该文以"牺牲"阳极溶解法在0.04mol／L(Bu4N)Br的乙醇和乙酰丙酮混合溶液中,电流强度控制在0.2A,电解镁片6h,制得纳米氧化物粉体MgO的前驱体Mg(OEt)2-x(acac)xo控制pH=8.0左右,将含有前驱体的电解液直接水解。水解产物经洗涤、干燥后于500℃煅烧2h,制得纳米MgOg粉体。采用红外(IR)、差热-热重分析(TG-DTA)、X-射线衍射(XRD)、电子透射技术(TEM)等手段对前驱体和纳米MgO进行了表征。结果表明:制备得到的纳米粉体呈单分散结构,平均粒径在12nm左右。用此种方法比较容易制得所需产物,是一种合成纳米氧化物的很有前途的方法。     

Characterisation and behaviour of Ti/TiO2/noble metal anodes

The morphology, composition and the electrical and electrochemical behaviour of the anodic microporous layer, prepared by the galvanostatic anodisation of Ti after sparking, followed by galvanostatic deposition of Pt or Ir have been investigated. These electrodes are proposed to function as dimensionally stable anodes (DSAs). For Ti/TiO₂/Pt electrodes, Pt is deposited within some of the micropores of the oxide film. In contrast, for Ti/TiO₂/Ir, the metal is deposited preferentially on the top surface. This difference is thought to result from the position of the metal deposition potential with respect to the flat band potential of n-TiO₂. Optical imaging of both types of DSA suggests that only a few sites on the surface are responsible for electron exchange at the DSA-electrolyte interface. C-AFM measurements of Ti/TiO₂/Pt samples subjected to long-term anodic polarisation, suggest that the Ti-noble metal contact is progressively insulated by thickening of the TiO₂ barrier layer, promoting passivation of the DSA. For Ir coated anodes, catalytic activity is directly related to the presence of Ir and to the stability of the catalytic oxide layer. Under Cu electrowinning conditions, the electrochemically formed hydrated Ir oxide was found to be catalytically less stable, than the iridium oxide film subjected to a heat treatment.     

如何提高预焙铝电解槽阳极质量

预焙阳极的质量已严重制约铝电解技术的发展，必须予以足够的重视．国外在提高阳极质量方面的有效措施，可以供国内阳极工厂技术改造及科研攻关借鉴．     

Electrochemical destruction of chlorophenoxy herbicides by anodic oxidation and electro-Fenton using a boron-doped diamond electrode

The degradation of herbicides 4-chlorophenoxyacetic acid (4-CPA), 4-chloro-2-methylphenoxyacetic acid (MCPA), 2,4-dichlorophenoxyacetic acid (2,4-D) and 2,4,5-trichlorophenoxyacetic acid (2,4,5-T) in aqueous medium of pH 3.0 has been comparatively studied by anodic oxidation and electro-Fenton using a boron-doped diamond (BDD) anode. All solutions are totally mineralized by electro-Fenton, even at low current, being the process more efficient with 1 mM Fe²⁺ as catalyst. This is due to the production of large amounts of oxidant hydroxyl radical (OH) on the BDD surface by water oxidation and from Fenton’s reaction between added Fe²⁺ and H₂O₂ electrogenerated at the O₂-diffusion cathode. The herbicide solutions are also completely depolluted by anodic oxidation. Although a quicker degradation is found at the first stages of electro-Fenton, similar times are required for achieving overall mineralization in both methods. The decay kinetics of all herbicides always follows a pseudo first-order reaction. Reversed-phase chromatography allows detecting 4-chlorophenol, 4-chloro-o-cresol, 2,4-dichlorophenol and 2,4,5-trichlorophenol as primary aromatic intermediates of 4-CPA, MCPA, 2,4-D and 2,4,5-T, respectively. Dechlorination of these products gives Cl⁻, which is slowly oxidized on BDD. Ion-exclusion chromatography reveals the presence of persistent oxalic acid in electro-Fenton by formation of Fe³⁺-oxalato complexes, which are slowly destroyed by OH adsorbed on BDD. In anodic oxidation, oxalic acid is mineralized practically at the same rate as generated.     

Binder effect on cycling performance of silicon/carbon composite anodes for lithium ion batteries

The cycling performance of a silicon/carbon composite anode has been significantly enhanced by using acrylic adhesive and modified acrylic adhesive as binder to fabricate the electrodes for lithium ion batteries. The capacity retentions of Si/C composite electrodes bound by acrylic adhesive and modified acrylic adhesive are 79% and 90% after 50 cycles, respectively. These two binders are electrochemically stable in the organic electrolyte in the working window. They also show larger adhesion strength between the coating and the Cu current collector as well as smaller solvent absorption in the electrolyte solvent than polyvinylidene fluoride (PVDF). Furthermore, sodium carboxyl methyl cellulose (CMC) plays an important role on improving the properties of acrylic adhesive, which increases the adhesive strength of acrylic adhesive and improves the activation of the electrodes.     

Advanced Sn/C composite anodes for lithium ion batteries

Metallic tin was deposited in fine particulate form on the surface of carbonaceous mesophase spherules (CMS) and in the pores of porous carbon by the decomposition and reduction of tin(II) 2-ethylhexanoate at 450 °C. The Sn/C composite powders obtained were used as anode materials for lithium ion cells. Electrochemical cycling tests of coin cells show that the dispersion of tin into the carbonaceous materials enhances the reversible capacity of the electrodes. The capacity retention at the 50th cycle is 91 % for Sn/CMS composite containing 22% tin, against 428 mAh g^–1 at the first cycle. With further increase in tin content, the capacity fade upon cycling is more rapid.     

锂离子电池层状LiMnO2正极材料的研究进展

论述了锂离子电池层状LiMnO2正极材料的结构、性能、制备、存在的问题和掺杂改性等方面的研究状况,讨论了今后层状LiMnO2的研究趋势.     

浅析预焙阳极配料控制

分析了粉料纯度及配料控制对炭阳极生产和炭阳极成品率的影响，结合中国铝业青海分公司的生产状况，从预焙阳极配料控制方面，就如何提高炭阳极成品率、保持生阳极生产工艺稳定进行论述。     

Electrochemical ferrate generation for waste water treatment using cast irons with high silicon contents

This paper deals with the electrochemical preparation of ferrate in 15 M NaOH media, with a view to treatment of waste waters. Grey cast irons with high silicon contents were shown to allow current yields in the range 20–40% depending on the applied current density, up to 34 mA cm^–2. Ferrate solutions with contents up to 0.08 M could be produced in a divided cell of simple design, and provided with flat or packed-bed electrodes. Deactivation of the anode surface was shown to be of moderate significance for hour-long runs. The ferrate produced was tested for treatment of industrial liquid wastes: coagulation efficiency of the suspended matter was comparable with that of an electrocoagulation process with sacrificial Al anodes. The potential of waste water treatment by addition of ferrate is discussed.     

延长预焙阳极使用周期的研究与应用

通过分析延长预焙阳极使用周期的途径、阳极消耗的影响因素以及预焙阳极生产工艺状况，确定通过提高预焙阳极的质量来延长其使用周期，研究制定并详细论述了改善预焙阳极质量的具体工艺改进措施。阐述了改进预焙阳极工艺后取得的效果、预焙阳极的质量状况以及为企业创造的经济效益和社会效益。