Mixed oxide supported hydrodesulfurization catalysts—a review

Support effects form important aspect of hydrodesulfurization (HDS) studies and mixed oxide supports received maximum attention in the last two decades. This review will focus attention on studies on mixed oxide supported Mo and W catalysts. For convenience of discussion, these are divided into Al₂O₃ containing mixed oxide supports, TiO₂ containing mixed oxide supports, ZrO₂ containing mixed oxide supports and other mixed oxide supports containing all the rest. TiO₂ containing mixed oxides received maximum attention, especially TiO₂–Al₂O₃ supported catalysts. A brief discussion about their prospects for application to ultradeep desulfurization is also included. An overview of the available literature with emphasis on research carried out in our laboratory form the contents of this publication.     

小剂量辐射对肿瘤细胞K_（562）及肿瘤病人天然杀伤细胞（NK）活性的影响

已知小剂量辐射可增强机体免疫功能。从对高本底地区的调查发现，该地区居民肿瘤死亡率及某些肿瘤发病率有所降低（１）。ＮＫ细胞能直接杀伤肿瘤细胞，在肿瘤免疫中起着重要的作用。本文观察小剂量辐射对肿瘤病人和正常人外周血淋巴细胞ＮＫ活性的相对效应以及对人红白血病细胞（Ｋ（５６２）细胞）的影响，以期从体外买验来探索较小剂量辐射对肿瘤治疗的影响     

测定钠中杂质的手动阻塞计的研究

文章介绍了测定钠中杂质浓度的手动阻塞计的原理、装置和实验结果。为了减少测量误差,我们研究了影响准确测定阻塞温度的因素,并且找到了减少测量误差的办法。在同样的杂质饱和温度下,该阻塞计测得的高、低阻塞温度所对应的杂质浓度差是很接近的。对氧其差值为1.03ppm;对氢为0.0763ppm。     

软X射线对血液有形成分表面电荷的影响——2、淋巴细胞和血小板膜电荷的变化

软X射线不仅能引起红细胞表面电荷的变化,同时也能导致淋巴细胞和血小板表面电荷下降,表现为照射后它们的电泳率下降。低剂量范围内,这种电荷的变化是暂时性的,照后4小时降到最低点,24小时后恢复到对照的水平。细胞电泳率的下降与辐射剂量相关。淋巴细胞是一个复杂的细胞群,正常状态下,按细胞在电场中泳动速度的快慢,可分为两个组分:快峰为T细胞,慢峰为B细胞。软X射线照射以后,T和B细胞的电泳率皆减慢,频数分布峰值下降,离散度加大。血小板成分单一,电泳率较一致。 从照射浓集的血小板再加回自身血浆中电泳率的下降较照射血浆再加到血小板中的电泳率下降大得多;受照射的血小板在磷酸缓冲液中电泳率下降较在血浆悬液中严重得多;2000 rad照后,悬浮于血浆中的血小板电泳率能恢复,而悬浮于磷酸缓冲液中则不能恢复,三个方面来看,血浆中可能存在抗辐射因子。超氧化物岐化酶能有效地预防血小板电泳率的下降,从而可阻止血小板的凝聚。     

Poly(butylene terephthalate)–clay nanocomposites prepared by melt intercalation: morphology and thermomechanical properties

Nanocomposites based on poly(butylene terephthalate) (PBT) and an organoclay (Cloisite 30B) were prepared by melt blending using a twin‐screw extruder. Two kinds of PBTs, ie PBT‐A and PBT‐B, with different inherent viscosities (η_inh), were used for this study (η_inh of PBT‐A and PBT‐B were 0.74 and 1.48, respectively). Dispersion of the clay layers in the PBT nanocomposites was characterized by using X‐ray diffraction (XRD) and transmission electron microscopy (TEM). Tensile and dynamic mechanical properties and non‐isothermal crystallization temperatures of the nanocomposites were also examined. Nanocomposites based on the higher‐viscosity PBT (PBT‐B) showed a higher degree of exfoliation of the clay and a higher reinforcing effect when compared to the composites based on the lower‐viscosity PBT (PBT‐A). The clay nanolayers dispersed in PBT matrices lead to increases in the non‐isothermal crystallization temperatures of the PBTs, with such increases being more significant for the PBT‐B nanocomposites than for the PBT‐A nanoocomposites. Copyright © 2004 Society of Chemical Industry     

