Luminescence Characterization of Mg Doped Y2O2S:Ti Long Afterglow Phosphor

Y1.94-xMgxO2S:0.06Ti (0≤x≤0.10) phosphors with long afterglow were synthesized by solid state reaction route. The photoluminescence spectra, decay curves, thermoluminescent spectra and chromaticity coordinate curves were investigated. The results show that the luminescence intensity of Y1.94-xMgxO2S:0.06Ti (0≤x≤0.10) phosphors decrease gradually with increasing Mg2 ion content, and the shape of luminescence spectra and chromaticity coordinate change as well. Furthermore, two thermoluminescent peaks in single Ti-doped Y2O2S sample are found at 91.8 and 221.5 ℃, respectively. Nevertheless, significant different spectra were found for the Mg, Ti co-doped Y2O2S samples that three thermoluminescence peaks appear at 52.3, 141.7 and 226.8 ℃, respectively. These results indicate that the co-doped Mg ion changes the inherent trap depth of single Ti-doped Y2O2S:Ti phosphor, and induces simultaneously a new trap level in the Y1.94-xMgxO2S:0.06Ti phosphor. Based on the analysis of thermoluminescent spectra, photoluminescent spectra, decay curve and crystal structure defect, it was proposed that the varied structure defect and introduced new trap level by the doped Mg2 ions should be responsible for reducing luminescence intensity and varying color in the Y1.94-xMgxO2S:0.06Ti phosphor.     

高温稀土永磁Sm2(Co,Cu,Fe,Zr)17 的制备和性能

制备了高温稀土永磁材料Sm(Coba1Fe0．26Cu0．05Zr0．026)7．0，研究了磁性能与工艺条件的关系．结果表明：提高烧结温度可使材料的Br和(BH)max增大，但是使Hci降低；适当提高真空预烧温度，可使材料在较低烧结温度下致密化，具有较高的Hci和(BH)max和温度稳定性．真空预烧温度过高使性能的急剧降低，其主要原因是Sm的析出．在最佳工艺条件下材料的磁性能参数分别为：Br1．08T3Hci2286kA／m，Hcb932kA／m，(BH)max220．8kJ／m^3；β20-200℃为-0．19％／℃．     

稀土溶液标准物质的研制

选择7种稀土元素:La、Ce、Sm、Eu、Yb、Lu、Y为研究对象,采用高纯稀土氧化物(≥99 99%)为原料,经ICP MS及ICP AES对纯度进行分析后,分别制备成浓度为1000μg mL的稀土溶液标准物质。采用准确、可靠并能溯源的EDTA络合滴定法进行量值核对、均匀性及稳定性检验。对标准物质的不确定度进行了全面的评定。研制的稀土溶液一级标准物质,总不确定度优于0 6%,稳定性达两年以上。     

Nd3+ Doped Silicate Glass Photonic Crystal Fiber with Random Hole Distributions

The fabrication of one kind of large core area Nd3 doped silicate glass photonic crystal fiber, and demonstration of the fiber's waveguidence properties were reported. This fiber owns a random air hole distribution in the cladding. The measured minimum loss of this kind of fiber is 10 dB·m-1 at 660 nm. These fibers can sustain only a single mode at least over wavelength ranging from 660 nm to 980 nm.     

Monoalkyl Esters of Isoalkylphosphonic Acid as Extractants in Rare Earth Separation

Four monoalkyl esters of isoalkylphosphonic acids have been studied for the chromatographic separation ofrare earths (RE).The relationship between distribution ratios and acid concentration of the eluants forsamarium and ytterbium has been explored.The characteristics of these extractants loaded onto macroreticularpoly (methyl methacrylate) resin beads for the separation of lanthanum,cerium,praseodymium and neodymiumhave been compared.Among the extractants studied,mono(1-methylheptyl) ester of isooctylphosphonic acidwas found to be the best for RE separation.The acidity for separation is lower than any known P-containingextractants for the same purpose.For instance,with 1.73 mol·L~(-1) nitric acid as eluent,thulium,ytterbium andlutetium can be separated quantitatively.The extractant-loaded resins possess high column efficiency with goodkinetic characteristics.The extraction mechanism was also explored.     

Mesomorphism of Lanthanide(Ⅲ) 4-Hexyloxybenzoates

The 4-alkoxybenzoic acids are well-known liquid crystals showing several mesophases(nematic,smectic C phase or both)depending on the alkoxy chain length and whereby the rigid core of the mesogen is formed by intermolecular hydrogen bonds.In this paper it is shown that the thermal behaviour of lanthanide salts of 4-hexyloxybenzoic acids depends on the lanthanide ion(Ln=La,Pr,Nd,Sm,Eu).The lanthanum(Ⅲ)and praseodymium(Ⅲ)4-hexyloxybenzoates exhibit a smectic A mesophase.No mesophase is found for the corresponding compounds of heavier lanthanides.The thermal properties of the lanthanide(Ⅲ)4-hexyloxybenzoates were investigated by differential scanning calorimetry(DSC),polarising thermo-optical microscopy and synchrotron X-ray radiation.     

高等级公路边坡防护设计

分析了影响边坡稳定的因素 ,对不同环境条件下采用的不同路基边坡防护类型进行了介绍 ,重点阐述了经济有效的三维固土网垫结合植被护坡的类型 ,指出边坡稳定是保障公路畅通的重要基础     

铒氨基酸固态配合物的光声光谱研究

合成了Er(Gly)3Cl3·3H2O、Er(Ala)3Cl3·3H2O和Er(Gly)3Phen·3H2O二元及三元固态配合物微晶粉末,在300nm～800nm范围内测定并解释了其光声光谱。通过对光声相对强度计算得到铒氨基酸固态配合物的光声支量,讨论了氨基酸配体对中心稀土离子铒f-f跃迁的微扰作用。结合Er(Ala)3Cl3·3H2O配合物的光声光谱和吸收光谱研究了其荧光性质及弛豫模型。     

CO毒化AB5型合金分形特征研究

研究了三种贮氢合金 L a Ni5、L a Ni4 .7Al0 .3、Ml Ni4 .5Al0 .5被 10 0× 10 - 6 CO毒化后的分形特征 ,求出这三种合金在含 10 0× 10 - 6 CO的氢中循环 ,分维分别为 0 .2 5 4 7、0 .170 9、0 .0 72 5。可以较好的解释合金被毒化的宏观现象。     

Limited reinforced space in segmental retaining walls

Current design of geosynthetic reinforced segmental retaining walls considers an a priori limitless length for reinforcement installation. Such length is typically 0.5–0.7 times the height of the wall. However, often there are constraints on such space; e.g., bedrock formation located at a small distance behind the facing. The objective of this note is to introduce a procedure for assessing the required long-term strength of the reinforcement while considering its limited length. Predictions by a conventional slope stability analysis were first checked against a continuum-mechanics based numerical analysis. Upon obtaining good agreement, a design chart was developed. The chart enables the determination of the reduction in the lateral earth pressure coefficient due to the constrained space. The revised earth pressure coefficient can be used with current analytical methods to account for the limited space. The results appear to be valid for conventional walls retaining a limited volume of soil. Comparison with limited experimental results for unreinforced backfill shows reasonably good agreement.