成形工艺对快速凝固Al—Cu—Mg合金组织和性能的影响

采用自制离心雾化装置制取了快速凝固LY12硬铝合金粉末,研究了以该粉末制成的真空热压件和挤压丝材的组织和性能。结果表明,所得粉末为泪滴状,其显微组织为树枝状晶和胞状晶。真空热压件密度高时所对应的强度高。450℃、10min、150MPa为较合理的工艺,此时粉末颗粒间结合密实,晶粒尺寸没有明显改变。在500℃热挤压时,挤压丝的组织已发生了再结晶,晶粒尺寸仍较细小。挤压丝材的抗拉强度达460MPa,其断口为韧窝状,韧窝尺寸小于3μm,且分布均匀。     

孔型热轧时轧制力的实用计算公式

采用修正系数法,利用板材在带刻槽的冲头进行深冲与平面冲头下深冲时的接触压力的比值确定孔型影响系数,进而推导出孔型热轧时轧制力的实用计算公式.     

熔融 NaCl-(Na,K)_2SO_4引起的 Fe-Cr 合金的热腐蚀

本文采用电化学方法研究了 Fe-Cr 合金在800℃、熔融 NaCl-(Na,K)_2SO_4中的腐蚀行为,并对腐蚀产物进行了观察和分析。结果表明,提高合金 Cr 含量可以改善合金耐蚀性能。氧化-硫化是Fe5Cr、Fe10Cr 合金腐蚀破坏的主要方式;氧化膜的熔融反应是 Fe20Cr、Fe25Cr 合金加速腐蚀的主要原因。同时,氧化膜的机械破裂也加速了合金的腐蚀。     

连铸坯红送热装应用效果分析

对加热炉用连铸坯红送热装效果的分析结果表明，该技术的应用可节能降耗，提高产量和加热质量。     

Phase Composition of Oxide Scales during Reheating in Hot Rolling of Low Carbon Steel

Low carbon steel was oxidized over the temperature range 1000‐1250°C in O₂‐CO₂‐H₂O‐N₂, O₂‐H₂O‐N₂, and O₂‐CO₂‐N₂ gas mixtures. Oxidation times were 12‐120 min. and the scales were 50‐2000 μm thick. The variations of these parameters were chosen to elucidate the phase composition of oxide scales under conditions similar to those of reheating furnaces in hot strip mills, using either thin slab casting or conventional casting and rolling technology. Two types of scales have been observed which are influenced by the furnace atmosphere, oxidation time, and temperature. The first type is a crystalline scale with an irregular outer surface, composed mostly of wustite (FeO), and a negligible amount of magnetite (Fe₃O₄). The second type is the classical three‐layer scale, composed of wustite (FeO), magnetite (Fe₃O₄), and hematite (Fe₂O₃). In general, the experiments showed that an increase in oxidation time decreased the percentage of wustite while the percentages of magnetite and hematite increased. A rise in oxygen concentration in the gas mixture increased the percentages of magnetite and hematite, confirming earlier experimental findings. In water vapour‐free atmospheres O₂‐CO₂‐N₂, the oxide scales had a low percentage of wustite, and high percentage of magnetite and hematite. Carbon dioxide showed a small influence at 1100°C, and a negligible one at 1250°C.     

热轧左旋螺纹钢的开发

介绍了在轧钢厂二车间开发顾客需要的Φ18、Φ20、Φ22的热轧左旋螺纹钢。在原有Φ18、Φ20、Φ22热轧圆钢的工艺基础之上做工艺设计，经实际生产轧制，其产品质量完全符合顾客要求。     

国家粮储库屋面防水APP卷材施工技术

针对国家粮食储备库的特点，就屋面防水APP卷材热熔法施工的施工准备及工艺流程进行了介绍，提出了具体的施工技术要点及质量通病的防治措施，取得了良好的施工效果。     

不锈钢热轧浊环水处理工艺设计

介绍了宝钢集团上海五钢不锈钢长型材热轧工程浊循环水处理的工艺设计，探讨了采用化学除油工艺、自动反清洗过滤器等技术和设备，处理不锈钢热轧浊环水的技术特点。     

膦化合物对加氢催化剂的影响

丁辛醇装置丁醛加氢催化剂在装置扩能投产以后热点上移 (失活 )的速率较快 ,针对催化剂老化的原因进行分析、判断 ,找出原因 ,采用相应的解决措施 ,可延长催化剂使用寿命 ,增加装置效益