超低水泥浇注料在宝钢环形加热炉炉底的应用

高铝质超低水泥浇注料在宝钢环形加热炉炉底使用结果表明，该浇注料具有热态强度高、结构均匀致密、耐磨损、抗侵蚀等特点。槽底厚度损耗比磷酸盐结合捣打制降低３５％左右。     

5000t/d水泥窑Kalina循环余热发电系统应用

根据氨-水混合物的物性,讨论了不同热源温度下Kalina循环适用的工质参数匹配,以5 000 t/d新型干法水泥生产线为研究对象,将Kalina循环系统用于水泥窑余热发电.通过系统的流程仿真模拟,得出了Kalina循环在给定废热条件下的做功能力及系统热力学性能.计算结果表明,Kalina循环系统比Rank ine循环系统发电功率提高20.4%,热效率绝对值提高2.66%,效率达到44.31%.     

Binding materials of dehydrated phases of waste hardened cement paste and pozzolanic admixture

Fly ash (FA) and ground granulated blast-furnace slag (GGBFS) were added to improve the performances of regenerated binding materials (RBM) which refer to dehydrated phases with rebinding ability of waste hardened cement paste. Flowability tests, compressive strength tests, SEM, TG-DSC, and non-evaporable water content tests were employed to study the performances of the combined binding materials and the interactions between RBM, FA, and GGBFS. Results show that adding FA or GGBFS can improve the workability of RBM paste, and GGBFS has positive effects on strength of RBM. Pozzolanic reactions happen between RBM, FA, and GGBFS. And the activation effect of RBM to FA and GGBFS is superior to that of P.O grade-32.5 cement, especially at earlier ages, because of the high reactive f-CaO existing in RBM. On the advantages of the synergetic effects of RBM and pozzolanic admixtures such as FA and GGBFS, new combined binding materials can be prepared by blending them together. Funded by the National Science Foundation of China(No. 50508034)     

Strength of limestone-based non-calcined cement and its properties

A new type of cement was prepared with ground limestone powder, blastfurnace slag, steel slag and gypsum without calcination. The fraction of ground limestone powder in the cement was as high as 40 wt%–60 wt% without Portland clinker. All of its physical properties can meet the requirements of masonry cement standards. The impact of limestone content on physical properties of the cement and determined its impact on law was investigated. The steel slag can excit the aquation activity of this cement effectively, and the influence of its quantity on the strength of the materials was studied, which shows that the optimum quantity of mixing is 10%. By way of changing the different content of the lime stone by quartzy sample, the law of the compression strength and the PH value was determined, confirming that the lime stone can promote the early aquation of the slag and improve the early strength. The main hydration product of this cement is calcium aluminate hydrate, ettringite and calcium silicate hydrate, as indicated by XRD and SEM analysis.     

混凝土底板温度及温度应力影响参数分析

借助参数化设计语言(APDL)分析了水泥品种及标号、结构尺寸、外界约束对混凝土底板温度及温度应力的影响.结果表明:与普通硅酸盐水泥525相比,普通硅酸盐水泥425、矿渣水泥425可使底板最大拉应力分别减低约21%、37%;底板平面尺寸增大,压应力几乎保持不变,拉应力增大,发展较为平缓;底板厚度越大,出现最高温度的龄期越晚,底板降温时持续高温时间更长,且温度应力随厚度增大而增大.     

铝基原料对磷光粉SrAl2O4：Eu^2＋，Dy3＋发光性能的影响

采用高温固相反应法,分别以高纯氧化铝、自制纯净铝酸钠溶液及精制工业铝酸钠溶液为原料合成了黄绿色SrAl2O4：Eu^2＋Dy^3＋磷光粉,通过测量其激发光谱、发射光谱及余辉时间,考察了不同铝基原料对磷光材料发光性能的影响．结果表明,所制备的3种磷光粉的激发光谱和发射光谱的波长基本一致,激发光谱位于300-450nm之间,主发射波长在510nm左右．用工业铝酸钠溶液制备出的长余辉材料的发射强度不低于用另外两种原料制备的长余辉材料,余辉时间比用另外两种原料制备的长余辉材料稍长,效果较好,采用工业铝酸钠溶液制备铝酸盐基长余辉材料,可以降低能耗、节约成本．     

早强剂对掺硅灰的水泥砂浆强度与结构影响的研究

探讨了不同早强剂对掺硅灰的水泥砂浆强度及微观结构的影响.结果表明：掺入不同的早强剂均可提高掺硅灰的水泥砂浆早期强度,且对其1 d抗压强度的增强效果优于3 d.其中掺入适量的硫酸钠可迅速生成大量的钙矾石晶体,提高水泥砂浆的密实度,同时促进了硅灰的火山灰反应,明显提高了掺硅灰的水泥砂浆的早期强度,但早强剂对掺硅灰的水泥砂浆后期强度影响不大.3种早强剂对掺硅灰的水泥砂浆早期强度增强作用从大到小的顺序依次为硫酸钠、氯化钙、三乙醇胺,其中硫酸钠掺量为3%时增强作用最佳.     

矿渣掺量对水泥性能的影响

采用矿渣与熟料分别粉磨再混合的方式,研究了不同掺量和不同细度的矿渣对水泥强度和凝结时间的影响,确定了水泥中矿渣的最佳掺量.     

熟料粒度对骨粉/磷酸钙生物骨水泥结构与性能的影响

采用新方法首次将动物骨中的鱼骨引入到磷酸三钙和磷酸氢钙等原料体系中通过高温烧结制备磷酸钙基生物骨水泥（CPC）,以柠檬酸和柠檬酸钠的缓冲液为固化液、按一定的液固比制备固化试样,通过扫描电子显微分析（SEM）和力学性能测试等方法,研究了熟料粒度对其固化试样结构与抗压强度的影响.结果表明：制备过程中骨水泥粉末的粒度对其固化试样的微观结构及其抗压强度有着较为显著的影响,通过调整骨水泥粉末的粒度可达到优化其固化试样的微观结构和改善其力学性能的目的.     

中等浓度含硅铝酸钠溶液深度脱硅过程物理化学性质的研究

通过对脱硅过程中含硅铝酸钠溶液表面张力和黏度的测定,研究脱硅温度、氧化铝浓度、苛性比等因素对溶液的表面张力和黏度的影响.实验结果表明：低温、高浓度、高苛性比的溶液表面张力和黏度较大,反之则较小.通过XRD检测手段对脱硅后的渣相进行分析,用衍射峰与结构的关系解释溶液的表面张力和黏度的变化对硅量指数的影响.