Strain hardening of porous iron under uniaxial compression

A series of experiments was carried out with powder iron of 1–40% porosity including deformation by compression to various degree of deformation, and strain hardening curves were calculated. It was established that change in the loading sign relative to uniaxial tension had practically no effect on the strain hardening laws of the solid phase, although it basically changed the porosity contribution to the loading curve formation. Translated from Poroshkovaya Metallurgiya, Nos. 1–2(411), pp. 106–112. January–February, 2000.     

中温SOFC密封玻璃热稳定性研究

研究了一种热稳定性好的中温固体氧化物燃料电池密封玻璃. 研究表明, 此密封玻璃的热膨胀系数(室温～631℃)为9.8×10^-6/K, 与8YSZ电解质的热膨胀系数10.0×10^-6/K(室温～631℃)接近, 并且在700℃热处理300h后, 该密封玻璃的热膨胀系数几乎没有变化. 粘度实验表明, 玻璃在700℃下具有足够的刚性, 适合于运行温度在700℃左右SOFC的密封. 化学相容性的研究显示, 在700℃下与8YSZ反应300h后没有发现显著的界面反应.     

添加物对Fe_2O_3超微粒的稳定作用

粒子的尺寸直接关系着气敏元件性能的好坏．为了防止Ｆｅ２Ｏ３超微粒在气敏元件烧结过程中长大，我们在纯Ｆｅ２Ｏ３中掺入５ｍｏｌ％碱土金属离子，利用ＸＲＤ和ＴＥＭ系统研究了掺杂物对Ｆｅ２Ｏ３超微粒子的稳定作用，并对由掺杂引起的Ｆｅ２Ｏ３电学性质的变化作了初步探讨．     

等离子喷焊铜基自熔性合金的研制

为了克服铜铁异种材料喷焊过程中易产生焊缝裂纹和基体裂纹的倾向,研制开发了一种Cu-Ni-Sn自熔性合金粉末材料.通过对Cu-Ni-Sn粉末材料的化学成分的设计,喷焊层的组织显微结构及抗腐蚀性能的综合分析,认为该材料等离子喷焊工艺性能良好,焊层耐腐蚀效果十分明显.在生产实际中应用等离子喷焊制备Cu-Ni-Sn焊层,能明显提高粉末材料的熔敷率和性能,并且改善劳动工作环境.该合金性能优于传统材料,值得推广.     

用熔盐电解法制备超细钨粉

在NaCl-KCl-Na2WO4-WO3熔体中,用熔盐电解法电解氧化钨制取细钨粉和超细钨粉。在电解温度为720℃,阴极电流密度为250mA/cm^2的条件下,得到平均等积圆直径为1．2μm、长宽比为1．6的超细钨粉。在低阴极电流密度时,阴极的电解反应为W^6 放电,在高阴极电流密度时,阴极的电解反应为Na^ 放电。研究了温度、阴极电流密度和Na2WO4的含量对电流效率的影响。     

钨铜化合物氢还原制备钨铜复合粉研究

通过对钨铜化合物氢还原过程进行热力学分析,找到了制备均匀细颗粒钨铜复合粉的热力学途径--彻底快速除去还原系统中的水分.设计了封闭还原系统,用此系统进行氢气热还原,不仅使氢气得到充分利用,而且容易判断反应终点.通过系统内的特殊装置除水,降低了还原温度,在600℃下还原得到了混合均匀的钨铜复合粉.系统能彻底快速除去反应生成的水分,使反应物的湿度大大降低,确保得到细颗粒的钨铜复合粉,其平均粒径小于80nm.     

The Effect of Formulation on Radioiodide Thyroid Uptake in the Hyperthyroid Cat

This investigation was designed to compare in vitro dissolution profiles from sodium iodide capsules with radioiodide thyroid uptake in hyperthyroid cats using sodium iodide capsules prepared with a formulation exhibiting a complete release of radioiodide (I-123) in vitro and a formulation with an incomplete release of radioiodide. In vitro dissolution profiles for I-123 sodium iodide capsules with two different formulations were determined using the USP XXIII dissolution test. The two formulations studied in vitro were sodium phosphate dibasic powder with 1% magnesium stearate and calcium phosphate dibasic powder with 3% magnesium stearate. By 20 min after initiation of the dissolution test, over 95% of the I-123 was released from capsules of sodium phosphate dibasic powder. The capsules of calcium phosphate dibasic powder reached 75% at 65 min, with no further release occurring thereafter. There was a statistically significant difference in the dissolution profiles of the two formulations. The thyroid uptake of I-123 from capsules exhibiting complete release and incomplete release of radioiodide was determined in hyperthyroid cats. At 4 hr, the mean percentage thyroid uptake value for sodium phosphate dibasic powder with 1% magnesium stearate (complete release formulation) was 12.0% compared to 9.4% for calcium phosphate dibasic powder with 3% magnesium stearate (incomplete release formulation); at 24 hr, the values were 34.4% compared to 23.7%. The data suggest that the incomplete dissolution profile observed in vitro may correlate with a reduction in the bioavailability of the radioiodide in vivo. However, using the Wilcoxon signed rank test, statistically significant differences did not occur between the complete release formulation and incomplete release formulation at either 4 hr or 24 hr (p >. 05). The results of the in vivo study with five hyperthyroid cats were not conclusive due to the variability in response between individual cats.     

次级电子激发过程的Monte Carlo模拟计算

在总结前人工作的基础上，利用MonteCarlo方法建立了次级电子激发过程的数学模型。然后利用此模型计算了一类重要的次级发射体──高铅硅酸盐玻璃的次级发射性能。本文首次把次级电子发射体的材料构成与其次级电子发射性能通过MonteCarlo计算联系了起来，为新型次级电子发射材料的设计提供了一种计算方法。     

应用水化硅酸盐纳米粉体制备块体材料

以磨细生石灰和硅质原料的混合物为前驱物,采用动态水热合成方法制备了水化硅酸盐纳米粉体.借助SEM、TEM及氮吸附等测试方法,分析了制得的水化硅酸盐粉体的形貌、粒径和比表面积.将制得的水化硅酸盐纳米粉体压制成块状固体.采用正交设计方法研究了成型压力、水泥掺量、纤维掺量、聚合物掺量等因素对块体材料力学性能的影响.结果表明:由该粉体压制成的块体材料立即具有强度和耐水性,且表观密度低;成型压力是影响其力学性能最显著的因素.