冷却器盘管失效分析及防范措施

本文介绍了冷却器盘管破裂泄漏的情况，分析了失效破坏的原因，并提出防止冷却器盘管破裂泄漏的措施。     

MgO／Ni系梯度功能材料的设计与制备

对ＭｇＯ／Ｎｉ系梯度功能材料（ＦＧＭ），分别用实验和微观力学模型测定和计算了用于热应力缓和设计的各物性参数。讨论了两种结果之间存在差异的原因。用有限元方法模拟了制备过程中ＦＧＭ的热应力，得到ＭｇＯ／Ｎｉ系ＦＧＭ的综合设计准则。按设计结果进一步调整粉末工艺性质，成功地烧制出ＭｇＯ／Ｎｉ系ＦＧＭ。     

Slow stable crack growth in high density polyethylenes

The phenomenon of slow stable crack growth in polyethylene is investigated using notched specimens subject to constant load and the concepts of fracture mechanics. The effect of specimen geometry and dimension, the loading and the mode of loading on the applied stress intensity factor versus crack speed ($\text{K}{}_{\mathrm{c}}\text{-}\text{a}\text{?}$) curves has been studied to demonstrate that K_c is the controlling stress parameter for crack growth under suitable conditions. $\text{K}{}_{\mathrm{c}}\text{-}\text{a}\text{?}$ curves are obtained for a high density polyethylene homopolymer in distilled water and in a diluted detergent solution at four different temperatures. Results are also obtained for a much tougher medium density polyethylene copolymer whenever possible. Several mechanisms can be identified from the form of the $\text{K}{}_{\mathrm{c}}\text{-}\text{a}\text{?}$ curves. Two, in particular, have been observed but not explained before: (i) crack growth with a time dependence of 0.25, and (ii) the high $\text{K}{}_{\mathrm{c}}\text{-}\text{a}\text{?}$ slopes for crack growth in a tough copolymer. With the help of scanning electron microscopic studies of the fracture surfaces, (i) is postulated to be due to diffusion controlled void growth process and (ii) is considered to be the result of crack tip blunting effects. From the temperature dependence of crack growth, the activation energy of the diffusion controlled crack growth process is found to coincide with that of the x-relaxation process in polyethylene implying that diffusion controlled crack growth may be related to the motion of main chains in the polymer.     

Creep and Creep Fracture in Hot-Pressed Alumina

The creep and creep fracture behavior of two hot-pressed aluminas are presented, for both flexural and tensile testing. Steady-state power-law creep is observed with a stress exponent of about 2 for each material. Three distinct fracture regimes are found. At high stress in flexure, fracture occurs by slow crack growth with a high stress dependence of the failure time. At intermediate stresses, in both flexure and tension, creep fracture occurs by multiple microcracking after modest strains. Failure times exhibit a modest stress dependence (stress exponent of 2.5 in tension and 3 in flexure), with a constant failure strain equal to 0.09. The failure times are considerably longer in flexure than in tension, because of the constraint imposed on crack growth by the bending geometry. We conclude that flexure cannot be used for creep lifetime assessment, even in simple, single-phase materials such as Al₂O₃. At low stresses, in tension, failure also exhibits a modest stress dependence but with a much higher failure strain. The material shows the onset of super-plastic behavior.     

无底柱分段崩落法采矿进路受力过程分析

在使用无底柱分段崩落法的矿山,大都存在着地压现象。其主要表现是采矿进路和联络道的变形破坏。对采矿进路在开挖和回采过程中各阶段受力情况的分析表明,进路的变形、破坏主要是受到岩体初始静应力、爆破动应力和矿柱支撑应力的综合作用的结果。     

我公司进行热电联产的可行性分析

大压差减温减压是能的严重贬值。根据公司供热现状，分析了热电联产的可行性，利用蒸汽余压发电后，再供生产系统各热用户，这样既节约了能源又缓解了集团公司用电紧张的局面，而且有相当可观的经济效益。     

CGA560增强助磨剂在水泥粉磨中的应用研究

研究了CGA560增强助磨剂在水泥粉磨中对台时产量和水泥质量的影响。试验结果表明:在磨机状况不改变的条件下,CGA560增强助磨剂的加入可提高磨机产量10%-30%;同时可有效减少过粉磨现象,优化水泥颗粒级配,提高了水泥粉磨细度及比表面积;因而使水泥强度等性能得到了明显改善和提高。     

胶层厚度对拉伸试样应力分布影响的数值分析

运用弹塑性有限元法研究了胶层厚度对承受拉伸载荷的对接接头胶层内应力分布的影响．三维有限元法数值分析的结果表明，随胶层厚度减小，胶层中正应力SZ与剪应力SYZ的分布趋于均匀；而对正应力SY而言，胶层厚度为0．15mm时，其边缘峰值应力最低。     

Shear-rate dependence of first normal stress difference of poly(isoprene-b-styrene) in solution near the order-disorder transition temperature

Viscoelastic properties of poly(isoprene-b-styrene) in dioctylphthalate under steady shear flow were measured near the order—disorder transition temperature. In ordered states, first normal stress difference N₁ is proportional to shear rate at low region, but becomes proportional to at the high region, similar to the N₁ behaviour of polymer blends undergoing shear-induced homogenization. Because the existence of microdomains was confirmed at the high region by the flow birefringence method, it is concluded that the above N₁ behaviour is not caused by shear-induced homogenization, but is probably caused by the shear-induced alignment of the microdomain structure.     

考虑中主应力效应Gudehus-Bauer亚塑性模型的改进

针对Gudehus-Bauer亚塑性模型不能考虑中主应力影响,在Gudehus提出的响应包络线理论基础上,提出了在模型的非线性项乘以一个考虑中主应力的因子进行改进.这种改进增加了土体剪切时的强度,改变了土体受压时的变形.新模型对中主应力的变化在中主应力参数影响程度能够有一定反映.同时将改进后的模型与中主应力参数为常量的真三轴实验进行了比较.结果表明改进后的模型可以模拟中主应力对砂土强度和变形特性的影响,能够定量预测由于中主应力影响产生的体积应变.