Effect of fretting amplitudes on fretting wear behavior of steel wires in coal mines

Given that fretting wear causes failure in steel wires, we carried out tangential fretting wear tests of steel wires on a self-made fretting wear test rig under contact loads of 9 and 29 N and fretting amplitudes ranging from 5 to 180 μm. We observed morphologies of fretted steel wire surfaces on an S-3000N scanning electron microscope in order to analyze fretting wear mecha-nisms. The results show that the fretting regime of steel wires transforms from partial slip regime into mixed fretting regime and gross slip regime with an increase in fretting amplitudes under a given contact load. In partial slip regime, the friction coefficient has a relatively low value. Four stages can be defined in mixed fretting and gross slip regimes. The fretting wear of steel wires in-creases obviously with increases in fretting amplitudes. Fretting scars present a typical morphology of annularity, showing slight damage in partial slip regime. However, wear clearly increases in mixed fretting regime where wear mechanism is a combination of plastic deformation, abrasive wear and oxidative wear. In gross slip regime, more severe degradation is present than in the other regimes. The main fretting wear mechanisms of steel wires are abrasive wear, surface fatigue and friction oxidation.     

GCr15轴承钢连铸过程中热物性参数的研究

借鉴前人实验数据,采用一定的数学方法,对轴承钢的热物性参数进行了研究.结果表明：GCr15轴承钢的液相线温度为1 465.7℃,固相线温度为1 328.4℃,零强度温度为1 380℃左右,零塑性温度为1 330℃左右;在固相区、液固两相区、液相区分别采用不同的公式进行处理,可使结果更加准确,还避免了奇异性.研究结果可为轴承钢连铸工艺有限元模拟提供基础.     

Intergranular oxidation of silicon in 20Cr-25Ni niobium-stabilized stainless steel at 1140–1230 K

The kinetics of intergranular oxidation of silicon in a 20Cr-25Ni Nb-stabilized stainless steel are reported, at temperatures in the range 1140–1230 K, in CO₂ at 40 bar pressure. The depth of attack increased parabolically with respect to time, with an activation energy of 335±30 kJ/mol. The mechanism of growth is discussed in terms of classical internal-oxidation theories, and an alternative explanation based on an available-space theory is developed. The internal oxidation rates in a number of different alloys are compared with diffusivities of metals in the base alloy. It is proposed that intergranular oxidation in the 20–25 Nb steel is controlled by the rate of outward diffusion of iron or chromium in the alloy.     

Effects of laser heat treatment on the fracture morphologies of X80 pipeline steel welded joints by stress corrosion

The surfaces of X80 pipeline steel welded joints were processed with a CO2 laser, and the effects of laser heat treatment （LHT） on H2S stress corrosion in the National Association of Corrosion Engineers （NACE） solution were analyzed by a slow strain rate test. The fracture morphologies and chemical components of corrosive products before and after LHT were analyzed by scanning electron microscopy and energy-dispersive spectroscopy, respectively, and the mechanism of LHT on stress corrosion cracking was discussed. Results showed that the fracture for welded joints was brittle in its original state, while it was transformed to a ductile fracture after LHT. The tendencies of hydrogen-induced corrosion were reduced, and the stress corrosion sensitivity index decreased from 35.2% to 25.3%, indicating that the stress corrosion resistance of X80 pipeline steel welded joints has been improved by LHT.     

