Synthesis of ZSM‐5 Films and Monoliths with Bimodal Micro/Mesoscopic Structures

A route to synthesize ZSM‐5 crystals with a bimodal micro/mesoscopic pore system has been developed in this study; the successful incorporation of the mesopores within the ZSM‐5 structure was performed using tetrapropylammonium hydroxide (TPAOH)‐impregnated mesoporous materials containing carbon nanotubes in the pores, which were encapsulated in the ZSM‐5 crystals during a solid rearrangement process within the framework. Such mesoporous ZSM‐5 zeolites can be readily obtained as powders, thin films, or monoliths.     

Fracture and deformation properties of Ni-Fe superalloy in cryogenic high magnetic field environments

The present paper includes experimental and analytical data on the fracture properties of a nickel-iron superalloy, a ferromagnetic austenite, at 4 K in magnetic fields of 0 and 6 T. The tensile, notch tensile and small punch tests are employed. A finite element analysis is also performed to convert the experimentally measured load-displacement data into useful engineering information. To interpret the results we review the available theory of the influence of magnetic field on the stress intensity factor for a crack in ferromagnetic materials.     

微桥法镍膜的弹性模量和残余应力测量

利用MEMS技术制作了不同尺寸的镍(Ni)膜微桥结构样品。采用纳米压痕仪XP系统测量了微桥载荷与位移的关系,并结合微桥力学理论模型得到了两种不同尺寸的Ni膜的弹性模量和残余应力。结果表明,两种不同尺寸的Ni膜的弹性模量结果一致,为190 GPa左右,但是残余应力变化较大。与采用纳米压痕仪直接测得的带有硅(Si)基底的Ni膜弹性模量186.8 7.5 GPa相比较,两者符合较好。     

Effect of oxygenation on electrocatalysis of La0.6Ca0.4CoO3−x in bifunctional air electrode

A vacuum-annealed La_0.6Ca_0.4CoO_3−x was consecutively oxygenated in air at temperatures decreasing from 800 to 100 °C, and its electrocatalytic activities for oxygen reduction and evolution were then measured as a function of the oxygenation temperature. The valence of Co cation, changing between +2 and +3, was found susceptible to annealing either in vacuum or air. The catalytic activities initially decrease monotonically as the oxygenation temperature was decreased from 800 to 300 °C, as a result of increasing oxygen content, and then rise abruptly with the oxygen reduction activity reaching a maximum at 200 °C and the oxidation activity at 150 °C. X-ray photoelectron spectroscopy analysis indicated that the enhancements by the low-temperature oxygenation involved increased OH coverage and less charged cations at surface. The results clearly reveal the importance of the post-calcination annealing process for optimizing the performance of La_0.6Ca_0.4CoO_3−x in air electrode applications.     

滑坡相似材料试验结果优化分析研究

在运用模糊综合评判确定的滑坡相似材料试验配合比隶属度基础上，利用方差分析确定各因素的数学优化区间，结合变量有上下界的改进单纯形法，获得技术，经济上的最佳配合比，克服了统计优化理论不能在连续区间寻优的缺点，这对从事滑坡相似材料试验研究具有一定的实际意义。     

Effect of Stoichiometry on Properties of Rare-Earth-Based Hydrogen Storage Alloy for Nickel-Metal Hydride Secondary Battery

Effect of stoichiometry on microstructures, electrochemical properties and PCT characteristics of the alloys MI(Ni0.71Co0.15-Al0.06Mn0.08)x (MI=Lanthanum-rich Michmetal, x=4.6~5.2) have been investigated. The lattice constants a, c, and cellvolumes of non-stoichiometric alloys are bigger than those of the stoichiometric alloy. With the increasing stoichiometry x,the value of a decreases, and the value of c and cell volume increases except for those of the stoichiometric alloy; the plateaupressure of PCT curve, discharge capacity and cycling stability all increase. The alloy with x=5.2 shows the highest dischargecapacity and the best cycling stability among the studied alloys.     

机械合金化Fe-Ni粉末的相结构

使用XRD和Moessbauer等方法，研究了在Ar气氛下机械合金化Fe—Ni粉末相结构的变化．结果表明，在机械合金化Fe64-Ni36粉末过程中，fcc相的数量随着球磨时间的增加先增加然后减少，与加乙醇球磨Fe64-Ni36的情形相同．当Ni的含量(原子分数)大于50％时，有fcc相、顺磁相和FeNi3形成，当Ni的含量低于50％时，bcc相的数量随着Ni含量减少而增加．Moessbauer谱的结果表明，因球磨时间或Fe、Ni比例的不同，Fe—Ni球磨粉末固溶体具有不同结构的原子配比。     

CNTs/Polyester复合材料的微波吸收特性研究

研究了添加不同质量分数CNTs的聚酯基复合材料的电磁波吸收性能,初步分析了CNTs的螺旋结构和手征性质导致8～40GHz波段良好的吸收。其中厚度为1.40mm±0.05mm的CNTs/Polyester复合材料在25GHz有较强的吸收峰。