研究了一种热稳定性好的中温固体氧化物燃料电池密封玻璃. 研究表明, 此密封玻璃的热膨胀系数(室温～631℃)为9.8×10^-6/K, 与8YSZ电解质的热膨胀系数10.0×10^-6/K(室温～631℃)接近, 并且在700℃热处理300h后, 该密封玻璃的热膨胀系数几乎没有变化. 粘度实验表明, 玻璃在700℃下具有足够的刚性, 适合于运行温度在700℃左右SOFC的密封. 化学相容性的研究显示, 在700℃下与8YSZ反应300h后没有发现显著的界面反应.     

翅片管路焊接接头断裂原因分析

通过KYKY2800扫描电镜等技术手段对翅片管路焊接接头进行失效分析。分析表明,焊缝与2#环管的焊趾处存在有不连续的咬边,造成应力集中;在交变应力的作用下于咬边处产生微裂纹,并沿一定方向扩展（同时材料的不均匀性也为裂纹的扩展提供了有利条件）,直至最后疲劳断裂,造成失效。最后提出了预防措施。     

Forecasting with unequally spaced data by a functional principal component approach

The Principal Component Regression model of multiple responses is extended to forccast a continuous-time stochastic process. Orthogonal projection on a subspace of trigonometric functions is applied in order to estimate the principal components using discrete-time observations from a sample of regular curves. The forecasts provided by this approach are compared with classical principal component regression on simulated data.     

Characterization of residual stresses from cold expansion using spatial statistics

Residual stress fields from cold expansion have been widely used to extend the fatigue life of aircraft structures. However, the spatial statistical character of these residual stress fields has not been established and has not been incorporated in current analysis methods. The objective of this study was to establish a spatial statistical method to quantify the residual stress field around a cold expanded hole. A framework called the Spatial Analysis of Residual Stress (SpARS) was developed utilizing spatial correlation, response surface modelling techniques and statistical resampling methods to characterize the residual stress field. Our results showed that tolerance bounds on residual stress can be quantified using this method. We also demonstrated the SpARS method using recently published round robin case studies. The newly developed model will be useful for aircraft structural fatigue crack growth analyses to incorporate residual stress fields for extending inspection intervals for fatigue and fracture critical structures.     

Mechanisms of the FMR1 Repeat Instability: How Does the CGG Sequence Expand?

A dynamic mutation in exon 1 of the FMR1 gene causes Fragile X-related Disorders (FXDs), due to the expansion of an unstable CGG repeat sequence. Based on the CGG sequence size, two types of FMR1 alleles are possible: “premutation” (PM, with 56-200 CGGs) and “full mutation” (FM, with >200 triplets). Premutated females are at risk of transmitting a FM allele that, when methylated, epigenetically silences FMR1 and causes Fragile X syndrome (FXS), a very common form of inherited intellectual disability (ID). Expansions events of the CGG sequence are predominant over contractions and are responsible for meiotic and mitotic instability. The CGG repeat usually includes one or more AGG interspersed triplets that influence allele stability and the risk of transmitting FM to children through maternal meiosis. A unique mechanism responsible for repeat instability has not been identified, but several processes are under investigations using cellular and animal models. The formation of unusual secondary DNA structures at the expanded repeats are likely to occur and contribute to the CGG expansion. This review will focus on the current knowledge about CGG repeat instability addressing the CGG sequence expands.     

油基岩屑残渣自悬浮支撑剂的制备及性能评价

目的为了安全有效地处置和利用页岩气开采过程中产生的油基岩屑残渣,采用其烧结陶粒支撑剂,同时,为提高支撑剂在清水中的悬浮性能、改善支撑剂在裂缝中的分布、简化压裂施工工艺、提高压裂增产效果,进行了自悬浮支撑剂的制备与研究。 方法通过聚合反应将聚丙烯胺树脂包覆在支撑剂表面,制得膨胀型自悬浮支撑剂,研究了交联剂用量、单体量、合成温度对自悬浮支撑剂膨胀性能的影响。 结果覆膜材料配比(质量比)为:m(陶粒)∶m(丙烯酰胺)∶m(N,N′-亚甲基双丙烯酰胺)∶m(过硫酸铵)∶m(N,N,N′,N′-四甲基乙二胺)=10.000∶2.000∶0.002∶0.020∶0.031时,自悬浮支撑剂性能最佳,其膨胀倍数为4.3,沉降速度为45 mm/s。 结论覆膜支撑剂自悬浮功能的实现主要与聚丙烯酰胺树脂的溶胀有关,树脂的体积膨胀和聚丙烯酰胺分子链向外延伸引起溶液黏度的增加,提升了支撑剂在溶液中的沉降阻力。该研究对拓宽油基岩屑烧结支撑剂的应用范围、提高油基岩屑残渣资源化利用产品附加值有十分重要的意义。      

变电站不锈钢金属膨胀节泄漏原因分析

从化学成分、断口电镜扫描、X射线能谱和金相试验等方面,分析了沧州供电公司某变电站电流互感器不锈钢膨胀节泄漏的原因,认为泄漏是不锈钢膨胀节外表面点状电化学腐蚀所致,而该膨胀节表面状态的不连续性,周围潮湿的空气介质及空气介质中富含S、Cl等元素,是造成膨胀节外表面点状电化学腐蚀的主要原因。     