马钢2号高炉中修后开炉达产操作实践

对马钢2号高炉中修后开炉达产操作实践进行了总结。通过制定科学的开炉方案,快速提高煤比、降低焦比,实现了顺利开炉、快速达产达效的目标。     

Immobilizing chromium in stainless steel slags with MnO addition

This work investigates the stabilizing impact of MnO on the leaching behavior of hazardous Cr-containing CaO-SiO₂-Al₂O₃-Cr₂O₃-MnO stainless steel slags after equilibrating at various elevated temperatures and evaluates the potential immobilization of Cr into a MnCr₂O₄ spinel phase from the existing Cr₂O₃ phase. The MnCr₂O₄ spinel phase was found to be an excellent Cr-stabilizer in stainless steel slags, where the leaching tendency of potentially hazardous Cr-related ions decreased with higher MnO content and lower equilibration temperatures within the range of 0 to 15 mass pct. and 1500 to 1300°C, respectively. Thermodynamic calculations by conducting the phase stability diagram also showed that the MnCr₂O₄ spinel phase was relatively stable and the Ca₃Si₂O₇ (Ca_3-xMn_xSi₂O₇) phase was relatively unstable compared with other crystal phases in acid extractant with pH value of 3.2. Combined with the scanning electron microscopy and X-ray powder diffraction results along with the thermodynamic calculations, the leached Cr-related ions was predominantly originating from the unstable amorphous glass phase.     

Wear mechanisms of PcBN tools when machining AISI 316L

This paper investigates the machinability of AISI 316L stainless steel without and with NMI treatment, when machined with three different PcBN tool grades: low cBN content (50% vol.), medium (65% vol.) and high (90% vol.). The NMI treatment consisted of resulfurized and Ca-treated steels with two different Si/Al ratio. The tool materials were evaluated in terms of tool life, showing the best performance for the medium cBN content grade. Results showed that the crater wear has a more significant effect on the tool performance than the standard wear criteria of maximum flank wear. The worn tools were examined using scanning electron microscopy (SEM), focused ion beam (FIB) and transmission electron microscopy (TEM). In most cases, the crater exhibited three distinct regions from the edge to the end of the contact zone: the plateau, middle crater, and the upper region. Plateau and crater region displayed tool protective layer (TPL), consisting mostly of Al, Si, Mg and Ca-oxides; and some dimples in the tool from preferential wear of cBN grains. In the upper region of the best performing material, a ~1.5 μm thick TPL of mostly MnCr₂O₄ spinel was found, a result of the transfer of Mn- and Cr-rich oxide NMIs found in this material or oxidation of workpiece material, during the machining process.     

High Temperature Oxidation of Steels in Air and CO2–O2 Atmosphere

Three kinds of hot rolled steel slabs, viz. high strength steel, bake hardened steel and low carbon steel, were oxidized isothermally between 1100 and 1250 °C for up to 2 hr in 1 atm of air and an 85%N₂–10%CO₂–5%O₂ gas mixture. The steels were oxidized in a similar fashion in both the atmospheres. The oxidation process followed an initial linear rate law, which then gradually transformed to a nearly parabolic rate law. Thick, porous and nonadherent scales formed rapidly, due to the high oxidation temperature. The scales formed consisted of Fe₂O₃,(Fe₂O₃+Fe₃O₄), (Fe₃O₄+Fe₂O₃ +FeO) and (FeO+Fe₃O₄) from the outer surface. The presence of supersaturated oxygen beneath the scale resulted in grain boundary oxidation and the formation of internal oxide precipitates.     

离心铸造高速钢轧辊铸造缺陷形成与控制技术研究

采用离心铸造方法制造高速钢轧辊工艺简单,操作方便,但易出现偏析、裂纹、气孔、缩孔及夹杂等缺陷,影响轧辊的力学性能和使用性能.采用稀土-钛复合变质处理改善合金的组织和性能,同时改进离心铸造工艺参数可以消除高速钢轧辊铸造缺陷,提高力学性能,改善使用效果.     

The influence of sulphate-reducing bacteria biofilm on the corrosion of stainless steel AISI 316

This work investigates microbially-influenced corrosion (MIC) of stainless steel AISI 316 by two sulphate-reducing bacteria, Desulfovibrio desulfuricans and a local marine isolate. The biofilm and pit morphology that developed with time were analyzed using atomic force microscopy (AFM). Electrochemical impedance spectroscopy (EIS) results were interpreted with an equivalent circuit to model the physicoelectric characteristics of the electrode/biofilm/solution interface. D. desulfuricans formed one biofilm layer on the metal surface, while the marine isolate formed two layers: a biofilm layer and a ferrous sulfide deposit layer. AFM images corroborated results from the EIS modeling which showed biofilm attachment and subsequent detachment over time.