Formation of CaO-TiO2-MgO-Al2O3 dual phase inclusion in Ti stabilized stainless steel

The formation of CaO-TiO2-MgO-Al2O3 dual phase inclusion in 321 stainless steel was investigated in the laboratory. The result indicated that the condition for the formation of CaO-TiO2-MgO-Al2O3 in 321 steel is [Ca]〉0.001wt%, [Ti]〉0.1wt%, and [A1]〉0.01wt%. The mechanism is the following： Al2O3 inclusion turns into CaO-Al2O3 after Ca-Si wire is fed into the molten steel; [Mg] is then obtained by reducing MgO in slag or crucible wall by [Al] and [Ti]; finally CaO-Al2O3 inclusion is changed into CaO-TiO2-MgO-Al2O3 by the reaction with [Mg], [Ti], and [O] in the molten steel simultaneously.     

华龙国际大厦混合结构构件及节点设计

论述了矩形钢管混凝土柱钢框架、混凝土核心筒结构在江西华龙国际大厦的应用，介绍了矩形钢管混凝土混合结构总体设计、节点大样及构造。     

合金钢中白点缺陷超声反射波辨析

通过对进口合金钢中白点缺陷超声反射波形的分析研究，为白点缺陷的判定提供借鉴，保证工程材料的使用安全。     

冷镦钢新型脱氧剂的试验研究

采用新型复合脱氧剂和脱氧工艺对冷镦钢进行工业性试验研究，研究结果表明：冷镦钢采用AlMg合金脱氧获得了良好的脱氧效果，可以避免形成大型夹杂物，提高钢水纯净度。     

时间分解光谱技术在钢铁分析中的应用

研究了单火花光谱在不同采样时间段分析灵敏度与窗口的关系,P、S、Al、Ni、Ti、B、Mg、Sb、Pb、As、Bi、Ta、Sn应用TRS技术检出限明显降低,而C、Si、Mn、Cr、Mo、V、W、Co、Nb则不显著;合适的采样窗口能提高Sb的分析准确度,Mg则可减少背景波动带来的影响,Cu可扩大分析线性范围;采用TRS技术在诸有效元素中分析灵敏度可提高1.36～5.00倍,能更好地满足品种钢的研究开发与生产检验的需求.     

现代钢铁生产流程的优化与发展

现代钢铁生产流程进入新世纪后正加快优化的进程.紧凑、高效和智能化是主要发展方向;新流程发展和现有流程的改造相结合,是流程变革的主要特点;与多学科新技术的结合,将成为发展的主要特征;符合社会可持续发展的要求是钢铁流程优化最重要的目标.     

65Mn热轧窄带钢的试轧

介绍了天津钢铁有限公司带钢厂开发带钢新品种,用65Mn弹簧钢试轧优质碳素结构钢钢带的工艺情况。总结了试轧过程存在的问题,提出了改进措施。     

钢筋混凝土用钢筋SD390产品开发

介绍了日标对SD390的要求及其开发过程。     

AOD冶炼脱碳反应模型与计算机模拟

AOD冶炼中,终点碳和终点温度的命中率是提高生产率和产品质量的关键。由初始温度,初始成分及补加合金量等原始数据,通过本模型可预报要达到目标终点碳所需要的脱碳时间以及相应的终点温度。本模型计算得到的终点碳与实际终点碳,在同等条件下,两者极为接近,可作为一般AOD冶炼中预报终点碳与脱碳时间关系之用。通过分级调整O2、Ar、N2气比例得到最佳脱碳效果,终点碳命中率可提高到98％以上,最高温度可以控制不超过1750℃,延长炉衬寿命。