含钡合金的生产及其对钢液脱氧行为的研究

介绍了含钡合金的生产状况。在MoSi2炉上对钢管钢进行了含钡合金脱氧行为的研究，然后在150tLF／VD精炼设备上进行了使用含钡合金的工业试验。研究中主要选取SiAlBa、SiCaBa、SiAlBaCa、SiAlBaCaSr及用于钙处理的SiCa包芯线，并选用Al和FeSiAl作为对比脱氧剂，分别考察了实验室条件下和实际生产过程中，采用钡系合金对钢液脱氧的全氧含量，脱氧产物的分布、尺寸和形貌，探讨了钡系合金脱氧和对夹杂物的变质作用的机理。     

自蔓延高温合成TiNi多孔体合金

为了开发新型的生体材料，本文对自蔓延高温合成TiNi多孔体合金——人造骨材料进行了研究。以单质钛粉和镍粉作原料，在氩气保护条件下，采用预热点燃模式和热爆模式制得了不同形态的多孔TiNi形状记忆合金。采用SEM和XRD分析了样品的孔洞特征和相组成，测试了其力学性能，并研究了合成条件参数与样品表面形貌和孔隙状态之间的关系。结果表明，用SHS法制备TiNi多孔体合金是可行的。     

Structure of rapidly solidified aluminum alloys

This paper is a summary of an extensive research program carried out by the authors on the structure of rapidly solidified aluminum alloys; and a comparison with the work of others also involved in this field. The paper discusses the changes in the dendritic and non-dendritic structure of the matrix at cooling rates from 10^–3 to 10¹⁰ K/s and discusses the hetergeneity of the structure caused by interdendritic-segretion during solidification.     

铝锂合金力学性能的各向异性

针对当前困扰铝锂合金实际应用的各向异性问题，概述关于铝锂合金中各向异性的表现规律，产生机理及对于降低各向异性所采用的方法等方面的研究现状和进展，对铝锂合金各向异性表现与微观组织结构的关系以及目前克服各向异性所采用方法的局限性进行分析。就此提出，若彻底解决这一问题则必须采用更先进的合金化方法及热加工工艺，研制新一代铝锂合金的观点和研究方向。     

镁合金表面喷铝防腐蚀层的微观组织分析

在AZ91D镁合金表面热喷铝，用以提高其表面的耐腐蚀性能。采用SEM，EPMA等方法对AZ91D表面喷铝扩散层的组织进行了仔细的观察与分析，发现在防腐蚀层上有大量的Mg17Al12相存在，且呈决状及非连续片状分布。经显微硬度测定，喷铝层硬度较镁合金基体高；腐蚀后这种相凸出于基体，比镁合金基体有较好的耐腐蚀性能。     

Oscillating Cup Viscosity Measurements of Aluminum Alloys: A201, A319 and A356

An oscillating cup viscometer was developed to measure the absolute viscosities of molten metals. Previous experiments established the capability of the apparatus to characterize the viscosities of molten nickel-based superalloys. However, modifications to the instrument and its theoretical analysis were required for reliable measurements on molten aluminum alloys, presumably due to their lower densities and lower viscosities. The theoretical literature for the fluid flow inside an oscillating cup is reviewed, and a working equation without any correction factor is developed for the improved viscometer. Some design parameters of the viscometer that directly affect the accuracy of viscosity estimation by using the working equation are discussed. A special vertical furnace was adopted to uniformly heat a longer cylindrical sample (10 mm inner diameter and 120 mm length) with a temperature difference of less than 2°C over the sample length. The measuring procedure was also improved to get more accurate motion parameters. It is estimated that the working equation and improved instrument provide an uncertainty of less than 4%. In addition, applications and experimental data are presented for pure aluminum and three aluminum alloys: A201, A319, and A356.     

Electroplating of nickel-cadmium alloys from alkaline solutions

The electroplating of Ni-Cd alloy coatings was carried out from alkaline baths (pH 10). For comparison, electroplating of the parent metals, Ni and Cd, was performed individually under the same conditions. The cathodic current efficiency for codeposition was high and decreased with increasing current density. The codeposition process is an anomalous type of plating with Cd being the preferentially deposited metal. The Ni content in the deposits increased with increasing current density. This increase in Ni content improves the corrosion resistance and microhardness of the deposits. X-ray diffraction analysis showed that the deposits consist of a mixture of Ni, β, γ, γ¹ phases.     

Crack growth in aluminium alloy sheet material under flight-simulation loading

Crack propagation tests were carried out on 2024-T3 sheet specimens to study the effects of omitting low-amplitude cycles from the gust-dominated TWIST load sequence (MiniTWIST) and the removal of small load ranges from the manoeuvre-dominated FALSTAFF load sequence (short FALSTAFF). In other tests high-amplitude loads of TWIST and MiniTWIST were truncated at different levels. The results are compared with data from similar test programmes, including crack initiation. Attention is paid to unstationary crack growth retardation and a transient retardation during initial crack growth started by an artificial crack.     

镍代钴矿用硬质合金的新进展

概述了镍代钴矿用硬质合金的国内外进展情况．     

Corrosion fatigue of extruded magnesium alloys

Corrosion fatigue tests were carried out on extruded AZ31 (3% Al, 1% Zn, 0.3% Mn, Mg—the rest), AM50 (5% Al, 0.4% Mn, Mg—the rest) and ZK60 (5% Zn, 0.5% Zr, Mg—the rest) Mg alloys in air, NaCl-based and borate solutions. N_sol/N_air ratios (the relative fatigue life) were used for the analysis of the corrosion fatigue behavior of Mg alloys in various environments, where N_sol and N_air are the numbers of cycles to failure in the solution and in air, respectively. Extruded ZK60 alloy reveals very high fatigue and corrosion fatigue properties in comparison with other alloys. However, it has the lowest relative fatigue life (N_sol/N_air 10⁻³–10⁻²) or the highest sensitivity to the action of NaCl-based solutions in comparison with that of AM50 and AZ31 alloys (N_sol/N_air 10⁻²–10⁻¹). Under the same stress, the corrosion fatigue life of extruded alloys is significantly longer than that of die-cast alloys (N_sol for extruded AM50 in NaCl is two to three times longer than that of die-cast AM50).