MAGNETORESISTANCE EFFECT OBSERVED IN Fe／Mo MULTILAYERS PREPARED BY ELECTRON BEAM EVAPORATION

The Fe/Mo multilayers were prepared by electron beam evaporation, the micro structure and magnetic properties of the multilayers were studied by X-ray diffraction, vibrating-sample magnetometer (VSM) et al. The experimental results revealed that the Fe/Mo multilayers in our experimental conditions behaved magnetoresistance effect with a sharp peak on magnetoresistance (MR) ratio curve, and magnetoresistance is easily saturated at low applied magnetic fields. For [Fe(1.5nm)/Mo(1.0nm)]4,2 multilayers, MR ratio could arrive to 0.1%. The antiferromagnetic interlayer coupling could be observed in some films at room temperature. The strength of the antiferromagnetic interlayer coupling J in the films is low because of the low saturation field Hs. The relationship between magnetic properties and micro structure was also discussed in this paper.     

[Co／Ti],[Co／Cu（Ni）]多层膜的结构与磁性

用双对向靶溅射方法制备了具有非晶磁性的「Ｃｏ／Ｔｉ」３０，「Ｃｏ／Ｃｕ（Ｎｉ）３０」两组多层膜，分别用Ｘ射线衍射，透射电镜和振动样品磁强计做了结构和磁性测量，在以非晶Ｃｏ和Ｃｉｕ－Ｎｉ合金构成的「Ｃｏ／Ｃｕ（Ｎｉ）」多层膜中，发现饱和磁化强度Ｍｓ随非磁性层厚度ｄｓ的增国发生振荡变化；在以非晶Ｃｏ和Ｔｉ构成的「Ｃｏ／Ｔｉ」多层膜中，ＭＳ和则随ｄｓ的增加而减小。     

TC4/Ni/ZQSn10-2-3扩散连接

采用镍箔做中间层,在真空下对TC4和ZQSn10-2-3进行扩散连接.使用扫描电镜对接头的界面组织进行了研究.确定TC4/Ni/ZQSn10-2-3接头的界面结构是TC4/β-Ti/Ti2Ni/TiNi/TiNi31Ni/Cu(Cu,Ni)/ZQSn10-2-3.通过最优工艺试验,确定最佳工艺参数为连接温度830℃,连接压力10 MPa,连接时间30 min.此时接头最大抗剪强度为135 MPa,接头断口为带有一定塑性的结晶状形貌.通过x射线衍射对断口分析认为,断裂位于TC4/Ni界面处的金属间化合物TiNi3层.     

SiCw/6061Al铝基复合材料粉末夹层瞬间液相扩散焊接工艺

采用质量比为2:1的铝铜混合金属粉末作为中间夹层,通过TLP扩散焊接工艺焊接了SiCw/6061Al铝基复合材料.结果表明,在真空度为1.33 Pa、焊接预紧力20 MPa的条件下,最佳工艺参数为:焊接温度620℃,保温时间60 min.采用扫描电镜研究了焊缝的微观组织,发现较低温度下焊缝存在较多的孔洞.用电子探针分析焊缝周围元素分布,结果表明,在焊缝处富集较多的氧元素和镁元素.这是因为基体铝合金中的镁与铜粉颗粒表面的氧化铜以及焊接工件表面的氧化膜(Al2O3)发生置换反应,生成细小的MgO和Al2MgO4颗粒.该反应有利于减小氧化膜的影响,提高接头强度.     

3DEC modeling on effect of joints and interlayer on wave propagation

1 Introduction Natural rock mass is not homogeneous, and it is full of various weak planes with different structures and different geological mechanisms, such as fractures, joints, and cracks. These structural weak planes seriously hinder and affect the …     

胶层厚度和耐湿老化对夹层玻璃中PVB胶与玻璃界面粘结性能的影响

夹层玻璃的耐久性和安全可靠性与其界面粘结性能密切相关。本文首次提出了十字交叉法测量夹层玻璃中PVB胶与玻璃的界面拉伸和剪切粘结强度,分别研究了加载速度效应、PVB胶层厚度效应和湿度老化等的影响。结果表明:测量夹层玻璃中PVB胶与玻璃粘结强度的加载速度应选取5mm/min。当胶合层厚度相同时,界面拉伸粘结强度高于其剪切粘结强度,PVB胶层厚度越大,其拉伸粘结强度和剪切粘结强度都逐渐越低。单层PVB胶片与玻璃之间的界面拉伸粘结强度最大值为11.49MPa。耐湿老化对玻璃与PVB胶的界面粘结强度影响不大,即使老化60天后,其拉伸粘结强度也仅下降12.3%。     

