Co^3＋—modified Surface of LiMn2O4 Spinel for its Improvementof Electrochemical Properties

Cobalt was used to modify the surface of spinel LiMn2O4 by a solution technique to produce Co^3 -modified surface material (COMSM). Cobalt was only doped into the surface of LiMn2O4 spinel. XPS(X-ray photoelectron spectroscopy) analysis confirms the valence state of Co^3 . COMSM has stable spinel structure and can prevent active materials from the corrosion of electrolyte. The ICP(inductively coupled plasma) determination of the spinel dissolution in electrolyte showed the content of Mn dissolved from COMSM was smaller than that from the pure spinel. AC impedance patterns show that the charge-transfer resistance (Rct) for COMSM is smaller than that for pure spinel. The particles of COMSM are bigger in size than those of pure spinel according to the micrographs of SEM(scanning electron microscopy). The determinations of the electrochemical characterization show that COMSM has both good cycling performance and high initial capacity of 124.1 mA/h at an average capacity loss of 0.19 mAh/g per cycle.     

Ce3+离子对掺Er3+碲酸盐玻璃光谱性质的影响

研究了Ce3 + 对掺Er碲酸盐玻璃荧光光谱性质的影响 ,比较了不同的Ce3 + 掺杂浓度下Er3 + 离子荧光发光强度的变化 ,分析了Ce3 + 离子对Er3 + 离子作用的原理 ,应用经典方程计算了Er3 + 离子 4I1 1 / 2 能级的荧光寿命及其变化     

Optical data storage by novel photoelectrochromic polymer

A novel elastic polymer containing 4,4′-bipyridinium salts with tetrakis[3,5-bis(trifluoromethyl)phenyl]borate as part of the main chain was synthesized. The cast film showed persistent and reversible colour changes due to photoinduced electron transfer upon excitation of an ion-pair charge-transfer band (_ex >365 nm) in vacuo. The lifetime of the coloured state markedly depended on temperature. The optically written data were stored without decay below 0°C and were erased thermally at elevated temperatures. The colour changes were reversibly repeatable for many times.     

Ti 离子注入 LiNbO_3表面光学性能

本文研究了 x,y,z 三种切向的 LiNbO_3单晶片注入350keV 高能 Ti 离子(注入剂量为1.5×10~(17)/cm~2)后的表面光学性能。利用光谱仪及 AUEL 椭偏仪对三种切向 LiNbO_3试样在不同工艺处理后的光透射率及折射率进行了测试。注入损伤造成的光损耗可通过热处理消除,使晶格结构恢复至与完整晶格排列相近;注入层的折射率可增加11—13％左右。     

铵离子交换处理负硬水供锅炉应用技术

本文论述了负硬水只用氯化铵再生时离子交换器的运行过程及离子交换软化除碱的方法,并阐述了控制出水中残留碱的简便方法。经研究证明,此方法可达到除碱度、除硬度、除盐、延长锅炉使用寿命、减少腐蚀、减少排污量、节约燃煤等效果。经济效益十分显著。     

离子注入对铁及其低合金、铝及其合金耐腐蚀性能的影响

离子注入对金属腐蚀行为的研究已达30年．研究结果表明离子注入对改变金属表面成分和表面性能是极为有效的技术．本文概述了离子注入对铁及其低合金、铝及其合金的腐蚀电化学行为的影响．涉及的注入离子达十余种。     

氮离子注入尼龙1010的摩擦学特性

用高能离子注入机对尼龙 10 10进行 N+注入改性 ,注入能量为 4 5 0 ke V,剂量分别为 5× 10 14 /cm2 、2 .5× 10 15/cm2 及 1.2 5× 10 16/cm2 。以 Zr O2 及 Si3N4 球为上球样 ,分别与注入尼龙 10 10下盘样组成摩擦副 ,在销盘摩擦试验机上评价它们在干摩擦条件下的摩擦磨损行为。结果表明 ,几种剂量的 N+注入均增强了尼龙 10 10的耐磨性。未注入样品的磨损主要表现为粘着、塑性变形、犁沟和疲劳脱层 ,注入样品的磨损主要为轻微的磨粒磨损。     

等离子体浸没式离子注入-离子束增强沉积TiN膜研究

本文采用一种新型的等离子体浸没式离子注入 离子束增强沉积的技术(PIII IBAD),在Cr12MoV钢基体上制备出了TiN膜,对沉积膜的组织进行了光电子能谱分析,并对沉积膜进行了硬度检测、摩擦试验及磨痕形貌分析。试验结果表明,沉积膜中的组织为TiN、TiO2和Ti2O3,TiN膜具有高达Hv3200的高硬度和极其优良的摩擦性能。     

大庆蜡油在酸性催化剂上反应机理的研究

以大庆蜡油为原料，采用两种不同类型的催化剂，在流化床反应器实验装鬣上进行催化裂化反应。结果表明，大庆蜡油在酸性催化剂上反应所产生的干气组成与高烯烃催化裂化汽油相同，干气的产生主要是单分子裂化反应所造成的。从干气产率、组成以及液化气组成可以看出，大庆蜡油在不同类型的催化剂上明显地表现出裂化反应类型的差异。