基于NTC微珠状热敏电阻的稳态测量方法

稳态导热系数测量方法的原理和数学模型简单,但热源均温性要求高和测量时间长限制了稳态导热系数测量方法的实际应用。提出一种测量导热系数的新型微球法稳态热测量方法,建立对应的物理模型和试验方法。通过熔融共混法制备不同质量分数的石墨烯 石蜡复合相变材料,并采用微球法对不同质量分数的石墨烯 石蜡复合相变材料的导热系数进行测量。测量得到样品的导热系数分别为0.278 W/(m·K）(0%)、0.330 W/（m·K）(0.5%)、0.402 W/（m·K）(1%)、0.524 W/（m·K）(2%)、0.604 W/（m·K）(3%)、0.654 W/（m·K）(4%)和0.711 W/（m·K）(5%)。该方法具有微球体积小、热源均匀、测量快、样品制备简单等优点,可应用于实际工程中相变材料和液体的原位导热系数测量。     

不锈钢基厚膜PTC热敏电阻浆料的制备与性能研究

以二氧化钌和氧化铜的混合物为功能相制备出不锈钢基厚膜PTC热敏电阻浆料.研究了功能相与玻璃相的配比、功能相的粒度对厚膜电阻方阻及电阻温度系数(TCR)的影响规律.结果表明:固定浆料中玻璃相的成分与含量(30wt%),控制功能相中RuO2的比例(45.4wt%～88.9wt%)或功能相的粒度(0.30～1.0μm),可制得具有不同方阻(1.5～12.8Ω/□)和TCR(2100～2900×10-6/℃)的厚膜PTC热敏电阻.     

BaTiO_3基无铅PTC热敏电阻材料的制备与研究

利用传统陶瓷工艺制备了掺杂(Bi0.5Na0.5)TiO3(BNT),CaCO3和Mn(NO3)2的钛酸钡基无铅PTC陶瓷材料(Bi0.5Na0.5)xBa1–xTiO3-yCaCO3-0.000 2Mn(NO3)2(x=0.005,0.020,0.040,0.080;y=0,0.02,0.04,0.06,0.08),研究了BNT和CaCO3的掺杂量对所制陶瓷微观结构和导电特性的影响。结果表明:试样的晶格常数比c/a、居里温度tC以及室温电阻率ρ25均随着BNT掺杂量的增加而增大;CaCO3的加入能有效降低样品的室温电阻率。当x=0.080,y=0.06时所制得材料的性能最好,其室温电阻率为7×102.cm,居里温度高于150℃,升阻比(ρmax/ρmin)达到103。     

ZnLiFeO_3高温热敏厚膜材料的研究

ＺｎＬｉＦｅＯ３（ＺＬＦ）高温ＮＴＣ热敏厚膜材料，是以尖晶石结构的ＺｎＬｉＦｅＯ３导电陶瓷作厚膜浆料的导电相，以Ａｌ２Ｏ３瓷为基体，用厚膜工艺制成的。实验表明，在氮气中烧结的ＺＬＦ厚膜材料，室温方阻１０３Ω／□级，Ｂ值约１０００Ｋ。在高温５００～７００℃范围内，方阻降为１０２Ω／□级，Ｂ值仍小于１０００Ｋ。是一种很有前途的高温热敏材料。     

基于非晶锗热电阻的柔性MEMS流速传感器的设计与仿真

针对铂等常用金属热敏材料电阻温度系数(TCR)不高,导致热式MEMS流速传感器宽量程测量时功耗高的问题,设计了 一种基于非晶锗(a-Ge)薄膜热电阻的低功耗、宽量程柔性MEMS流速传感器.非晶锗热电阻材料具有较高的TCR系数(约为-0.02/K)和室温电阻率(5Ω·m),传感器在较低的工作温差和功耗下可获得宽量程的流速测量.阐述了该柔性MEMS流速传感器的设计结构、工作原理、3D有限元建模和热-流场仿真结果.利用聚酰亚胺衬底空腔膜上的四个非晶锗热电阻同时作为自加热热源和测温元件.四个非晶锗热电阻组成一个惠斯通电桥,同时结合热损失和热温差原理来实现宽量程流速测量和测向.仿真结果表明,惠斯通电桥采用恒电流供电只需120μA,使得非晶锗热阻的工作温度与环境温度之间的温差不高于6 K,就可对0～50 m/s范围内的流速进行测量,且功耗在1.368 mW以内.该柔性流速传感器易于采用MEMS技术批量制造,可贴于曲面应用,非常适于物联网等低功耗流速传感领域.     

Structural and electrical properties of NiMgxMn2−xO4 NTC thermistors prepared by using sol-gel derived powders

Structure and electrical properties of NiMg_xMn_2−xO₄ (where x = 0, 0.1, 0.2, 0.3 and 0.4) ceramics prepared by using sol-gel derived powders have been studied. A careful control of the synthesis process enables producing NiMn₂O₄ phase with spinel structure at a relatively low calcining temperature of 600 °C. All compositions showed a linear increase in ln ρ vs. 1/T over the measured temperature range, indicative of negative temperature coefficient (NTC) characteristics. As the concentration of Mg increased from 0.0 to 0.4, the ρ₂₅, B_25/85 stability constant and activation energy of NiMg_xMn_2−xO₄ thermistors increased from 4026 to 11,943 Ω cm, 3825-4144 K and 0.329-0.357 eV, respectively. In addition, the ΔR/R value first reduced fleetly from 0.78% to 0.32% and then decreased slowly to 0.12%.     

热敏电阻网络参数的计算方法

提出一种用改进的基因算法优化热敏电阻网络参数的方法，举例说明了该方法的应用，并将其与传统的优化方法进行比较，结果表明，该方法不要求预先假定接近最优解的初始参数值，且比传统优化方法有效。     

应用微机标定半导体热敏电阻及建立其数学模型

本文提出了一种方法，即在同一变化的温度场下，用一已知温度特性的高精度热敏电阻对一批未知温度特性的热敏电阻进行标定，由此得到其相关参数及数学模型，只需将参数写入智能测温仪器的存贮器，就可直接用其测温，而不需要改变硬件线路，克服了热敏电阻的非线性、离散性。     

BaCO_3和TiO_2的物化特性对PTC热敏电阻器性能的影响

探讨了ＢａＣＯ３与ＴｉＯ２的物化特性，诸如纯度、杂质含量、晶型、热特性、颗粒形状、粒度分布及平均粒径等对ＰＴＣ热敏电阻器性能的影响。并据此提出了ＢａＣＯ３与ＴｉＯ２的技术标准。     

激光合成新型线性NTC热敏电阻材料

本文采用CO2激光器作热源合成了Al2O3-WO3系热敏电阻材料,该材料具有负的温度系数,在一定温区内阻温特性呈线性变化。并对材料的导电机理进行了初步探讨。