精对苯二甲酸反应器桨叶断裂分析与修复

为了保证进口精对苯二甲酸装置氧化反应器中钛制搅拌器的正常工作，对钛制搅拌器桨叶在运行中断裂脱落的原因进行了分析，并叙述了桨叶修理的方法和要求。经修理后的桨叶投入生产使用，达到了预期的目标。     

Morphological aspects of rubber fracture and wear

Morphology of carbon black (CB)‐filled rubber was studied with AFM and SEM and the classification of filler agglomerates, based on their internal structure and filler–matrix interactions, has been proposed. It varies according to the activity of CB and the kind of rubber. It has been shown that fracture of rubber starts either inside filler agglomerates (de‐cohesion) or in a filler–matrix interphase (de‐adhesion) initiating wear of the material. Microscopic observations correlate well with TGA and EPR data of wear debris collected during friction of rubber. The increase of thermal stability of CB and the appearance of additional spin signals, respectively, for elongated samples or debris, are proposed to be associated with de‐cohesion or de‐adhesion of the agglomerates. New approach to the fracture of rubber called “fatal agglomerate concept” is presented. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

小生境遗传算法AVOA反演

采用具有水平对称轴的横向各向同性(HTI)模型研究裂缝性油气藏,P波振幅随炮检距和方位角变化(AVOA),表现出较强的方位各向异性特征。本文基于Ruger提出的HTI介质模型的P波反射系数公式,利用由基准测线和另外两条与之呈45°、90°测线的P波反射系数的相对差异估算裂缝方位;同时引入小生境遗传算法,对基准测线和与之呈90°测线的P波反射系数差进行反演,得到了较高精度的纵、横波波速比和Thomsen各向异性参数。     

Bruchanalyse an Hohlgläsern

Failure analysis of hollow glasses The failure analysis is very important to clarify damages of hollow glasses. Damages of glass bottle through over pressure are very often linked with damages to persons. This is the reason why the causal research is from particular importance. Different surface characteristics of glass fragments as well as the fracture pattern give hints to the direction of the crack, the stress just before breakage and the reason of stress. A reconstruction of the bottle is a further helpful instrument for cause studies. The difference of the various characteristics of the surface will be explained. Further on there will be discussed different reasons and mechanism of fracture.     

Probabilistic cell modelling of cleavage fracture

Various aspects on probabilistic modelling of cleavage fracture are discussed. The investigation involves consideration of a unit cell with an explicitly modelled void. The results from this model are compared with results for the case when the void content is accounted for in the sense of a Gurson-Tvergaard law. It is found that explicit modelling of the void can give substantially different results for the fracture probability. The effect depends on the exponent in the assumed Weibull distribution, the threshold stress, the constraint conditions and the hardening of the material. This revised version was published online in August 2006 with corrections to the Cover Date.     

激光对望远系统损伤的研究

本文对激光光束通过望远系统后光束的变化进行了分析，并对６倍望远镜进行了激光损伤和破坏的实验研究，实验结果表明，激光对望远系统的损伤破坏主要是热效应所致，损伤破坏的情况与激光的能量，波长，脉冲宽度和望远系统的结构有关。     

Energetics of Plastic Deformation of Metastable Austenitic Stainless Steel

The change in the internal energy during uniaxial tensile deformation of austenitic stainless steels EN 1.4301 (AISI 304) and EN 1.4318 (AISI 301LN) was determined by measuring the extent of γ→α'‐martensite transformation and the temperature increase of the samples. From the results the fraction of the stored energy of cold work and the free energy change related to the strain‐induced γ→α'‐martensite transformation were determined. The fraction of stored energy varied around 0.4. With the metastable steel grades the free energy change related to the γ→α'‐martensite transformation was found to vary between ‐98 MJ/m³ and ‐206 MJ/m³ depending on the austenite stability of the steel. Furthermore, the magnitude of the mechanical driving force was estimated by comparing the results with the free energy change of thermally induced transformation.     

SiCf/O′-SiAlON composite: properties and oxidation retained properties

A composite of O′SiAlON (Si_2-xAl_xN_2-xO_1+x, with x 0.14) reinforced with 20 vol.% SiC monofilaments was fabricated by hot-pressing, at 1600°C, for 2 h under 34 MPa pressure. The mechanical and interfacial properties of the composites, as-fabricated as well as post-oxidized, were, investigated. The composite exhibited a significant improvement in ultimate flexure strength (640 MPa) and work of fracture (42 kJ m⁻²) compared with that (350 MPa and 1.8 kJ m⁻², respectively) of the monolithic material. These mechanical properties were slightly increased after the composite was heat treated for 24 h in air at 1200 and 1300°C. However, the composite exhibited a significant degradation in ultimate strength, while the work of fracture (WOF) remained unchanged after exposure in air at temperatures beyond 1400°C. The as-fabricated composite revealed a low interfacial shear strength (6.2 MPa) and a frictional sliding stress (3.2 MPa). After the composite was oxidized at elevated temperatures, the interfacial bonding and sliding stresses were reduced to noticeable extents, resulting from the degradation of the carbon coating layer of the SiC monofilaments.     

Influence of water and accelerated aging on the shear fracture properties of glass/epoxy composite

The degradation of interlaminar shear strength and shear fracture toughness of glass/epoxy composites due to uptake of distilled water and sea water has been studied. The composites were immersed in water for up to eight months at temperatures up to 70 °C. Unreinforced matrix resin samples were also immersed for periods up to 2 years. Sea water was absorbed less rapidly than distilled water. Weight gains below 1% did not influence the shear strength while higher weight gains reduced shear strength up to 25%. The loss in apparent interlaminar shear strength was uniquely related to specimen weight gain. Mode II fracture toughness, G _IIc, also decreased with increasing immersion time after an initial incubation period, but the accelerated tests were found to reduce G _IIc less than the room temperature tests at comparable weight gains.     

填充HDPE复合材料基体结晶形态的控制因素

本文以HDPE/玻璃微珠和HDPE/CaCO₃体系为研究模型,通过扫描电镜、红外光谱、偏光显微、小角激光散射和材料力学性能实验等方法考察了这两种体系的界面粘结性、填料含量、粒径及试样成型冷却速率等与其材料性能及基体结晶形态变化间的关系。实验结果表明;在复合材料试样成型过程中,因基体树脂冷却收缩而产生的界面应力可干扰基体中球晶的生长环境,应变诱导填料颗粒周围基体树脂的结晶,促使其表面伸展链晶体结构的形成,并由此而明显改变了复合材料的耐热性;复合材料的界面粘结性是产生这种应变诱导作用,并控制异相结晶的关键。