大掺量粉煤灰轻质墙体砌块的研制

大掺量粉煤灰轻质墙体砌块是以粉煤灰为主要原材料 ,普通硅酸盐水泥为胶凝材料 ,配以各种外加剂 ,经发泡剂发泡 ,在常温、常压条件下养护而成。具有重量轻、导热系数小、抗冻性高以及粉煤灰掺量大、成型方便、工艺简单、投资小、见效快等优点。     

螺旋焊管内涂层涂敷挥发份的清除

针对大口径螺旋焊管内涂层涂敷作业时，钢管内残留的涂料挥发份如何清除的问题，介绍了一种自行设计制造的内涂层涂敷挥发份吹除装置。     

甲基丙烯酸乙酯合成工艺研究

以大孔强酸性离子交换树脂为催化剂,甲基丙烯酸(MAA)与乙醇直接酯化合成甲基丙烯酸乙酯(EMA)。在MAA与乙醇摩尔比为1:3、反应温度89～93℃、空速0.3h~(-1)的条件下,MAA转化率不低于98％,EMA的选择性不低于99％。     

探讨缩聚催化剂对聚酯切片质量的影响

通过试验，分析比较了江西Sb2O3、南宁Sb2O3和大连Sb(Ac)3三种缩聚催化剂对聚酯切片质量的影响。试验结果表明，Sb(Ac)3是优良的缩聚催化剂。     

建筑墙体表面传热系数辨识研究

对实验房间南向墙体内表面中心区域的换热过程进行实验，发现当风速在0－5．5m/s之间时，表面传热系数在8－18W（m^2.K）之间波动，而风向对墙体表面传热系数影响不大；用辅助变量法分析墙体表面传热过程，并结合实验推导出墙体表面传热系数。模型的预测结果与实测结果吻合良好。     

Preparation of Laminin-apatite-polymer Composites Using Metastable Calcium Phosphate Solutions

A synthetic polymer with a laminin-apatite composite layer on its surface would be useful as a percutaneous device. The preparation of such a composite was attempted in the present study using poly（ ethylene terephthalate ） （PET） and polyethylene （PE） as the synthetic polymer. PET and PE plates and those pretreated with an oxygen plasma were alternately dipped in calcium and phosphate ion solutions, and then immersed in a metastable calcium phosphate solution supplemented with laminin （ LCP solution ）. The PET and PE plates pretreated with an oxygen plasma formed a uniform and continuous layer of a laminin-apatite composite on their surfaces. In contrast, the PET and PE plates that had not been pretreated with an oxygen plasma did not form a continuous layer of a laminin-apatite composite on their surfaces. The hydrophilic functional groups on the PET and PE surfaces introduced by the plasma treatment were responsible for the successful laminin-apatite coruposite coating.     

硼酸铝晶须增强环氧树脂和双马来酰亚胺树脂体系的研究

本文以硼酸铝晶须为增强剂，以4，5-环氧环己烷-1，2-二甲酸二缩水甘油酯(TDE-85)，甲基纳狄克酸酐(MNA)、N，N’-二胺基二苯甲烷型双马来酰亚胺(BMI)/O，O′-二烯丙基双酚A(BA)体系分别作为基体制备晶须增强复合材料。研究了晶须对树脂的尺寸、表面处理方法、含量对树脂体系力学性能和热性能的影响；通过扫描电子显微镜(SEM)分析了浇注体的弯曲、冲击断口，研究晶须的增强机理。     

Structure and properties of CE/CTBN/EP blends: II. Effect of EP on the mechanical properties and thermostability of the CE/CTBN system

Carboxyl‐terminated butadiene‐acrylonitrile rubber (CTBN) has often been used to improve the toughness of cyanate ester (CE) resin while sacrificing modulus and thermostability. In this paper, the addition of the appropriate amount of epoxy resin (EP) to the CE/CTBN system is shown to not only increase the modulus and thermostability of the blend, but also improve the toughness. The values of impact strength showed a maximum for the CE/CTBN/EP 100/5/5 blend. The temperature of 10 % weight loss (T₁₀) improves from 376 °C for CE/CTBN 100/5 to 407 °C for the CE/CTBN/EP 100/5/2.5 blend. It is proposed that addition of the appropriate amount of EP can decrease the mobility and increase the stability of CTBN via the reaction between the terminal carboxyl group of CTBN and the hydroxyl group of EP. But a very high EP concentration will decrease the crosslinking density of CE, consequently reducing the mechanical properties and thermostability of the blends. Copyright © 2004 Society of Chemical Industry     

Preparation and properties of novel polyurethane insulating coatings based on glycerin‐terminated urethane prepolymers and blocked isocyanate

Novel polyurethane insulating coatings were prepared from the reaction of glycerin‐terminated polyurethane prepolymers (GPUPs) and a blocked isocyanate curing agent (BIC). The GPUPs were prepared from the reaction of one equivalent of polycaprolactone polyol (CAPA 210) with an excess amount of 4,4′‐methylene bis(phenyl isocyanate) (MDI) and subsequent reaction of the NCO‐terminated polyurethane with glycerin. The BIC was prepared from the reaction of trimethylol propane (TMP), toluene diisocyanate (TDI) and N‐methylaniline (NMA). The polyols and curing agent were characterized by conventional methods while the curing condition was optimized via gel content measurements. The curing kinetics of the polyurethane coating were investigated and the kinetic parameters derived. The crosslink densities of the samples were determined via the equilibrium swelling method, using the Flory–Rehner equation. The relationships between the crosslink density and the electrical, physical, mechanical and dynamic mechanical properties of the coatings were also studied. Copyright © 2005 Society of Chemical Industry     

聚合物-金属界面相形貌的研究

环氧树脂在 Al 合金表面生成纤维状的界面相结构,其形成、发展和特征与树脂的体系、交联反应条件以及 Al 合金的表面状态有关。环氧树脂的基础相为颗粒状的超结构组织。聚合物界面相的力学破坏表现为纤维体的拉伸、变形和断裂,而基础相在纯剪切受力时出现在45°方向的裂纹,并发展导致连接层的破坏。