Characterization of a Microhollow Cathode Discharge Plasma in Helium or Air with Water Vapor

Microhollow cathode discharge (MHCD) plasmas were generated in gas mixtures containing water vapor at pressures of up to 100 kPa of He or 20 kPa of air. The cathode diameter was 1.0 mm with a length of 2.0 mm. The electrical characteristics showed an abnormal glow mode. Spectroscopic measurements were carried out to examine the plasma and radicals. An analysis of the spectral profile of Hα at 656.3 nm enabled a derivation of the electron densities, namely 2×10 14 cm 3 (at 10 kPa) and 6×10 14 cm 3 (at 4 kPa) for the helium and air atmospheres, respectively, in the negative glow region. By comparing the observed OH radical spectra with those calculated by the simulation code LIFBASE, the gas temperature was deduced to be 900 K for 4 kPa of He at a discharge current of 50 mA.     

湿度对热镀锌钢材在海洋大气环境中氢脆敏感性的影响

采用改进的双面电解池检测热镀锌钢材在恒温30℃、不同湿度条件下的氢渗透电流,并结合慢应变速率拉伸和断口形貌分析,研究其在海洋大气环境中的氢脆敏感性。结果表明:在相对湿度小于70%时,热镀锌钢材未检测到明显的氢渗透电流,但随着湿度的增加,氢渗透电流密度逐渐增大;当镀层存在缺陷时,镀锌层在为钢材基体提供阴极保护的同时也会促进氢向钢材基体中渗透,且氢渗透电流密度的最大值随镀层缺陷面积的增加而降低;氢吸收和氢渗透降低了热镀锌钢材的断后伸长率,导致其断口切边处出现少量撕裂棱,表明热镀锌钢材在高温、潮湿的海洋大气中使用时,其氢脆敏感性将有所提高。     

沙漠浮土中可溶性盐对铝的大气腐蚀影响

通过干湿循环加速试验模拟Al表面沉积沙漠浮土情况下的大气腐蚀过程,利用失重分析、扫描电镜（SEM）和大气腐蚀监测仪（ACM）研究浮土中可溶性盐对Al的大气腐蚀的影响。结果表明：浮土中的可溶性盐会使发生大气腐蚀的相对湿度范围变宽,随着可溶性盐含量的提高,Al的腐蚀不断恶化。在可溶性盐成分中,MgCl₂对Al的腐蚀影响最大,NaCl次之, MgSO₄和Na₂SO₄的影响较小。     

A corrosion study of the ferrous medieval reinforcement of the Amiens cathedral. Phase characterisation and localisation by various microprobes techniques

In this study, long term corrosion mechanisms are approached through the characterisation of corrosion products formed on ancient artefacts over 500 years. Thirty-one artefacts were sampled in the Amiens cathedral. The thick corrosion product layers have been characterised at a microscopic scale by coupling complementary microbeam analytical techniques (SEM-EDS, Raman microspectroscopy, X-ray microdiffraction and microfluorescence, X-ray absorption microspectroscopy under synchrotron radiation). The main phase of the corrosion layer is goethite but lepidocrocite and akaganeite are also present locally in the corrosion layer. In addition, the presence of low crystallinity phases (feroxyhyte and/or ferrihydrite) is showed. These phases are electrochemically reactive, thus they could play a key role in the corrosion mechanisms.     

超音速等离子喷涂制备金属陶瓷涂层的抗冲蚀性能

通过高效能超音速等离子喷涂(SAPS)制备WC-Co及WC-Ni Cr金属陶瓷涂层,对比研究了2种涂层的抗冲蚀性能及在热腐蚀条件下的结构和性能演变。结果表明:2种涂层在喷涂过程中均会发生一定程度的脱碳,表现为W_2C相的形成;同时在WC-Co涂层中有少量的Co_3W_3C和Co_6W_6C相生成,且该涂层在热腐蚀后表层的WC相出现了分解与氧化,形成了W_3C、W_6C_(2.54)等脱碳相与CoWO_4、WO_3等氧化物相。在普通冲蚀条件下,WC-Co涂层的抗冲蚀性能更为优异,但热腐蚀会极大降低WC-Co涂层的抗冲蚀性能;与之相反,WC-NiCr涂层中的NiCr相在热腐蚀环境下生成的Cr_2O_3可以有效阻挡涂层内部与外部之间的物质扩散,从而降低了热腐蚀对涂层结构的破坏,在热腐蚀条件下表现出了优良的抗冲蚀性能。     

