics of the anodic alumina membranes by careful choice of experimental conditions.