Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

HA/β-TCP plasma sprayed coatings on Ti substrate for biomedical applications

The present work focuses on the fabrication of βTCP (β-tricalcium phosphate) and HA/βTCP (hydroxyapatite/β-tricalcium phosphate) composite coatings by plasma spraying. The starting powders were produced via solid-state method using 2 wt% MgO to stabilize βTCP phase. The synthesized powders were preliminarily granulated to be used by the plasma spray process. Coatings obtained on titanium substrates are uniform and well adherent but due to the high temperature and cooling rate typical for plasma spraying process, βTCP phase is almost totally transformed into the α allotrope. Thermal treatment at 800 °C allows the reconversion of the phase αTCP→ βTCP. It is therefore possible to produce coatings with tuneable dissolution properties by selecting the proper initial powder mixture and the specific thermal treatment.     

Macrophage Immunomodulation Through New Polymers that Recapitulate Functional Effects of Itaconate as a Power House of Innate Immunity

Itaconate (ITA) is an emerging powerhouse of innate immunity with therapeutic potential that is limited in its ability to be administered in a soluble form. A library of polyester materials that incorporate ITA into polymer backbones resulting in materials with inherent immunoregulatory behavior is developed. Harnessing hydrolytic degradation release from polyester backbones, ITA polymers result in the mechanism specific immunoregulatory properties on macrophage polarization in vitro. In a functional assay, the polymer-released ITA inhibits bacterial growth on acetate. Translation to an in vivo model of biomaterial associated inflammation, intraperitoneal injection of ITA polymers demonstrate a rapid resolution of inflammation in comparison to a control polymer silicone, demonstrating the value of sustained biomimetic presentation of ITA.     

Study of the effect of BDMA catalyst in the epoxy novolac curing process by isothermal DSC

Epoxy novolac/anhydride cure kinetics has been studied by differential scanning calorimetry under isothermal conditions. The system used in this study was an epoxy novolac resin (DEN431), with nadic methyl anhydride as hardener and benzyldimethylamine as accelerator. Kinetic parameters including the reaction order, activation energy and kinetic rate constants, were investigated. The cure reaction was described with the catalyst concentration, and a normalized kinetic model developed for it. It is shown that the cure reaction is dependent on the cure temperature and catalyst concentration, and that it proceeds through an autocatalytic kinetic mechanism. The curing kinetic constants and the cure activation energies were obtained using the Arrhenius kinetic model. A suggested kinetic model with a diffusion term was successfully used to describe and predict the cure kinetics of epoxy novolac resin compositions as a function of the catalyst content and temperature. Copyright © 2003 Society of Chemical Industry     

渣油胶质和沥青质在分散型催化剂作用下的临氢热反应行为

采用四组分法从辽河减压渣油中分离出胶质、沥青质，分别考察了它们在分散型催化剂作用下的临氢热反应行为。结果表明，胶质、沥青质一方面要裂化生成较轻的产物；另一方面也要发生缩合反应生成较重的反应产物以及甲苯不溶物。渣油在临氢热反应过程中，沥青质是生焦的主要来源，其次才是胶质。比较了热反应生成的沥青质与原生沥青质之间以及热反应生成的胶质与原生胶质之间化学组成的区别，结果表明，反应生成的沥青质和胶质较原生的沥青质和胶质分子结构缩合程度高，并且反应苛刻度越高，缩合程度也越高。     

Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

Ni-Al2O3纳米复合电镀工艺的初步研究

初步研究了复合电镀各工艺条件：电流密度、镀液pH值和温度以及搅拌方式对Al2O3纳米微粒在镍基复合镀层中含量的影响。研究表明：电流密度增大不利于提高镀层中纳米微粒的含量；pH值增大也明显使复合量降低;镀液温度升高，镀层中微粒的复合量随之略有改变；电镀时，加强搅拌或适当改变搅拌方式，可以使复合镀居中的纳米微粒含量提高。还利用扫描电镜及能谱对Ni-Al2O3镀层表面进行了观察与分析。     

Oxidation of Hastelloy-XR Alloy for Corrosion-Resistant Glass-Coating

The oxidation behavior of Hastelloy-XR alloy was investigated to obtain the optimum surface condition for corrosion-resistant glass-coatings. The surface morphology of oxide scales changed significantly with variation of temperatureand oxygen partial pressure (po2 ). The oxidation kinetics was mainly parabolic independent of oxidation conditions.The oxide scales were consisted of inner Cr2O3 and outer spinel layers. The phase component of spinel layers wereMn1.5Cr1.5O4 and (Mn,Ni)(Cr,Fe)2O4 for the oxygen partial pressures po2<10 kPa and po2>10 kPa, respectively.The optimum oxidation condition to obtain an oxide scale for well-adhered glass-coating to the substrate was 1248 Kand po2 =0.01 kPa for the oxidation time of 43 ks.