Compressibility of the polymer crystal

Results for the compressibilities of a wide range of polymer crystals along the fibre- and the transverse crystal axes are presented. Good agreement is found between the theoretical and the experimental results of different authors.     

碳钢贮热水箱的模拟腐蚀试验及涂层耐蚀性能研究

碳钢贮热水箱长期在30～80°C温变的热水环境中工作,易受到热水及水中杂质的腐蚀。研究了不同温度下Q235钢在自来水及含100μg/mLNaCl的自来水中的腐蚀速率。对裸钢及其涂覆相同厚度的不同涂层──酚醛环氧(自制)、钛纳米聚合物和改性聚乙烯后在70°C自来水中的极化曲线进行了比较。采用动电位扫描极化曲线测量和电化学交流阻抗谱法(EIS)分别对涂覆不同涂层的Q235钢进行了耐蚀性能研究。结果表明,3种防腐涂层均具有较佳的抗热水性,耐蚀能力较强,适宜对Q235钢贮热水箱进行防护。     

P_2O_5影响Na_2O-B_2O_3-SiO_2系玻璃结构与性质的特殊性

本文通过不混溶温度的确定,分相玻璃沥滤速率的测定以及NMR定量分析,研究了P_2O_6对Na_2O-B_2O_3-SiO_2系统玻璃结构和沥滤性质的影响。结果表明,P_2O_5在很大程度上促进钠硼硅分相玻璃的沥滤并非压抑“硼反常”所致,而是由以下三种因素综合作用的结果:(1)P_2O_5促进了钠硼硅玻璃的分相,使连通富硅相骨架尺寸增大;(2)P_2O_5的加入使富硅相骨架间隙中沉积的SiO_2量减少,减小了可溶相扩散阻力;(3)P_2O_5也使可溶相的溶解速率加快。     

PVA基活性碳纤维的研制

探索了由民用大丝束聚乙烯醇纤维(PVAF)试制活性碳纤维(ACF)的可能性,以开辟新的原料路线,降低产品成本。PVAF首先用脱水剂处理,脱水剂浓度为10%(质量),然后在200—300℃进行热处理,处理后的纤维再经预氧化和碳化活化转化为ACF,ACF的收率为37.7%,比表面积为1050m~2/g。此外,还探索了用O_3处理PVAF。用差热、热失重和红外等手段对产物进行了表征,推论了相应的反应机理。结果表明:经适当处理的PVAF可制得具有较好吸附性能的ACF。     

涤纶短纤维生产现状及发展趋势

对目前国内外涤纶短纤维生产的企业规模和工艺技术现状进行了分析比较，并论述了涤纶短纤维生产的经济规模和今后的发展趋势。     

Preparation,characterization, and some physical properties of polypropylene/poly(methyl acrylate)‐grafted glass wool composites

Polypropylene/poly(methyl acrylate)‐grafted glass wool (PMA‐g‐GW) mixes were prepared. The polymerization process was carried out using potassium persulfate (PPS) and PPS/acetone sodium bisulfite (ASBS) as a redox‐pair initiation system at 60 and 70°C. The effect of using PPS or PPS/ASBS on the grafting percent and conversion percent reveals that the conversion percent values on using PPS as an initiator are higher than those of PPS/ASBS, while in the case of grafting, the inverse is true, that is, using PPS as an initiator gives grafting percent values lower than those that can be obtained using PPS/ASBS. The dielectric properties, thermal diffusivity, specific heat capacity, and thermal conductivity of PP loaded with modified glass wool as a function of different types and concentrations of initiators—used in the grafting polymerization process, namely, PPS and the redox initiating system—were also studied. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 723–732, 2003     

Monodisperse polymer/metal composite particles by electroless chemical deposition: Effect of surface functionality of polymer particles

Micron‐sized polymer particles were coated with layers of nickel compounds by plating electrolessly in the presence of aqueous solutions of nickel chloride, sodium hypophosphite, sodium citrate, and ammonium chloride at elevated temperature. The uniform functional polymer particle could be obtained by seeded polymerization. To investigate the effect of surface functionality on the conditions for nickel deposition, the polymer particle was functionalized with the thiol group. From morphological observation, it was found that the mode of nickel deposition was greatly dependent on the surface functionality of the polymer particle. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 420–424, 2003     

侧链为亚乙氧基结构的EVOH梳型聚合物的合成

以乙烯-乙烯醇共聚物(EVOH)为原料，制备了一种主链为疏水的聚乙烯链段，侧链具有亚乙氧基结构的多羟基梳形聚合物，用元素分析法、凝胶渗透色谱法、核磁共振谱法对其进行了结构表征；用热重分析法和示差扫描量热法对其热学性能进行了表征。结果表明，接枝后产物的玻璃化转变温度在-52--40℃之间，熔点在55～600℃之间，由于侧链的引入破坏了EVOH的结晶，因此梳形聚合物的热分解温度比EVOH降低了约20℃。     

Polyaniline as corrosion inhibitor for iron in acid solutions

In recent years, polymer amines have been studied as an efficient corrosion inhibitor for iron in acid media. In this article, the performance of water soluble polyaniline as corrosion inhibitor for iron in 0.5M H₂SO₄ has been evaluated by potentiodynamic polarization, linear polarization, and electrochemical impedance spectroscopy and compared with the performance of the aniline monomer. It has been found that polyaniline is an efficient inhibitor, since the maximum efficiency of 84% has been observed at a concentration of 100 ppm, whereas the monomer has accelerated the corrosion. FTIR studies have shown that the polyaniline is strongly adsorbed on the iron surface and inhibits the corrosion effectively. However, aniline has been found to improve the passivation tendency of iron at higher concentrations. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 2144–2153, 2006