BEHAVIOR OF Mg AND ITS EFFECT ON MECHANICAL PROPERTIES OF CAST Fe_3Al ALLOYS

Proper addition of 0.002 wt-% Mg to cast Fe_3Al alloy may obviously improve the room andhigh temperature tensile properties.Auger spectra show that Mg segregates near grainboundaries as very thin layers.Observation under TEM reveals that a suitable amount of Mgenhances ability of cooperative internal deformation so that the dislocations will ease the con-tinuous slip deformation through grain boundaries.The fracture feature of Fe_3Al alloy is oftransgranular cleavage at room temperature and cracks initiate at grain boundaries.     

STUDY OF INTERFACES AND SURFACES OF YBa_2Cu_3O_(7-x)-Ag

Interfaces and surfaces of YBa_2Cu_3O_(7-x)(YBCO)-Ag have been studied by SEM-EDXand AES.No effect of Ag on 123 structure in X-ray diffraction pattern was observedfor 0.4 mol Ag doped YBCO.AES analysis indicated that Ag segregated on surfaceof YBCO and resulted in decrease of YBCO-metal lead resistance.In addition,solutionand segregation of Ag as elemental state were often appeared on interfaces and surfacesof high temperature annealed YBCO,whether elemental Ag or compound Ag_2O andAgNO_3 adopted as doping material.     

DISACCOMMODATION OF INITIAL SUSCEPTIBILITY IN AMORPHOUS Fe_(90-x)Ni_xZr_(10) ALLOYS

The disaccommodation(DA)measurements of initial susceptibility were performed inamorphous Fe_(90-x)Ni_xZr_(10)(x=10,20,30)alloys.The DA was measured for two differentamorphous states:as-quenched and pretreated at 537 K for 45 min.For all the as-quenched samples,in the isochronal spectra of DA a well defined relaxation peak around350 K is accompanied by a samll but distinct peak near the Curie temperature ofFe_(90)Zr_(10) phase(T_c=230 K).The reversibility and annealing effect on DA are analyzedwithin the framework of two-level model.The fits of the theory to the experimentaldata of reversible relaxation processes gave a spectrum,of activation energies and pre-exponential factor.     

升温率和应变率对30CrMnSi拉伸强度的影响

报道了硬度ＨＲＣ为２０和４０的两种３０ＣｒＭｎＳｉ材料在１００－９００℃的力学性能及升温率，应变率和热处理条件对抗拉强度，屈服强度的影响。在低温区，材料性能随温度的升高，呈现缓慢下降，其数值与常温相差不多，热处理状态对该区影响甚大，升温率有一定影响；在高温区，材料强度大大降低，其数值随温度变化不大，不同升温速率的影响及热处理状态影响消失；在中温区，材料性能随温度升高呈现快速下降趋势，热处理状态对材     

34CrMoA转子钢高温循环蠕变断口分形维数与蠕变性能的关系

用垂直剖面法测定了34CrMoA转子钢在550℃循环蠕变断口的分形维数,分析、比较了分形维数与蠕变性能的关系,结果表明,分形维数与断裂应变呈线性关系。     

THERMAL DEMAGNETIZATION AND RANDOMNESS OF DOMAIN NUCLEATION OF SINGLE PHASE Nd_2 Fe_(14) B

Based on the observation of temperature variation of both domain structure and magnetic con-trast.the thermal demagnetization and randomness of domain nucleation was discussed.     

硼对快凝Ni3Al组织结构及力学性能的影响

本文通过快凝及加硼合金化的方法改善金属间化合物Ni_3Al的韧性。实验表明:加入0.5-1.4at.-％的硼对Ni_3Al的塑性提高最有利。结构分析表明:在含1.37at.-％硼的Ni_3Al中,硼以Ni_(23)B_6弥散相及晶界偏聚方式存在;当硼量增至2.22at.-％时,硼以粗大的Ni_(23)B_6及NiB_(12)相在晶界处析出。无硼的Ni_3Al晶界为大角度晶界;当硼加至1.37at.-％时,Ni_3Al晶界以位错排列成亚晶界,以小角晶界形式存在。     

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Mg-Li ALLOY WITH Ca ADDITION

Mg-9wt%Li-2wt%Zn alloy was prepared and studied in this article. The addition of Ca to the alloy from 0.1wt% to 1wt% can refine the α-Mg and the best effect of refinement occurs when Ca content is 0.4wt%-0.5wt%. The billets can be rolled to thin sheets at room temperature, from which it is obvious that the addition of Ca improves alloys ormalin. while it decreases with the excess addition of Ca. The results also show that the ultimate tensile strength （UTS） and yield strength （YS） of the alloy with lwt% Ca may rise by 28% and 25%, respectively, however, the elongation decreases. It is clarified that the adsorption of proper Ca on the grain boundaries refines α-Mg and improves the tensile properties, but the presence of excess Ca and stable Ca2Mg6Zn3phase worsens the elongation.     

Intelligent optimal control for lead-zinc sintering process state

The intelligent integrated predictive model of synthetical permeability was established using the fuzzy classifier to combine the time sequence predictive model with the craftwork parameter predictive model. Then, the estimation model of bum-through point（BTP） based on pipe stress point（PSP） method and the predictive model of BTP were proposed. The optimal control of permeability and heat states was implemented by using the fuzzy expert controller with self-studying mechanism. The application of the intelligent control technique suppresses 17% of the fluctuation of synthetical permeability and 12% of the fluctuation of BTP, stabilizes the output and quality of sinter and settles the basis for the optimization of output and quality of sintering process.     

Dependence of dielectric properties on BT particle size in EP/BT composites

The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared.BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation.The dielectric properties, such as dielectric constant, dielectric loss and electrical breakdown strength, of the EP/BT composites were studied.The morphology of the composites was characterized by the means of scanning electron microscopy (SEM).The results show that the dielectric constant of the composites is much higher than the epoxy matrix at frequency range from 1 kHz to 10 MHz, and it is also obviously dependent on the size of BT particles.The electrical breakdown strength of the composites decreases with the increase of the BT content.The dependence of electrical breakdown strength on BT particle sizes was also discussed.