Effects of an organic phosphorus nucleating agent on crystallization behaviors and mechanical properties of poly(propylene)

The effects of an organic phosphorus nucleating agent on the crystallization behavior and mechanical properties of poly(propylene) were investigated. As the concentration of nucleating agent increased from 0 to 0.8%, the tensile and flexural strengths of the nucleated poly(propylene) resin increased by 15%, the flexural modulus increased by 35%, the crystallization peak temperature increased by 10°C, and the nucleation density (calculated with the nonlinear Voltrra integral equation) increased by 10⁶ times. Mechanical properties increased with nucleation density. Linear equations between the mechanical properties and the logarithmic nucleation density were revealed. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 297–301, 2003     

On the observation of inductive high-frequency impedance behaviour during the electrodeposition of Au—Sn alloys

Inductive high-frequency impedance behaviour is often observed in metal electrodeposition systems. This behaviour is typically attributed to equipment limitations or non-idealities in the cell set-up and electrical connections. Such instrumental artefacts would nevertheless be relevant to a frequency range which is expected to be well above that in which inductive behaviour is in fact observed (down to a few tens of Hz). In this paper some results on an acidic Au—Sn electrodeposition system are reported. Electrochemical impedance and potentiostatic transients were measured. These results suggest that the high-frequency inductive behaviour may be related to metal nucleation processes. A correlation is proposed between the pseudo-inductive potentiostatic nucleation transients and the pseudo-inductive behaviour of the impedance spectra.     

Investigation into the effect of carboxylic acid monomer on particle nucleation and growth in emulsifier-free emulsion copolymerization of styrene-butadiene-acrylic acid

Latexes of carboxylated styrene-butadiene rubber were prepared via batch emulsion copolymerization with different amounts of acrylic acid in the absence of emulsifier. The effect of acid monomer was investigated in the particle formation and growth. It was observed that the amount of acrylic acid strongly affected the particle formation. The number of particles and thus polymerization rate increased with increasing of the acid content. There was no significant difference in the polymerization rate per particle in all experiments. The results show that in this case particle growth process is less dependent on the acrylic acid amount in comparison with its influence on nucleation stage and then particle number. Several parameters such as polymerization rate and number of latex particle per unit volume of the aqueous phase were calculated. Attempt was made to evaluate the average number of growing chain per particle. Also average particle diameter of the above carboxylated SBR latexes was obtained through some calculations from the direct measurement of average particle diameter in the swollen state by light scattering technique for the first time.     

Effect of DAG on milk fat TAG crystallization

The effect of milk fat and standard DAG on the crystallization behavior of milk fat TAG (MF-TAG) was investigated. When milk fat DAG were added to MF-TAG at the 0.1 wt% level, crystallization was delayed. Racemic purity was shown to be an important factor in the ability of DAG to influence TAG crystallization. Only sn-1,2 isomers of blends of MF-TAG with 0.1 wt% of the racemic mixtures of dipalmitin and diolein increased the activation free energy barrier to MF-TAG nucleation (ΔG _c ) and delayed the subsequent crystallization process by increasing the crystallization induction time (τ_SFC) determined from solid fat content-time measurements. Although crystallization kinetics were affected, the properties of the resulting network structures remained unchanged upon addition of milk fat minor components at the 0.1 wt% level     

高含量ZnO对Li2O-Al2O3-SiO2系统微晶玻璃晶化和性能的影响

采用差热分析、X-射线衍射分析和扫描电镜等分析手段研究了高含量ZnO对Li2O-Al2O3-SiO2系统微晶玻璃晶化和性能的影响.结果表明随着ZnO由9wt%增加到11wt%,该系统玻璃转变温度降低,晶化峰值温度降低,最佳成核温度从755±2℃降至745±2℃.通过计算,样品的晶化活化能E和晶化指数n分别为303±3(kJ/mol)、286±3(kJ/mol)、278±3(kJ/mol)和2.9±0.2、3.1±0.2、3.4±0.2.说明了ZnO在能降低玻璃熔融温度的同时能促进玻璃晶化,但ZnO含量达到11wt%时,其热膨胀系数发生突变.     

