变形温度和变形程度对Ti－31合金性能和组织的影响

通过高温和室温拉伸试验，研究了变形温度和变形程度对Ｔｉ－３１合金板材性能和组织的影响。结果表明，合金在７５０～８５０℃的温度下变形５％～２０％空冷后，其室温机械性能均能达到材料的技术指标要求。并发现了材料在９００℃的临界变形区。     

冷成型模具低温锌系磷化

研制出适用于冷成型模具高硬度表面的低温锌系磷化工艺。其中磷化液含Zn(H2 PO4 ) 2 ·2H2 O 6 0g/L ,Zn(NO3) 2 ·6H2 O 90g/L ,NaNO2 1.5g/L ,稀土促进剂 0～ 1.0g/L ,游离酸度 4～ 6点 ,总酸度 70～ 75点。该磷化液在 4 0℃下 ,处理 30～ 4 0min后可获得厚约 10 μm的磷化膜。性能测试表明 ,其减摩、润滑性能良好 ,摩擦系数约降 0 .1,与未处理试样相比磨损量下降 96 % ,附着力 1级。     

Recrystallization/precipitation behaviour in microalloyed steels

Microalloyed high-strength low-alloy (HSLA) steels contain additions of Nb, V, Ti, or in combination, in amounts of 0.01 to 0.1 weight percent to improve mechanical properties, which are strongly dependent on the thermomechanical interaction taking place in the course of rolling mill processes. The recrystallizatian of hat-twisted austenite has been investigated in a cylindrical specimen (f 6×50 mm) machined from hat rolled plates of 0,052 wt % Niobium microalloyed steel. Continuous and interrupted torsion test were carried out in the temperature range 1123 K to 1173 K after a solution treatment of 1.5 minutes at 1423 K and torque-twist data were analysed. The various methods were discussed for obtaining results from torsion tests. The effect of precipitation kinetics was appreciated by way of connection t_p/t_p(red), where t_p is the experimental measured time for the peak stress and t_p(red) is the newly defined reduced time. The softening ratio X and time t_0.05R for start of static recrystallization were established.

The correlation between precipitation and recrystallization is presented as a graphs for chosen requirements (temperature of austenitization, carbon and niobium content and strain rate). If temperature goes below 850°C, the restoration processes are hardly suppressed, both are limited by diffusion and Nb(CN) precipitation, which are extended dynamically in the range of strains rates 10⁻² to 1 s⁻¹.

In the present paper, an attempt is made to derive the PRTT diagram and to define all mathematical equations for describing recrystallization times t_0.05R, t_0.5R, t_0.95R and t_0.05P for the start of precipitation. In real metal forming processes such as the hot rolling of plates or strips the knowledge of these parameters and results is extremely important for the the correct microstructure and sheet quality to be obtained.     

内外齿复合冷挤压成型实验研究

通过对轿车转向盘毂件内外齿进行的复合挤压实验研究 ,得到了新式复动式复合挤压模具结构 ,并确定了一种合理的成型工艺方案     

Synthesis and Evaluation of Blends Formed by Polymeric Crown Ethers and a Fullerene-Containing Primary Ammonium Salt in Organic Thin Films

The synthesis of a series of polymers and cyclopolymers bearing crown ethers of differing structure and affinities towards primary ammonium ions is discussed. These polymers have been tested in their efficiency to form structurally homogeneous thin films when blended with an amphiphilic C₆₀ compound containing a primary ammonium ion functional group. The X-ray reflectivity characterization of the films revealed that the polymer bearing the crown ether with the least affinity for primary ammonium ions, but having the highest degree of polymerization, is the most effective in forming structurally homogeneous thin films.     

枣35断块沙三段玄武岩储层特征及成藏条件分析

从地质、地震、测井及试油试采等方面入手，并采用新技术，对自来屯构造枣35断块沙三段玄武岩储层特征及成藏条件进行了分析。其结果为该区下一步勘探、开发及进一步研究奠定了基础。     

关于粉体成球机盘体几何形状的研究

通过对粉体小球在粉体成球机盘底上运动轨线的研究,利用Euler定理,结合其参数特点,得到了不同几何形状的盘底在成球过程中对粉体小球运动的影响,球面盘底较平面盘底更有利于成球的结论。     

梯恩梯-吉纳、地恩梯-太安装药体系自旋爆轰特性的研究

本文研究了梯恩梯-吉纳(TNT-DINA)和地恩梯-太安(DNT-PETN)体系的自旋爆轰现象,爆轰波是以低频脉冲方式传播.这些体系具有的爆速、爆热分别为DJ=7.3～7.4km/s和Qv=(5.40±0.01)MJ/kg.不同组成的爆速和爆压PJ通过SW程序计算.用扩散区的爆压P3和爆温T3来评估爆轰波的衰减和重新点火.敏化剂含量相同,梯恩梯-黑索金(TNT-RDX)体系的爆压PJ大于TNT-DINA的爆压,TNT-RDX体系的温度T3比TNT-DINA高60～100K.计算值与实验结果吻合较好.     

翻领成型器领口曲线的程序计算展开法

根据翻领成型器领口曲线的数学模型，介绍一种利用计算器复杂公式存贮的特殊功能，预编程序计算相关参数。然后画领口曲线展开图的方法。     

工业产品的艺术造型与技术美学

本文从技术美学的角度，广义的介绍了工业产品艺术造型的基本方法，着重从美学原则和色彩设计两方面论述产品造型设计的手法，以及技术美学在产品造型设计中的基本应用。