Water electrolysis is an efficient approach for high-purity hydrogen production. However, the anodic sluggish oxygen evolution reaction (OER) always needs high overpotential and thus brings about superfluous electricity cost of water electrolysis. Therefore, exploiting highly efficient OER electrocatalysts with small overpotential especially at high current density will undoubtedly boost the development of industrial water electrolysis. Herein, we used a simple hydrothermal method to prepare a novel FeOOH–CoS nanocomposite on nickel foam (NF). The as-prepared FeOOH–CoS/NF catalyst displays an excellent OER performance with extremely low overpotentials of 306 and 329 mV at 500 and 1000 mA cm⁻² in 1.0 M KOH, respectively. In addition, the FeOOH–CoS/NF catalyst can maintain excellent catalytic stability for more than 50 h, and the OER catalytic activity shows almost no attenuation no matter after 1000 repeated CV cycles or 50 h of stability test. The high catalytic activity and stability have exceeded most non-noble metal electrocatalysts reported in literature, which makes the FeOOH–CoS/NF composite catalyst have promising applications in the industrial water electrolysis.     

Al-10Mg型固溶合金自然时效稳定性研究

测定了ZL30 5合金自然时效 33年的力学性能变化 ,观察了晶界的析出相 ,研究了组织和性能的关系 ,从而确定了ZL30 5合金具有长期自然时效稳定性。     

硫化氢吸收液的电化学分解条件研究

理想的脱硫工艺应满足体积小、费用低、净化度高、无二次污染等要求。在碱性溶液吸收微量硫化氢时同步进行电解，可有效减小设备体积，并将硫化氢转变为氢气和硫磺，不产生恶性气味。为此，实验研究了温度、浓度、电流密度、pH值等因素对电解阳极过程的影响，确定了适宜的电解条件，并在该条件下进行了吸收实验。结果表明，在最佳电解条件下，硫化钠溶液能充分吸收天然气中经变压吸附提浓的硫化氢（800 mg/m³），吸收率大于99.9％。     

Electro-organic synthesis without supporting electrolyte: Possibilities of solid polymer electrolyte technology

The application of ion exchange membranes as solid polymer electrolytes (SPE) in fuel cells is state-of-the-art. This technology needs no supporting electrolyte; consequently it can be applied for electro-organic syntheses in order to save process steps. In this case the process is not predetermined to a maximized energy efficiency so that the selection of the cell design, of the electrode materials and of the operating conditions can be focused on a high selectivity of the electrode reactions. The electro-osmotic stream, which is caused by the solvation shells of the ions during their migration through the membrane, and hence is a typical property of SPE technology, has a significant effect on the electrode reactions. It generates enhanced mass transfer at the electrodes, which is beneficial for reaction selectivity. It can be influenced by the choice of, and possibly by the preparation of, the membrane. An additional remarkable advantage of SPE technology is the exceptional long durability of oxide coated electrodes. By combination of several process engineering methods stable operation of SPE cells has been realized, even for examples of non-aqueous reaction systems. Experiments up to 6000 h duration and in cells of up to 250 cm² membrane area show the potential for industrial application.     

掺杂聚苯胺导电膜的制备及对核设施表面铀的去污

制备了掺杂导电聚苯胺可剥离膜，首次采用涂膜、电解联用去污方法，进行涂膜电解去除渗透到核设施金属材料内部形成氧化物的铀。在膜中，聚苯胺、盐酸、EDTA-2Na含量各为4％、0．5％～1%、1％；电解电压2．3V、电解时间25min～30min时，其去污率可达99％，优于其它的方法。     

Mechanical behavior of 30–50 nm thick aluminum films under uniaxial tension

We present uniaxial tensile test results for 30–50 nm thick freestanding aluminum films. Young’s modulus and ductility were found to decrease monotonically with grain size. Reverse Hall–Petch behavior was observed with no appreciable room temperature creep. Non-linear elasticity with small irreversible deformation was observed for 50 nm thick specimens.     

氯碱电解槽槽电压构成现状与进展

依据槽电压构成的诸多因素,介绍了目前槽电压构成的现状和进展。     

功率电子器件用AlN陶瓷基板的研制

阐述了AlN陶瓷的烧结原理 ,分析了烧结工艺参数对大面积AlN基板性能的影响 ,成功研制出了高热导率(190W /m·K)、大面积 (14 0mm× 90mm)、翘曲度为 2 0 μm/5 0mm的AlN陶瓷基板。     

Laboratory study of property-modified prebaked carbon anode and application in large aluminum electrolysis cells

A kind of complex additive mainly containing Al, Mg, F, and O was prepared. The synthetical performances of the property-modified prebaked anodes containing additives were tested in laboratory. On the basis of ideal testing results obtained, a large number of industrial prebaked property-modified anodes are prepared in a large-scale aluminum company. Further more, they are all used in 160 kA prebaked anode aluminum electrolysis cells. The statistic result show that, compared with common anodes, the property-modified ones enhance current by 11.6 kg per ton aluminum averagely.     

硼酸铝晶须增强环氧树脂和双马来酰亚胺树脂体系的研究

本文以硼酸铝晶须为增强剂，以4，5-环氧环己烷-1，2-二甲酸二缩水甘油酯(TDE-85)，甲基纳狄克酸酐(MNA)、N，N’-二胺基二苯甲烷型双马来酰亚胺(BMI)/O，O′-二烯丙基双酚A(BA)体系分别作为基体制备晶须增强复合材料。研究了晶须对树脂的尺寸、表面处理方法、含量对树脂体系力学性能和热性能的影响；通过扫描电子显微镜(SEM)分析了浇注体的弯曲、冲击断口，研究晶须的增强机理。