多功能杀菌剂的合成及其性能研究

在现有季铵盐类杀菌灭藻剂上增加一个脂键，连接一个有机酸基团，合成一种兼具阻垢缓蚀功能的新型工业水处理用杀菌灭藻剂(多功能杀菌剂)，经一系列评价实验表明：新型杀菌剂是较理想的杀菌剂，在较低浓度下，对硫酸盐还原菌(SRB)及腐生菌(TGB)均有很好的杀灭效果，优于1227杀菌剂，同时还具有较好的缓蚀阻垢效果。     

模糊层次分析法在腐蚀影响因素分析中的应用

结合国内外对碳钢CO2腐蚀影响因素的研究成果,采用模糊层次分析法对影响输油管道 CO2腐蚀的因素进行定量分析,明确界定出这些因素对二氧化碳腐蚀影响的相对重要性(权重),为后续制定经济有效的管道内腐蚀防护措施提供了客观依据。     

魏氏组织对20#碳钢H2S应力腐蚀开裂性能的影响

文章对H₂S-CO₂-H₂O腐蚀环境下发生H₂S应力腐蚀的20^＃碳钢弯管（无缝钢管）进行了成分、组织、拉伸、硬度和应力腐蚀开裂等性能的试验研究，并与同材质、同时投产、腐蚀环境基本相似而未发生应力腐蚀开裂的在役弯管及未使用的新弯管作对比，结果表明魏氏组织是引起20^＃钢发生应力腐蚀开裂的主要原因；正火能消除魏氏组织，降低钢的应力腐蚀开裂敏感性。     

N-油酰基肌氨酸钠对除盐水缓蚀性能的探讨

对N-油酰基肌氨酸钠单体的缓蚀性能以及与常用除盐水缓蚀剂的协同作用作了探讨,发现在一定浓度下,单体对经过加氨调节后的高温除盐水(氨后除盐水)有良好的缓蚀作用,且与大多数除盐水缓蚀剂有良好的协同效应。在此基础上研制了一种复合药剂,并对其缓蚀、阻蚀性能作了研究。动电位极化曲线扫描图谱表明,该复合药剂属于抑制阳极腐蚀的阳极型缓蚀剂,其适用的水质条件为[Cl~-+SO_4~(2-)]不超过50 mg／L,pH不低于8.0；与阻垢剂复配,可以适用于含Ca~(2+)不超过45 mg／L的水质条件。     

Intergranular corrosion of a light aircraft aluminum alloy propeller

Examination of the wreckage of a light aircraft revealed that approximately 20 cm was missing from one tip of the aluminum alloy propeller. Fractographic and metallographic examination of the remaining portion of the propeller revealed extensive grain-boundary separation in the vicinity of the fracture, and grain edges and corners rounded by corrosion on the fracture surface. Energy dispersive X-ray analysis (EDXA) revealed fluorine on, and in the vicinity of, the fracture surface. In the ensuing litigation, it was asserted that the crash occurred because the propeller fractured in flight as the result of intergranular attack caused by the use of a fluorine-bearing cleaner.     

泡沫夹克管的防水与保温

针对辽河油田应用泡沫夹克管道的情况，从泡沫夹克管的制作和敷设施工直到设计等环节，结合泡沫夹克管防腐保温的机理，并从理论与实践相结合角度出发，提出导致泡沫夹克管腐蚀损坏的最主要原因是管道保温层漏水，进而提出了在设计和施工过程中提高泡沫夹克管质量的措施。     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

核电材料在模拟反应堆环境中应力腐蚀破裂测试技术与性能评价

简要介绍了采用慢应变速率试验，Ｕ型弯曲和Ｃ形环试验等技术，分别对８００合金，３０４和３１６及３１６Ｔｉ不锈钢Ａ５３３Ｂ压力容器用多在模拟核反应堆环境中的应力腐蚀破裂敏感性性进行的试验研究的一些主要结果；并结合电化学测试和表面膜俄歇电子能谱分析结果进行了讨论。     

湿硫化氢环境下的球罐腐蚀状况分析

在湿硫化氢环境下 ,尤其储存介质中的硫化氢含量超标时 ,很容易对储存容器壳体 (含焊缝和母材 )造成硫化氢应力腐蚀或氢鼓包。作者较仔细分析了 1 0 0 0m3 丙烯球罐产生硫化氢应力腐蚀开裂和40 0m3 LPG球罐产生氢鼓包的原因。提出了此类设备在设计选材、设备制造、施工安装和使用维护等环节应注意的问题。