Role of anionic and nonionic surfactants on the control of particle size and latex colloidal stability in the seeded emulsion polymerization of butyl methacrylate

The evolution of the main colloidal parameters in the seeded starved‐feed semi‐continuous emulsion polymerization of butyl methacrylate (BMA) was investigated, with the main purpose of assessing the effectiveness of the semi‐empirical relationship S = K · S_S · ΔA/A_S as a tool to define the surfactant/monomer feed ratio (∝ K) best suited to achieve a target particle size. In particular, the effect of the type and amount of surfactant [i.e., anionic, sodium dodecyl sulfate (SDS), or nonionic, Brij 58P] added during the semi‐continuous stage was considered. Coagulum formation was never observed under the adopted experimental conditions. To detect the occurrence of secondary nucleation or particle aggregation, or both, the particle size and number of particles, the surface tension and the particle surface coverage ratio were correlated. The best results were obtained with SDS and 0.8 ≤ K ≤ 3. In fact, under the selected experimental conditions, only with SDS did the number of particles remain nearly constant throughout the polymerization at the value defined by the seed latex; the particle size distribution was highly monodisperse, and the final particle diameter closely matched the calculated one (～ 120 nm). The above semi‐empirical relationship based on the adjustable parameter K was validated by running test polymerizations aimed at lattices with well‐defined particle size. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3083–3094, 2006     

Nucleating activity of the quinacridone and phthalocyanine pigments in polypropylene crystallization

The nucleating ability of two organic pigments, quinacridone and phthalocyanine, in nonisothermal polypropylene (PP) crystallization was investigated. The investigations were carried out using DSC and polarizing microscopy. The efficiency of pigments in the nucleation process was determined in a simple test comparing the crystallization temperature of the PP‐containing pigments with respect to the pure polymer. Both pigments revealed good nucleating activity. In the presence of pigments the increment of the crystallization temperature and the increase of nucleation rate were observed. The nucleating efficiency of pigments was confirmed in investigations of the obtained structure. The nucleating activity of pigments was explained by their features fulfilling several requirements for good nucleating agents. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3957–3964, 2003     

Mullitization of Diphasic Aluminosilicate Gels

Recent studies have shown that the mullitization of diphasic aluminosilicate matrices comprising transitional alumina and amorphous silica occurs via a nucleation and growth process. Nucleation is preceded by a temperature-dependent incubation period. Following this incubation period, rapid nucleation of mullite occurs, producing about 1.8 × 10¹¹ nuclei/cm³, which remains constant throughout the rest of the transformation. Both incubation and mullite growth are thermally activated processes with apparent activation energies of 987 ± 63 and 1070 ± 200 kJ/mol, respectively. The growth rate of mullite grains under isothermal conditions is time dependent. An interpretation of these results is proposed on the basis of the nucleation and growth concepts of LaMer and Dinegar which supports the concept that the growth rate of mullite grains is controlled by the dissolution of transitional alumina into the amorphous matrix.     

Heterogeneous nucleation of organic vapours on a cold substrate

The heterogeneous phase transition of the organic vapours, cyclohexane and p-xylene, on a cold substrate was observed by cooling the substrate at a slow rate under reduced pressure conditions. Either organic vapour at a vapour pressure lower than 130 Pa formed directly solid crystals but p-xylene vapour at a higher vapour pressure formed liquid condensates with subsequent formation of solid crystals. The dependence of the critical supersaturation ratios on the critical temperatures and the physical properties of the organic vapours has been clarified by the equation derived on the basis of classical nucleation theory.     

我国硅锌矿结晶釉研究进展

本文介绍近十多年来我国硅锌矿结晶釉基础研究在以下几个方面的进展：（１）硅锌矿成核机制的研究；（２）硅锌矿的生长形态学研究；（３）硅锌矿的生长动力学研究。此外，还简要地探讨了今后科研工作的方向。