HCl氧化物MOS结构质子辐照诱导的界面陷阱效应

用微分电容法研究质子辐照HCl氧化物铝栅MOS结构诱导的界面陷阱,栅氧化层在1 160℃很干燥的、含0～10％HCl的气氛中热生长而成,质子辐照能量为120～300keV,注入总剂量范围为8×10~(13)～1×10~(16)p/cm~2。结果表明,辐照诱导的界面陷阱能级密度随质子能量、剂量增加而增加。然而,氧化层中掺入6％HCl时,辐照诱导的界面陷阱明显减少。这样,已能有效地改变MOS器件的抗辐照性能。实验结果可用H~+二级过程解释。     

含微量元素铜焊锡丝的研制

在６０／４０的锡铅焊料中加入０．２％左右的铜，凝固后具有均匀细小的共晶组织，其熔点为１８３℃，焊点强度和扩展率均高于未加铜的６０／４０锡铅焊料，并且含铜的锡铅焊料在焊接时，对铜烙铁头和微细铜线了小的熔蚀性。     

Morphology and Forming Mechanism of Rare Earth Inclusions During Solidification of Steel

ＭｏｒｐｈｏｌｏｇｙａｎｄＦｏｒｍｉｎｇＭｅｃｈａｎｉｓｍｏｆＲａｒｅＥａｒｔｈＩｎｃｌｕｓｉｏｎｓＤｕｒｉｎｇＳｏｌｉｄｉｆｉｃａｔｉｏｎｏｆＳｔｅｅｌ￥ＺｈａｉＱｉ－Ｊｉｅ（ＤｅｐａｒｔｍｅｎｔｏｆＭｅｔａｌｌｕｒｇｙ，ＵｎｉｖｅｒｓｉｔｙｏｆＳ...     

Pit to crack transition in stress corrosion cracking of a steam turbine disc steel

Long term exposure tests have been carried out on a 3 NiCrMoV steam turbine disc steel in the form of cylindrical tensile test specimens self-loaded to 90% of σ_0.2 and exposed to three environmental conditions, viz. deaerated pure water, aerated pure water, and aerated water containing 1.5 ppm of chloride ion. Pitting occurred in all environments but the density and depth of pits in the chloride-containing medium was markedly greater. No cracking was observed in deaerated pure water but cracks initiated in aerated water between 13 and 19 months and in less than 7 months in aerated 1.5 ppm Cl⁻ solution. The probability of a crack initiating from a pit of specific depth in aerated solution could be described well by a Weibull function. Profiling of pits and cracks in the disc steel tested in aerated 1.5 ppm Cl⁻ solution showed that there while there were many cracks with a depth greater than that of the corresponding pit the depth of some cracks was smaller than that of the corresponding pit, suggesting that cracks do not necessarily initiate from the bottom of the pits. The growth rate of short cracks emerging from pits appeared greater than that of long cracks in fracture mechanics specimens.     

Thickness-dependence of stoichiometry and microstructure characteristics in correlation with conductivity type of CdTe films

CdTe films were prepared by physical vapour deposition on a substrate at room temperature (RT) as well as on a cold (LT) one using low deposition rate. The thickness-dependence of stoichiometry revealed an abrupt decrease in the Cd/Te ratio as the thickness increases. Change of thickness did not affect the type of observed (111) crystallographic texture, only the degree of preferred orientation is enhanced as the film grows. The internal strain was negligible while the crystallite size increased rapidly at small thickness (up to 400 nm), and less thickness dependence was observed with further film growth. However, thickness dependence of lattice parameters showed a minimum and a maximum at approximately 300 nm in the case of RT and LT, respectively. The observed change in conductivity from n- to p-type and its vital correlation with the stoichiometry and structural characteristics were presented. Based on thickness dependence of stoichiometry and lattice parameters as well as the conductivity type, formation and annihilation of lattice defects were considered.     

RE／S值对控轧低碳Mn－Nb－RE钢硫化物成分和形貌的影响

用扫描电镜测定了含０．０４１％～０．０７６％ＲＥ的低碳Ｍｎ－Ｎｂ－ＲＥ钢中硫化物的成分、大小和形貌。ＲＥ／Ｓ值为２．８～３．０时，钢中的硫化物充分变质。     

调质状态下40Cr钢的焊接

在合理制定焊接工艺的基础上，采用R307珠光体耐热钢焊条成功地进行40Cr钢在调质状态下的焊接，解决了通常采用25—13型奥氏体焊条焊接出现的焊缝强度低、焊接接头性能差的问题。     

纳米SnO_2固体的相变内耗和模量

系统测量了不同颗粒尺度纳米 SnO_2固体的内耗和模量,发现60℃附近存在一个内耗峰,对应的模量出现异常.烧结温度升高,峰高变化不明显,模量异常减弱.当烧结温度高于400℃时,模量曲线在-15℃附近出现异常,这种模量异常随烧结温度升高而加强,对应的内耗曲线出现一小峰.初步认为,60℃附近内耗峰和模量异常与纳米固体中的结构再有序有关,而-15℃处的模量异常为结构相变引起.     

非均相成核中间相炭微球的形成过程及其结构演变

以含有喹啉不溶物的煤焦油沥青为原料，在410℃、不同反应时间下获得一系列中间相炭微球(MCMB)和小于0．5μm的碳质颗粒(SCP)。通过对中间相沥青的软化点、族组成和MCMB、SCP的形貌及MCMB断面结构的分析，认为非均相成核MCMB的形成和生长过程不同于均相成核的融并生长过程，而是SCP碳质颗粒的构筑过程，我们称之为“球形基本单元构筑”过程。在MCMB生长过程中，体系的黏度对SCP的形成和MCMB的生长起着重要的作用。非均相成核MCMB的内部结构不是三种模型结构(“地球仪”型、“洋葱”型和“同心圆”型)中的任一种，而是炭层具有收缩点的复杂结构，并且球体的结构不具有“继承性”，即随着反应时间的延长而不断发生变化和调整。MCMB内部分子在球体生长过程中的主要变化趋势是分子的不断缩合长大，而不是分子片层的平行趋向。     

高速硬车削淬火钢的实验研究

通过改变高速车削淬火钢（Cr12）的切削用量，对切削力、切削温度、加工表面质量等进行了研究，结果表明合理选择切削用量，高速硬车削淬火钢可显著提高生产率及加工表面质量，并在一定程度上可取代磨削加工。