Two-step method to deposit ZrO2 coating on carbon fiber: Preparation,characterization, and performance in SiC composites

Recently, ceramic matrix composites reinforced by short carbon fibers (CFs) attracted increasing attentions. To further improve mechanical properties and oxidation resistances, CFs were subjected to oxidation and acidification followed by sol-gel dip-coating to deposit ZrO₂ on their surfaces. ZrO₂-C_f/SiC composites were fabricated by joint hot compression molding and sintering, compared to C_f/SiC and SiC prepared by the same method. Microstructural analyses indicated that ZrO₂ coatings were successfully deposited on CF surfaces, formed strong bonding and interfaces between CF and the matrix. Meanwhile, CFs were found uniformly distributed in SiC matrix with random orientations. Flexural curves of ZrO₂-C_f/SiC and C_f/SiC revealed the presence of “false plasticity” regions after sharp drops, which were quite different from brittle flexural behavior of SiC ceramic. Compression strength of the three samples showed step-up growth. ZrO₂-C_f/SiC exhibited the highest value, indicating the introduction of CFs and ZrO₂ coatings do have great influence on mechanical performances. After heat treatment, ZrO₂-C_f/SiC exhibited better oxidation resistance than C_f/SiC, with weight loss ratios estimated to ??3.76% and ??6.43%, respectively. These improved properties indicated that ZrO₂-C_f/SiC would be excellent alternatives to other existence materials under ultra-high temperature environments.     

Design and optimization of ceramic membrane structure: From the perspective of flux matching between support and membrane

The support flux was first investigated as a separate influencing factor for its effect on performances of ceramic filtration membranes. Three pre-membranes were prepared by tape-casting and then transfer-coated to supports to form dual-layer ceramic membranes after sintering. Experiments demonstrated that membrane layers with almost the same properties were obtained despite the huge difference in support flux. When the support flux increases from 3.120 to 97.53 m³m^?2h^?1, the flux of these three membrane series have increased by 75%, 186% and 228%, respectively. Experimental rules can provide structural design and evaluation from the perspective of permeability. The limit membrane flux of a certain system was derived according to the resistance distribution law of internal membrane structure and the Darcy's theorem. On this basis, a method for designing support flux was proposed. Furthermore, we present a criterion to quickly and easily evaluate the match between the support and the top layer, which is the ratio of membrane resistance to total resistance. Finally, the filtration resistance of penetration caused by suction of membrane particles into the support was measured for the first time, taking the advantage of the transfer-coating method that inherently free of penetration. Our works are expected to deepen the understanding of the ceramic membrane structure and provided guidance for its rational design and optimization.     

Hierarchical micro-nanostructured albite-based glass-ceramic for high dielectric strength insulators

A novel glass-ceramic material based on albite type Na-rich feldspar has been synthesized by conventional ceramic process. High crystallinity, >94%?Vol.% is obtained by fast sintering which allows energy saving processing. Albite is the main crystalline phase and tetragonal SiO₂ is a secondary phase. Electrical properties were examined by complex impedance, DC measurements, and dielectric breakdown test. Dielectric characterization shows a non-Debye type dielectric behavior with low dielectric constant, 4.6 at 1?MHz, low dielectric losses, (～10^?3 at 1?MHz, and a large dielectric strength, ～60?kV/mm), that it is the largest value reported in ceramic insulators. Those dielectric properties are attained by the low glassy phase content in the samples and their unique micro-nanostructure. All these properties make this novel material a very promising candidate in the market of ceramic electrical insulator, highlighting for high-voltage applications.     

非常规蛋白基木材胶黏剂研究现状及发展前景

介绍了动物和植物型非常规蛋白资源的种类及其制备蛋白基木材胶黏剂的研究现状和存在的问题,展望了非常规蛋白胶黏剂的发展前景。     

Al2O3/Yttria‐Stabilized Zirconia Hollow‐Fiber Membrane Incorporated with Iron Oxide for Pb(II) Removal

Removal by absorptive ceramic membranes can simultaneously absorb and separate metal ions from water. Alumina/yttria‐stabilized zirconia (Al₂O₃/YSZ) hollow‐fiber membranes, fabricated using phase inversion and sintering process, were deposited with iron oxide by an in‐situ hydrothermal process. The results showed that α‐Fe₂O₃ was produced and incorporated across the membranes. A reduction in flux was recorded with the deposition of α‐Fe₂O_3. However, it improved the adsorption capacity for heavy metal adsorption. The adsorption‐separation test demonstrated that the optimized membrane is able to completely remove Pb(II) ions after two hours.     