NaCl沉积对Zn的大气腐蚀产物影响的FTIR光谱研究

用红外光谱技术研究了表面经有固体NaCl沉积的Zn试 样在含有10-6 SO2大气环境中的腐蚀，探讨了其腐蚀过程.表面沉积有NaCl的Zn在 干燥大气中的腐蚀产物是Zn5(OH)8Cl2·H2O，当具有该产物的Zn样品置于含有10 -6 SO2大气环境中时，腐蚀产物中会有多种硫酸盐成分存在，且硫酸盐的量随暴露时 间的延长而增加.     

稀土Ce对7A04铝合金耐腐蚀性能的影响

目的提高7A04铝合金的耐腐蚀性能。方法采用周期浸润腐蚀试验模拟海洋大气环境,研究了不同稀土Ce含量的7A04铝合金的腐蚀行为及规律。通过金相显微镜和扫描电子显微镜,观察了不同试样的组织和夹杂物形貌。采用失重法和电化学阻抗技术,分析了试样的腐蚀动力学规律及电化学行为特性。结果在Ce质量分数分别为0%、0.39%和0.81%的7A04铝合金中,稀土Ce的加入量为0.39%时,其晶粒最细小,第二相与夹杂最少且分布最均匀,合金的基体组织得到了改善。稀土7A04铝合金的腐蚀失重明显低于不含稀土Ce的7A04铝合金,且锈层电阻升高,其中含0.39%稀土Ce的7A04铝合金的锈层电阻最高。结论三种7A04铝合金均发生了明显的局部腐蚀,主要为点蚀。稀土Ce的加入,改变了非稀土铝合金中的T相和S相,生成了新的细小的块状金属间化合物,改善了组织的均匀性,提高了其腐蚀锈层电阻,增加了锈层对基体的保护能力,使铝合金耐海洋大气腐蚀性能提高。在三种稀土Ce含量的铝合金中,含0.39%稀土Ce的7A04铝合金的耐蚀性最佳。     

聚四氟乙烯/Al3O2-TiO2复合涂层的制备及其疏水性能研究

目的 在铝合金表面制备耐磨、耐蚀、高结合强度的疏水涂层。方法 采用大气等离子喷涂(APS)在铝合金基体上制备AT(Al3O2-Ti O2)涂层,在AT涂层上采用溶胶-凝胶法制备聚四氟乙烯(PTFE)面层,借助扫描电子显微镜、X射线衍射仪、3D形貌仪、接触角测试仪等仪器对涂层的显微结构、成分、粗糙度、接触角进行表征。结果 喷距为120 mm、电流为680 A、送粉量为18 g/min的条件下,实心AT涂层和空心AT涂层表面粗糙度为6.99μm、6.13μm,孔隙率为5.88%、15.18%,硬度为945.82HV0.3、768.1HV0.3,与基体的结合强度为32 MPa、28 MPa,实心AT涂层与PTFE涂层的结合强度为19 MPa。实心PTFE/AT复合涂层与水的静态接触角最大可达130.9°,PTFE涂层表面含有氟化物和硅化物。结论 实心粉末AT涂层表面粗糙度较大,综合性能优于空心粉末AT涂层,因此,将实心AT涂层作为复合涂层的底层。实心PTFE/AT复合涂层具有与荷叶表面相仿的微纳米二元粗糙结构,具有良好的疏水性能,疏水性能与表面含氟物质的疏水基团以及低表面能的二元粗糙结构相关。     

NaCl和CO2对Zn在薄液膜下腐蚀的协同作用

使用石英晶体微天平（ＱＣＭ：ｑｕａｒｔｚ ｃｒｙｓｔａｌ ｍｉｃｒｏｂａｌａｎｃｅ）为主要手段研究了在８５％ＲＨ（相对湿度）和ＮａＣｌ存在的条件下,金属Ｚｎ在不同ＣＯ２浓度下的大气腐蚀动力学,同时结合Ｘ射线衍射（ＸＲＤ）和扫描电镜（ＳＥＭ）研究了Ｚｎ在薄液膜下的大气腐蚀机理,并用扫描电子显微镜（ＳＥＭ）对腐蚀产物进行形貌分析,阐述了腐蚀产物的保护特征。实验结果表明,在薄液膜下,ＮａＣｌ的存在使金属