矿床技术经济评价

简要介绍了矿床技术经济评价中的评价阶段及条件。论述了评价的原则、方法和要素。指出在技术经济评价中 ,地勘费是否计入投资 ,对评价的结果影响甚大     

赣西浒坑钨矿床成矿岩体的磷灰石和锆石微量元素特征及其对成岩成矿的指示

赣西地区浒坑钨矿是我国华南钨、锡、铜多金属成矿区与中生代岩浆活动密切相关的典型矿床之一。对浒坑钨矿床中与成矿有关的白云母花岗岩开展了锆石U-Pb定年、磷灰石和锆石原位微量元素研究,结果表明：赋矿白云母花岗岩的成岩时代为（152.3±1.73）Ma;磷灰石具有特殊的“M”型REE球粒陨石标准化配分模式,富F和Mn,贫Cl和Mg;锆石具有高Th/U比值,REE球粒陨石标准化配分模式亏损LREE、富集HREE。锆石微量元素（Ce、U和Ti）温度计和氧逸度计结果表明,锆石形成于岩浆早期高温（800 ℃）和低氧逸度条件下。研究认为,浒坑赋矿花岗岩在演化初期经历了强烈的矿物结晶分异,矿床的形成可能与还原性高分异岩浆演化相关。     

Initial stages of tin electrodeposition from sulfate baths in the presence of gluconate

Tin electrodeposition in its initial stages in acid sulfate/gluconate baths was studied with varying tin and gluconate concentrations using potential-controlled electrochemical techniques. The deposit morphology was observed by scanning electron microscopy (SEM). A comparison with tin electrodeposition from acid sulfate baths in the absence of gluconate was also carried out. Use of a highly acidic bath leads to nonuniform deposits, even in the presence of gluconate; at pH 4 deposits are uniform, brilliant and suitable for finishing applications. Tin crystallites have a well defined morphology which depends on bath agitation conditions. In the absence of agitation, the crystallites have the same tetragonal shape as in a sulfate bath without gluconate.     

Quantitative X-ray powder diffraction analysis of clay minerals in Australian coals using Rietveld methods

The mineralogy of clay-rich mineral matter isolated from a range of Australian bituminous coals has been evaluated in quantitative terms from X-ray powder diffraction (XRD) patterns using a Rietveld-based data processing technique. The chemical composition of coal ash derived from this mineral matter has been calculated and compared to the directly determined composition of the ash prepared from the same coal samples. Although there are some minor differences due in part to uncertainty regarding the actual composition of several minerals, the compositions indicated by the two methods show a relatively high correlation, suggesting that the Rietveld technique provides mineralogical analyses that are consistent with independently determined chemical data. Comparison of the normalised clay mineral percentages from the Rietveld analysis to quantitative interpretations based on a peak intensities in glycolated and heat-treated oriented aggregates of the respective clay fractions also shows a high correlation, confirming mutual consistency of the two different mineralogical analysis methods. Such quantitative mineralogical data are significant to a range of coal exploration, mining and utilization activities, including seam correlation, material handling and ash and slag formation in combustion processes.     

Ni-ZrO2纳米复合电铸层抗高温氧化性能的研究

通过间歇式抗高温氧化实验,建立了纯镍电铸层和N i-ZrO2纳米复合电铸层高温氧化动力学模型,分析了电铸层表面和横截面的形貌,测定了电铸层的组织结构。结果表明,N i-ZrO2纳米复合电铸层抗高温氧化性能明显优于纯镍铸层,复合电铸层表面生成的氧化膜晶粒细小且致密,并且该氧化膜较薄,产生的内应力较小,与复合电铸层的黏附性较好。     

熔制玻璃用坩埚抗热震性的改进

在粘土 -蜡石质玻璃用坩埚的配方基础上 ,研究了蜡石的粒径和加入量的变化对试样抗热震性的影响。结果发现 :减小蜡石的粒径与加入量均可提高试样的抗热震性 ,但减小蜡石粒径对提高试样的抗热震性更有效 ;在配料中引入少量的蓝晶石细粉 ,可明显提高试样的抗热震性。     

适用于摩托车零件的多层镍电镀工艺

概括目前我国摩托车零件电镀所用镀层组合，对照有关金属覆盖层的国家标准，认为摩托车零件应用多层镍组合，并提供了工艺配方。     

Reforming of methane with carbon dioxide over supported bimetallic catalysts containing Ni and noble metal: I. Characterization and activity of SiO2 supported Ni–Rh catalysts

Cobalt catalysts supported on silica aerogel have been prepared using sol–gel chemistry followed by drying under supercritical ethanol conditions. Three different loadings of cobalt were synthesized: 2, 6, and 10% by weight. Transmission electron micrographs indicate that the metallic cobalt exists as discrete particles 50–70 nm in diameter for the 2 and 6% loadings. The 10% catalyst shows long needles of cobalt. BET and BJH measurements indicate that the catalysts retain the silica aerogel properties of high surface area (∼800 m²/g), large pore volume (∼5 cm³/g), and an average pore diameter in the mesoporous regime (∼25 nm). The catalysts were evaluated for Fischer–Tropsch activity in a laboratory-scale packed bed reactor. All three catalysts were active with the 10% Co catalyst achieving more than 20% CO conversion which corresponds to a rate of 1.53 g CO per g-cat per hour. The catalysts were selective for the C₁₀₊ hydrocarbons with more than 50% of the carbon contained within this fraction. A significant portion of the C₉–C₁₅ hydrocarbon product was observed as 1-olefins which reflects the enhanced mass transport within the very porous aerogel support.     

Effect of the use of mineral filler on the properties of concrete

Engineers of the concrete technology are increasingly concerned with the material passing through a sieve of the size under 0.149 mm. Materials called very fine aggregate or mineral filler may affect the performance of concrete in an either positive or a negative way. Discussions on aggregate containing very fine material are vitally important. Washing the aggregate residue has been the sole way to solve this matter to date. This is mainly based on the debatable opinion that materials of this kind are regarded as clay material. The goal of the study was to determine how the content of mineral filler might affect properties of concrete. Two types of aggregates with different amounts of cement and mineral filler were used. Basically, mineral filler replaced sand. The effect of applying different amounts of mineral filler on concrete was then determined. The addition of 7-10% of mineral filler to fine aggregate (0-2 mm) was found to considerably improve the properties of concrete.     

离子束加速电压对真空电弧沉积Ti(C,N)涂层性能的影响

利用等离子辅助真空电孤沉积技术分别在高速钢片和单晶硅片制备了Ti(C,N）涂层，通过X-射线衍射和扫描电镜研究了不同离子加速电压对单晶硅片上涂层结构和组织形貌的影响，并测定了高速钢片上涂层的显微硬度，同时进行了耐磨性实验。结果表明：涂层主要由TiN和Ti(C,N）组成，随着离子束加速电压的增大，涂层的沉积速度增大，Ti(C,N）的衍射峰不断宽化，晶格尺寸发生变化，但其表面形貌不受影响；当离子束加速电压为1500V时，涂层有较高的耐磨性和显微硬度，当离子束加速电压为2500V时，涂层的耐磨性和显微硬度都有所下降：