急冷烧结法制备六钛酸钾晶须的工艺研究

以分析纯K2CO3和工业纯TiO2为原料,采用急冷烧结法制备了六钛酸钾晶须,利用扫描电镜、X射线衍射仪等手段,研究了二次保温时间和钛源化合物类型等对其形貌及物相的影响.结果表明:以金红石型二氧化钛为钛源,TiO2/K2CO3的摩尔比为5.5∶1时,1200℃保温3h,然后在高于1114℃二次保温2h,再经急冷后进行解离、抽滤和烘干,即可得到分散性好、物相纯度较高的六钛酸钾晶须.     

Effect of Water on Adsorption Behavior at Polymer/γ-Fe2O3 Interface

The adsorption behavior of a hydroxylated polymer onto γ-Fe₂O₃ particles in a tetrahydrofuran/water solvent system was investigated. The saturation adsorption of the polymer decreased with an increase in the water content of the solvent system, and the degree of dispersion of the magnetic particles in the paint also decreased. It was shown that the water located not at the interface between the particles and the solution but in the solution. Water interacted with the polymer and increased the radius of gyration of the polymer in solution. Thus, the polymer did not interact with the particles, and the particles were prevented from having a high dispersion.     

异丁烯-马来酸酐共聚物的合成研究

以马来酸酐(MA)和异丁烯(IB)为原料,采用自由基溶液聚合方法合成MA-IB共聚物.筛选了溶剂体系和引发剂类型,并考察了反应温度、引发剂用量和单体质量分数对聚合产物的分子质量的影响,最后研究了不同分子质量的产品对分散氧化铁性能的影响.结果表明:在单体质量分数为40％,反应温度为70℃,引发剂用量为1％的条件下合成的MA-IB产品具有较好的性能.     

纳米TiO2光催化材料分散性及其降解效率研究

采用苯丙乳液、锐钛型纳米级二氧化钛和表面活性剂,制得应用于道路交通设施中的光催化净化大气环保材料,在日光照射下降解汽车尾气中的有害气体.研究了分散方法、分散剂的种类、分散剂的浓度及分散时间对纳米TiO2分散性的影响,利用透射电镜对其分散情况进行观察,并对其分散机理进行探讨与研究.结果表明,采用合理的分散方法和适量的表面活性剂能有效改善纳米TiO2在水中的分散度,提高颗粒的稳定性,增强了光催化材料的光降解能力,有效提高了对汽车尾气中有害气体的降解能力.     

氧化锌粉体在水中的分散及稳定性研究

初步制得了纳米ZnO的较为合适的高分子分散剂PE;利用自制高分子分散剂PE及合适的乳化剂对表面改性的纳米ZnO进行分散,加适量水配成适用于织物后整理的工作液;用激光粒度分布仪对整理剂和工作液的粒径分布进行了表征.结果表明,无论是整理剂还是工作液,都有很好的稳定性.对整理剂,24 h前后粒径在270 nm以下的粒子百分数分别为73.6%和61.0%;对工作液,24 h前后粒径在270 nm以下的粒子百分数分别为93.0%和77.2%.     

腐殖酸钠对石英分散性能影响的机理研究

采用沉降试验、zeta电位、FTIR光谱和颗粒间相互作用分析,研究了介质pH值和腐殖酸钠对石英分散性能的影响及作用机理。结果表明,随着pH值升高,石英在水介质中的分散性随之提高,表面zeta电位随之下降。当pH值为11.5,腐殖酸钠用量为0.5 g/L,进一步提高了石英的分散性,表面zeta电位则下降至-67.5 m V;光谱结果表明,石英谱线在2923 cm-1处出现了-CH2的不对称伸缩振动吸收峰,2855 cm-1处出现了-CH2的对称伸缩振动吸收峰,说明石英与腐殖酸钠发生了物理吸附作用;颗粒间相互作用结果表明,当pH值为11.5,颗粒间双电层排斥能高于范德华吸引能,同时腐殖酸钠增强了石英表面的亲水性,提高了水化膜作用势能。     

