PVC发泡制品用助剂--优泡剂

分析了PVC发泡制品成型加工时存在的缺陷,说明了添加优泡剂可弥补PVC发泡制品的缺陷,提高泡孔质量,介绍了优泡剂的品种和使用场合及使用量。     

Prediction model of compressive strength development of fly-ash concrete

Based on experimental results concerning the compressive strength development of concrete containing fly ash, the authors derived an estimation equation for compressive strength development. The equation can express coefficient , which indicates the activity of fly ash as a binder, in the form of a function of age, fly-ash content, and Blaine specific surface area of fly ash.

This equation is capable of explaining the increases in the early strength due to fly ash in place of part of fine aggregate, the decreases in the early strength due to fly ash in place of part of cement, the increases in the long-term strength due to pozzolanic reaction, the relationship between the fly-ash replacement ratio and the ratio of strength increase/decrease, and the effect of fly ash's Blaine specific surface area on the strength.     

CGA560增强助磨剂在水泥粉磨中的应用研究

研究了CGA560增强助磨剂在水泥粉磨中对台时产量和水泥质量的影响。试验结果表明:在磨机状况不改变的条件下,CGA560增强助磨剂的加入可提高磨机产量10%-30%;同时可有效减少过粉磨现象,优化水泥颗粒级配,提高了水泥粉磨细度及比表面积;因而使水泥强度等性能得到了明显改善和提高。     

胶层厚度对拉伸试样应力分布影响的数值分析

运用弹塑性有限元法研究了胶层厚度对承受拉伸载荷的对接接头胶层内应力分布的影响．三维有限元法数值分析的结果表明，随胶层厚度减小，胶层中正应力SZ与剪应力SYZ的分布趋于均匀；而对正应力SY而言，胶层厚度为0．15mm时，其边缘峰值应力最低。     

Rheology of cementitious paste with silica fume or limestone

The rheological behaviour of cementitious pastes where cement has increasingly been replaced by densified silica fume (SF), untreated SF or limestone has been studied. The effect of SF on the flow resistance, taken as the area under the flow curve, was found to depend on the dispersing ability of the plasticizer as illustrated by pastes with naphtalene sulphonate-formaldehyde condensate (SNF) and polyether grafted polyacrylate (PA).The gel strengths increased with increasing SF replacement of cement independently of plasticizer type. The cementitious gel strength was, however, depending on the type of SF since pastes with densified SF developed lower gel strengths than pastes with untreated SF. This phenomenon was attributed to agglomerates in the densified SF which remained unbroken by the mixing and measurement sequence.Both flow resistance and gel strength decreased with increasing limestone replacement. Thus, silica fume may have an advantage over limestone filler as stabilizing agent for self-compacting concrete preventing segregation upon standing and reduced form pressure due to a more rapid gel formation.     

Zonal disintegration phenomenon in enclosing rock mass surrounding deep tunnels -- Elasto-plastic analysis of stress field of enclosing rock mass

The zonal disintegration phenomenon (ZDP) is a typical phenomenon in deep block rock masses. In order to investigate the mechanism of ZDP, an improved non-linear Hock-Brown strength criterion and a bi-linear constitutive model of rock mass were used to analyze the elasto-plastic stress field of the enclosing rock mass around a deep round tunnel. The radius of the plastic region and stress of the enclosing rock mass were obtained by introducing dimensionless parameters of radial distance. The results show that tunneling in deep rock mass causes a maximum stress zone to appear in the vicinity of the boundary of the elastic and the plas-tic zone in the surrounding rock mass. Under the compression of a large tangential force and a small radial force, the rock mass in the maximum stress zone was in an approximate uniaxial loading state, which could lead to a split failure in the rock mass.     

大体积混凝土温升与强度增长的试验研究

针对大体积混凝土结构构件实体强度与普通标准养护试块强度发展规律间的差别等问题,通过研究实际工程尺寸试件温度场的分布和实验室混凝土变温养护试验,以不同养护制度下的试块强度得出了大体积混凝土结构实体强度的发展规律,为工程施工提供了依据,成功地解决了工期与质量的矛盾,取得了较好的技术经济效果.     

高速钢表面PN＋PVD复合处理工艺和性能研究

采用多弧离子镀设备,在高速钢W18Cr4V上先进行等离子氮化,再沉积TiN薄膜,研究了不同渗氮温度和时间对PN＋TiN薄膜组织和性能的影响。结果表明,温度为500℃左右和时间为2h以上条件下对W18Cr4V进行渗氮处理后再沉积TiN薄膜,可以得到最佳的薄膜表面显微硬度（1800～2000HV0.05）和膜／基结合力（50N）,涂层耐磨性也得到明显提高。     

Oxidation and Fracture Strength of High-Purity Reaction-Bonded Silicon Nitride

Reaction-bonded Si₃N₄ (RBSN) made from high-purity Si powder is unusually resistant to degradation caused by exposures to air for up to 50 h at temperatures up to 1400°C. The weight gain during oxidation of this SiH₄-originating RBSN is approximately 10 times less than conventional RBSN. Contrary to normally observed strength degradations, room-temperature strengths of this high-purity, oxidized RBSN (avg = 435 MPa, max. = 668 MPa) remained at their unusually high, as-processed levels after 1000° and 1400°C oxidizing exposures. Fracture toughness values were unaffected by oxidation ( K _IC= 2.3 to 2.4 MPa · m^1/2). This superior oxidation resistance results from the high purity and the small diameter pore channels (0.01 to 0.06 μm) achieved in this SiH₄-originating RBSN.     

高功率移相器粘接工艺初探

主要介绍了粘接技术在高功率铁氧体移相器上的应用。通过对其工艺途径及关键工序的控制，提出了采用粘接技术完成高功率移相器铁氧体的连接，不仅可以大量地缩短工作时间，而且可以使制造成本大幅度降低。