Preparation of highly crystalline titanium-based ceramic microfibers from polymer precursor blend by needle-less electrospinning

The aim of the present contribution is to study the influence of the post-spinning heat - treatment of single TiO₂/PVP precursor fibers on the properties and morphology of the final titanium-based microfibers. The post-spinning treatment conditions were: calcination in air at 450–600?°C and pyrolysis in argon at 1000–1700?°C. Calcination resulted in a production of anatase-rich and pure rutile fibers. The use of an alternative sintering method, the low-temperature plasma treatment, led to the crystallization of the composite Magnéli phases/polymer fibers. As a result of the same one precursor, pyrolysis at 1000?°C, the Carbon/TiO₂ composite fibers were obtained. Rising the treatment temperature in inert atmosphere led to the formation of the titanium carbide fibers. The formation process and all the obtained products were characterized by differential scanning calorimetry accompanied with thermogravimetric analysis (DSC/TGA), scanning and transmission electron microscopy (SEM, TEM), X-ray diffraction (XRD), and image analysis techniques.     

Effects of structural characteristics on microwave dielectric properties of low-loss (Zn1-xNix)ZrNbTaO8 ceramics

Low-loss (Zn_1-xNi_x)ZrNbTaO₈ (0.02?≤?x?≤?0.10) ceramics possessing single wolframite structure are initiatively synthesized by solid-state route. Based on the results of Rietveld refinement, complex chemical bond theory is used to establish the correlation between structural characteristics and microwave performance in this ceramic system. A small amount of Ni²⁺ (x?=?0.06) in A-site with the fixed substitution of Ta⁵⁺ in B-site can effectually raise the Q?×?f value of ZnZrNb₂O₈ ceramic, embodying a dense microstructure and high lattice energy. The dielectric constant and τ_f are mainly affected by bond ionicity and the average octahedral distortion. The (Zn_0.94Ni_0.06)ZrNbTaO₈ ceramic sample sintered at 1150?°C for 3?h exhibits an outstanding combination of microwave dielectric properties: ε_r =?27.88, Q?×?f?=?128,951?GHz, τ_f =?–39.9?ppm/°C. Thus, it is considered to be a candidate material for the communication device applications at high frequency.     

Kinetic,thermodynamic parameters and in vitro digestion of tannase from Aspergillus tamarii URM 7115

Tannase is an enzyme used in various industries and produced by a large number of microorganisms. The aim of this study was to evaluate tannase production to determine the biochemical, kinetic, and thermodynamic properties and to simulate tannase in vitro digestion. The tannase-producing fungal strain was isolated from “jamun” leaves and identified as Aspergillus tamarii. Temperature at 26°C for 67?h was the best combination for maximum tannase activity (6.35-fold; initial activity in Plackett–Burman design—15.53?U/mL and average final activity in Doehlert design—98.68?U/mL). The crude extract of tannase was optimally active at 40°C, pH 5.5 and 6.5. Moreover, tannase was stimulated by Na⁺, Ca²⁺, Mg²⁺, and Mn²⁺. The half-life at 40°C lasted 247.55?min. The free energy of Gibbs, enthalpy, and entropy, at 40°C, was 81.47, 16.85, and ?0.21?kJ/mol?·?K, respectively. After total digestion, 123.95% of the original activity was retained. Results suggested that tannase from A. tamarii URM 7115 is an enzyme of interest for industrial applications, such as gallic acid production, additive for feed industry, and for beverage manufacturing, due to its catalytic and thermodynamic properties.     

高温旋风除尘器的设计

在PTA(精对苯二甲酸)的生产过程中,工艺废气经尾气膨胀透平机降压后进入RTO蓄热式焚烧炉将有毒有害的有机物焚烧分解后排入大气,为了达到粉尘的排放标准(小于120mg/m~3),在焚烧炉之后加上这台高温烟气除尘器,废气经除尘后达到了排放标准,而且最大程度地减少了热量损失,实践证明此项改造是成功的。文章探讨如何进行高温烟气除尘器的设计,并介绍了高温多管陶瓷旋风烟气除尘器的结构。