喷雾干燥改性白果粉的分散性及流动性研究

对喷雾干燥改性白果粉的流动性及分散性进行了研究。以麦芽糊精、β-环糊精、阿拉伯胶为改性辅料,研究辅料品种、辅料添加比例对白果粉分散性及流动性的影响。还研究了水温对改性白果粉分散性的影响。结果表明:β-环糊精为最佳辅料,在60℃时,分散性随β-环糊精比例增加而增加,当β-环糊精与白果粉比例为4:10时,效果较好;在40℃时分散性随β-环糊精比例增加呈先增后减的趋势,当β-环糊精与白果粉比例为3:10时,效果较好。改性白果粉的分散性随着水温的增加呈先增加后减小的趋势,最大分散性出现在40~60℃范围内。     

不同粒径分布的纳米二氧化钛在醋酸纤维素超滤膜中的分散性能研究

在醋酸纤维素(CA)基料中添加不同浓度经表面改性的不同粒径的纳米二氧化钛(TiO_2)粒子,其中包括平均粒径10、40nm以及这两种粒子的质量比2∶1的级配混合粒子,利用相分离法制备了无机-有机纳米复合CA超滤膜,通过测定膜的孔隙率、孔径分布、渗透性能以及膜表面的电镜扫描(SEM)表征进而研究不同粒径分布对纳米粒子在铸模液中分散性能.结果表明:在不引起纳米粒子团聚的前提下,在CA中添加的纳米粒子粒径越小,复合膜的性能越好;而级配粒子的添加量高于单一粒径粒子的添加量.当膜的渗透性能达到最佳值时,上述3种不同粒径分布的粒子添加量分别为4%、3%、5%(质量分数),而成膜后孔隙率均可达到70%以上,纯水的透水量可分别达到527、443、591L/(m~2·h).这说明颗粒级配分布促进了纳米粒子在铸模液中的分散性能.由于两种粒子混合均匀后存在粒径带双峰分布颗粒级配,在剪切条件下,纳米粒子不易因粒子表面作用引起团结,而团聚在一起的级配颗粒却容易受剪切剥离分散,从而起到促进纳米粒子在聚合物溶液中的分散作用.     

Core‐shell structure of carbon nanotube nanocapsules reinforced poly(lactic acid) composites

In this study “core‐shell” structure of carbon nanotube (CNT) nanocapsules, which aimed at toughening poly(lactic acid) (PLA) were designed by a synthetic strategy consisting of two reaction steps. The first step was to produce reactive chemical bond to bridge CNTs and PLA. So coupling agent KH570 was used to modify CNTs (CNTs‐KH570). The second step involved ring open polymerization of lactide (LA). Lactide polymerized into PLA under catalysis and meanwhile grafted onto CNTs via KH570 (CNTs‐KH570‐PLA). Thus, the CNTs nanocapsules were constructed. Fourier transform infrared spectroscopy (FTIR) showed coupling agent KH570 succeeded in linking CNTs and PLA during LA polymerization. In addition, scanning electron microscopy (SEM) and transmission electron microscope (TEM) indicated CNTs dispersed homogeneous in PLA matrix and the compatibility between them was excellent. The mechanical test also suggested the designed nanocapsules had good effect on toughening PLA composites. This research found one economical and simple way to improve PLA mechanical properties and further broaden its application in many fields. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44919.     

纳米二氧化钛粉体在水中的分散行为

为使纳米TiO2在水溶液中良好稳定地分散,采用透光率法对粒径约为30 nm的锐钛型TiO2粉体在水溶液中分散行为进行了研究,并对其进行粒度分布、电位的测定。实验结果证明:加入量为二氧化钛质量0.8%的硅酸钠作为分散剂,调节pH值为8~10,超声分散约10 min可以使纳米二氧化钛在水溶液中获得良好稳定的分散。通过测定分散相在分散介质中的电位,验证了pH值影响纳米TiO2粉体在水中的分散行为。