Influence of ethyl methacrylate content on the volume‐phase transition of temperature‐sensitive poly[(N‐isopropylacrylamide)‐co‐(ethyl methacrylate)] microgels

A novel series of temperature‐sensitive poly[(N‐isopropylacrylamide)‐co‐(ethyl methacrylate)] (p(NIPAM‐co‐EMA)) microgels was prepared by the surfactant‐free radical polymerization of N‐isopropylacrylamide (NIPAM) with ethyl methacrylate (EMA). The shape, size dispersity and volume‐phase transition behavior of the microgels were investigated by transmission electron microscopy (TEM), ultraviolet–visible (UV–Vis) spectroscopy, dynamic light scattering (DLS) and differential scanning calorimetry (DSC). The transmission electron micrographs and DLS results showed that microgels with narrow distributions were prepared. It was shown from UV–Vis, DLS and DSC measurements that the volume‐phase transition temperature (VPTT) of the p(NIPAM‐co‐EMA) microgels decreased with increasing incorporation of EMA, but the temperature‐sensitivity was impaired when more EMA was incorporated, causing the volume‐phase transition of the microgels to become more continuous. It is noteworthy that incorporation of moderate amounts of EMA could not only lower the VPTT but also enhance the temperature‐sensitivity of the microgels. The reason for this phenomenon could be attributed to changes in the complicated interactions between the various molecules. Copyright © 2004 Society of Chemical Industry     

Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Low temperature synthesis of aluminium titanate by an aqueous sol-gel route

Formation of aluminium titanate (AT) has been achieved at low temperature through sol-gel process using boehmite and titanium hydroxide as precursors by controlling the particle size at nanoscale followed by in-situ peptisation. The formations of AT phase, particle size distributions, sintering and thermal expansion characteristics, and microstructural features have been reported. DTA and XRD analysis have been performed to confirm the formation of AT. A 94% relative density was obtained for aluminium titanate sintered at 1550 °C with controlled grain size in the range of 2-3 μm.     

Reactivity of steam in exhaust gas catalysis III. Steam and oxygen/steam conversions of propane on a Pd/Al2O3 catalyst

A 1% Pd catalyst (38% dispersion) was prepared by impregnating a γ-alumina with palladium acetylacetonate dissolved in acetone. The behaviour of this catalyst in oxidation and steam reforming (SR) of propane was investigated. Temperature-programmed reactions of C₃H₈ with O₂ or with O₂ + H₂O were carried out with different stoichiometric ratios S(S =[O₂]/5[C₃H₈]). The conversion profiles of C₃H₈ for the reaction carried out in substoichiometry of O₂ (S < 1) showed two discrete domains of conversion: oxidation at temperatures below 350°C and SR at temperatures above 350°C. The presence of steam in the inlet gases is not necessary for SR to occur: there is sufficient water produced in the oxidation to form H₂ and carbon oxides by this reaction. Contrary to what was observed with Pt, an apparent deactivation between 310 and 385°C could be observed with Pd in oxidation. This is due to a reduction of PdO_x into Pd⁰, which is much less active than the oxide in propane oxidation. Steam added to the reactants inhibits oxidation while it prevents the reduction of PdO_x into Pd⁰. Compared to Pt and to Rh, Pd has a higher thermal resistance: no deactivation occurred after treatment up to 700°C and limited deactivation after treatment up to 900°C, provided that the catalyst is maintained in an oxygen-rich atmosphere during the cooling.