含薄夹层盐岩地层套管等效应力分析

采用FLAC3D三维有限差分软件,建立了套管-水泥环-层状地层三维有限差分模型,分别研究了泥岩夹层弹性参数、厚度对含薄夹层盐岩地层界面处以及层内套管等效应力的影响。夹层厚度对上下岩层中的套管等效应力都有影响,泥岩和盐岩力学特性上的不匹配导致二者界面附近套管受力不均衡;夹层较厚时,套管等效应力相对较小;与泥岩相比,盐岩中套管等效应力较大,套管更容易发生屈服;夹层弹性参数不同时,夹层弹性模量越低,界面处以及夹层层内套管等效应力越大。该研究为含薄夹层盐岩地层套管设计和井筒安全性评价提供了理论依据。     

四川盆地侏罗系页岩层系岩相类型及储集特征

陆相页岩层系岩性复杂、非均质性强,制约了储层甜点优选和探井部署。为查明四川盆地侏罗系页岩层系不同岩相类型的储集特征和含气能力,以元坝地区Y2井自流井组大安寨段为例,采用有机碳含量测定、全岩X射线衍射、岩石薄片鉴定、聚焦离子束扫描电镜、高压压汞—氮气吸附联合测定以及物性分析等手段,划分了大安寨段二亚段（后文简称大二亚段）页岩及夹层的岩相类型,并针对不同岩相类型开展储集物性、孔隙结构、含气性及可压性研究,在此基础上评选了优势岩相和岩相组合。结果表明,Y2井大二亚段页岩层系可划分为3大类6亚类页岩岩相,2大类6小类夹层岩相以及3种宏观岩相组合。页岩孔隙类型以粘土矿物层间孔、方解石溶蚀孔等无机孔为主,为页岩气的赋存提供了储集空间。计算页岩总含气量为2.59～4.38 m³/t,游离气平均占比67 %,具有较好的勘探潜力,但优势岩相的脆性矿物含量仅为50 %,可压性较差。综合评价认为,AB-Ⅰ型岩相组合中页岩页理和纹理发育,生烃条件好,含气量和游离气比例较高,存在可压性较好的夹层,是元坝地区Y2井大二亚段最有利的勘探储层类型。     

纵向非均质砂层内石油运移和聚集的模拟实验

通过不同充注方式层内非均质砂层油运移和聚集的二维模拟实验表明:正韵律砂层中,不同非均质程度,即不同渗透率级差的砂层,在不同的充注方式和能量条件下,油气运移路径和通道与含油层位具有差异。当渗透率级差较小时,中部渗透率中等的砂层比下部渗透率大的砂层和上部渗透率小的砂层更容易成为油气运移路径和通道,成为含油层;当渗透率级差较大时,下部渗透率大的砂层比中部渗透率中等的砂层和上部渗透率小的砂层更容易成为油气运移路径和通道,为含油层。反韵律砂层中,渗透率级差较小时,上部渗透率大的砂层和中部渗透率中等的砂层比下部渗透率小的砂层更容易成为油气运移路径和通道,为含油层。在稳态充注条件下,侧向充注和断层充注含油层位基本相同,含油饱和度在垂向上表现为"韵律"特征;断层幕式充注下,含油面积更大,中等渗透率和大渗透率砂层均为含油层,且在大渗透率砂层中运移效率较高。     

X80M级准1219 mm×18.4 mm螺旋埋弧焊管全壁厚补焊工艺研究

利用夏比冲击、显微硬度和拉伸试验对6种焊材在相同补焊工艺下的全壁厚刨透补焊焊缝进行了性能对比研究,筛选出焊缝性能较优的对应补焊焊材。并以此焊材作为X80M级φ1219 mm ×18.4 mm螺旋埋弧焊管焊缝缺陷手工修补用专用焊材,进行了不同补焊工艺参数的全壁厚刨透补焊试验,并对补焊焊缝进行低温冲击试验,通过比较确定出X80M级φ1219 mm×18.4 mm螺旋埋弧焊管全壁厚刨透补焊工艺方案。结果表明,上海焊接器材厂生产的SH J557焊条用于X80M级φ1219 mm×18.4 mm螺旋埋弧焊管焊缝缺陷全壁厚刨透手工修补更为合适,各项性能指标更高;确定的补焊工艺参数合理可行,确保了补焊焊缝的质量和钢管的批量化生产。