S-P混杂纤维对混凝土长期性能与耐久性影响

采用对比的试验方法,研究并讨论了钢纤维、聚丙烯纤维及其混杂对混凝土长期性能及耐久性的影响.研究结果表明,用不同尺度、不同性质的钢纤维与聚丙烯纤维按二元混杂以总体积率0.9%掺入高性能混凝土中,明显改善了水泥混凝土的长期性能,90d干缩值减少36.6%,200d徐变度降低45.4%,并可显著提高混凝土的耐久性能,相对渗透系数降低79.03%,氯离子渗透系数降低30.5%.     

Damage and deterioration mechanism and curing technique of concrete structure in main coal cleaning plants

Concrete structures in main coal cleaning plants have been rebuilt and reinforced in the coal mines of the Shanghai Da-tun Energy Sources Co. Ltd., the first colliery of the Pingdingshan Coal Co. Ltd. and the Sanhejian mine of the Xuzhou Mining Group Co. Ltd. In these projects, the operating environment and reliability of concrete structures in the main plants of the three companies were investigated and the safety of the structures inspected. Qualitative and quantitative analyses were made on the spe-cial natural, technological and mechanical environments around the structures. On the basis of these analyses, we discuss the long-term, combined actions of the harsh natural (corrosive gases, liquids and solids) and mechanical environments on concrete structures and further investigated the damage and deteriorating mechanisms and curing techniques of concrete structures in the main coal cleaning plants. Our study can provide a theoretical basis for ensuring the reliability of concrete structures in main coal cleaning plants.     

大体积混凝土温升与强度增长的试验研究

针对大体积混凝土结构构件实体强度与普通标准养护试块强度发展规律间的差别等问题,通过研究实际工程尺寸试件温度场的分布和实验室混凝土变温养护试验,以不同养护制度下的试块强度得出了大体积混凝土结构实体强度的发展规律,为工程施工提供了依据,成功地解决了工期与质量的矛盾,取得了较好的技术经济效果.     

某厂区重交通水泥混凝土路面病害成因分析及治理

针对目前某工厂主厂道由于受到重交通作用而造成水泥混凝土路面损坏严重的现状,笔者先从水泥混凝土路面主要病害的种类及其产生的原因着手加以分析,进而对在旧路面上半直接式加铺水泥混凝土和钢纤维水泥混凝施工技术进行了介绍和总结.     

Study on early warning index of spatial deformation for high concrete dam

Owing to the deficiency in early warning for high concrete dam,a formula was established to characterize the deformation behavior of high concrete dam as a whole.The early warning index of spatial deformation was calculated by low probability principle on the basis of the deformation entropy formula proposed.The steps were as follows.Firstly,the probability method was utilized to define the degree of order and degree of chaos for each survey point.Secondly,the weight distribution among the survey points was...     

声参数的高性能混凝土强度推定模型

为研究高性能混凝土的声波传播特性及实现其强度的快速、准确、无损检测,基于超声波检测方法,应用嫩江、多宝山附近的沙石料,对高性能混凝土对声波的扩散性及其抗压性能与声参量之间的模型关系进行了研究.建立了高性能混凝土抗压强度与声速之间的多种数学模型.通过实测检测数据进行验证,满足精度要求.高性能混凝土的非均质性降低,其抗压强度与声速相关性较好,用超声的方法完全可以实现强度的快速推定.同时,也为将来高性能混凝土地区强度推定曲线的建立奠定了研究基础.     

A macro-meso constitutive law for concrete having imperfect interface and nonlinear matrix

The overall behavior of concrete depends on its meso structures such as aggregate shape, interface status, and mortar matrix property. The two key meso structure characters of concrete, bond status of interface and nonlinear property of matrix, are considered in focus. The variational structure principle is adopted to establish the macro-meso constitutive law of concrete. Specially, a linear reference composite material is selected to make its effective behavior approach the nonlinear overall behavior of concrete. And the overall property of linear reference composite can be estimated by classical estimation method such as self-consistent estimates method and Mori-Tanaka method. This variational structure method involves an optimum problem ultimately. Finally, the macro-meso constitutive law of concrete is established by optimizing the shear modulus of matrix of the linear reference composite. By analyzing the constitutive relation of concrete established, we find that the brittleness of concrete stems from the imperfect interface and the shear dilation property of concrete comes from the micro holes contained in concrete. Supported by the National Natural Science Foundation of China (Grant Nos. 50679022, 90510017, 50539090) and National Basic Research Program of China (Grant No. 2007CB714104)     

Experimental study on temperature stress calculation and temperature control optimization of concrete based on early age parameters

Temperature control curve is the key to achieving temperature control and crack prevention of high concrete dam during construction,and its rationality depends on the accurate measurement of temperature stress.With the simulation testing machine for the temperature stress,in the present study,we carried out the deformation process tests of concrete under three temperature curves：convex,straight and concave.Besides,we not only measured the early-age elastic modulus,creep parameters and stress process,but also proposed the preferred type.The results show that at early age,higher temperature always leads to greater elastic modulus and smaller creep.However,the traditional indoor experiments have underestimated the elastic modulus and creep development at early age,which makes the calculated value of temperature stress too small,thus increasing the cracking risk.In this study,the stress values of the three curves calculated based on the strain and early-age parameters are in good agreement with the temperature stress measured by the temperature stress testing machine,which verifies the method accuracy.When the temperature changes along the concave curve,the law of stress development is in consistent with that of strength.Under this condition,the stress fluctuation is small and the crack prevention safety of the concave type is higher,so the concave type is better.The test results provide a reliable basis and support for temperature control curve design and optimization of concrete dams.     

大内跨小边跨框架结构预应力筋优化布置方法

预应力筋的优化布置是大内跨小边跨的多跨预应力混凝土框架结构合理设计计算的关键.为满足控制截面承载力最大的需要,以往常将大跨所需预应力筋布置为连续曲线,并按水平直线延伸通过其相邻的两小跨,按这种布置方式仅使大跨内产生竖向向上的预应力等效荷载,可较好平衡大跨的竖向外荷载;而若将大跨及相邻的两小跨统一考虑,预应力筋按连续曲线布置,张拉产生的预应力等效荷载不但可有效平衡大跨的竖向外荷载而且也可平衡小跨的竖向外荷载,可以使荷载平衡得到优化实现.以一典型工程为例,分析了在相同条件下两种预应力筋布置过程中张拉引起的综合弯矩、主弯矩和次弯矩的分布和量值上差异,比较了两类布筋形式对正截面承载力计算结果的影响,验证了对大内跨小边跨框架结构统一考虑后整体上按三段连续正反抛物线预应力筋布置的合理性.     

Evaluation research on applicability of rapid iodide migration test

The applicability of the rapid iodide migration test was systematically studied. Comparative experimental tests of different test conditions, including several external voltages, test durations, concrete ages and mixing proportions, were carried out to make clear the transport behaviors of iodide under parallel electric fields. Numerical simulations were also done using the finite element method to found the correlation between chloride and iodide transport behaviors. The test and numerical results show that the chloride transport behaviors of RIM and RCM tests have a good correlation under the several conditions used in the present paper. Moreover, the influence of external conditions （external voltages, test durations） on the test results is small. Thus, it can be concluded that the RIM method is available to determine the chloride penetration resistance of the chloride-eroded structural concrete.