承德钒钛磁铁矿粉基础特性及烧结试验研究

通过研究承钢三种含铁精粉(黑山精粉、承德普通精粉、小营精粉)的矿相结构,差热分析及烧结特性,结果表明:三种铁矿粉均为典型的磁铁矿,铁品位、SiO2含量较低,TiO2、Al2O3、FeO含量较高;根据差热分析,三种矿粉均主要以磁铁矿形式存在,没有赤铁矿包裹磁铁矿的情况,矿粉增重的初始温度都比较低,高温区间TG曲线上升的斜率相同,均符合磁铁矿的氧化动力学条件;三种铁精粉单烧的垂直烧结速度慢,废气温度较低,烧损率较低,转鼓指数均较低,黑山精粉的转鼓指数最低,仅有55.33%;经混料烧结后,烧结矿转鼓指数得到明显提升,最高达到64.40%。研究结果为中钛型钒钛磁铁矿烧结提供了理论基础。     

Phase diagram of the CsBr-CaBr2 system

The phase diagram of the CsBr-CaBr2 system was re-determined by using differential thermal analysis and high ternperature and room ternperature X-ray diffraction analysis. It is concluded that there are three intermediate compounds in this system： a.congruently melting compound, CsCaBr3, with a melting point of 823℃ and two incongruently melting compounds, Cs2CaBr4 and Cs3Ca2Br7, whose peritectic points being 597℃ and 635℃, respectively. X-ray diffraction analysis indicated that compound CsCaBr3 is of slightly distorted perovskite structure.     

几种密封材料的差热分析鉴定

通过几种密封材料的差热分析,说明差热分析在材料剖析中的应用。     

锂质陶瓷釉析晶动力学DTA研究

本文通过差热分析(DTA)对锂辉石质陶瓷釉的析晶动力学问题进行了研究.求出了它的析晶活化能E=374.13KJ/mol;并借用一种新的动力学判据K_y(T),给出了它的析晶能力大小;同时发现,在锂辉石质陶瓷釉中引入成核剂TiO_2后,只会降低析晶程度;工艺条件改变会使它的析晶活化能减小,析晶能力下降.     

基于实例的煤矸石混凝土局部爆裂原因分析

针对某房屋楼板混凝土底部产生局部爆裂,且爆裂点出现不明黑色物质的现象,该文通过对现场情况的调查和取样测试分析,结合化学成分分析、X射线衍射分析、差热分析等相关数据,分析了产生爆裂的原因。研究表明,温度、湿度和接触介质变化导致煤矸石、蒙脱石等膨胀、崩解是楼板混凝土底部发生局部爆裂的原因,骨料中混杂煤矸石对混凝土外观、耐久性的潜在危害应引起高度重视。     

新型差式热量测定仪的研制探讨

一种新型水泥生料热测定仪,由供热炉膛、支持器、微机主机、温度变送器等部件构成,运用差热分析(DTA)原理,引入微机对供热炉进行程序升温控制,并对差热信号进行分析处理,进而测定水泥生料热。结构简单,操作方便,测定准确、快捷。     

燃烧合成法制备CaB6的研究

以CaO、B2O3、Mg粉为原料燃烧合成制备了CaB6粉末.考察了不同反应体系的差热曲线,采用XRD、SEM以及粒度分析技术对燃烧产物、浸出产物进行了表征.结果表明:Mg-B2O3-CaO反应体系872℃附近放热峰的表观活化能E=15.71kJ·mol-1,反应级数n=1.1,反应的表观活化能很小,说明合成CaB6的反应容易发生.燃烧产物由MgO、CaB6以及少量的Mg3B2O6和Ca3B2O6等组成,在空气中进行燃烧合成反应并不生成氮化物;燃烧产物经硫酸浸出处理后CaB6纯度达92.5%;随着制样压力的增大,CaB6粒度逐渐变小.     

镁热还原法制备钛粉的绝热温度计算和差热分析

计算了镁热还原自蔓延高温合成制备钛粉的绝热温度,对2Mg-TiO2进行了差热分析,并根据差热曲线计算了反应的活化能和反应级数.结果表明:当x＜2.4时,x Mg-TiO2自蔓延高温合成反应的绝热温度Tad≥1800K,反应可以自发进行;反应2Mg TiO2=Ti 2MgO在767K附近开始发生,反应为固-固反应;反应的活化能E=248.9kJ·mol-1,反应级数n=0.55.