TiAl基合金表面改性对高温抗氧化性的影响

研究了渗碳处理ＴｉＡｌ基合金试样的高温氧化行为，发现渗碳处理可以在ＴｉＡｌ基合金试样表层形成致密的多层结构的渗碳层，并发生表层Ａｌ、Ｔｉ重新分配。致密的渗碳层具有良好的高温抗氧化性和高温热稳定性，同时，Ｔｉ、Ａｌ重新分配形成的富Ａｌ最外层也能进一步提高合金的抗氧化性。     

新型银铁电触头材料试验研究

对采用粉末冶金与化学热处理相结合的方法研制的电触头材料进行了理化性能、显微组织和抗氧化性能试验，探讨其机理及对性能的影响因素。试验表明：所研制的触头的理化性能基本达到了国标规定的相近触头的指标，其显微组织和抗氧比性能则优于国标规定。Ａ＿（ｃ４）加速模拟电寿命试验的结果证实该种触头材料应用前景良好。     

氧化铝/锌合金复合材料界面的SEM观察

利用挤压铸造制备氧化铝／锌合金复合材料，在扫描电镜（ＳＥＭ）上观察复合材料的界面。结果表明，在复合材料中纤维与基体间存在致密界面层，合金元素通过适当的化学反应可改善纤维与基体间的结合；在凝固过程中，纤维／基体界面上的硅在共晶体的共生生长过程中起了领先相作用，导致复合材料的共晶转变是由铝硅共晶转变和锌铝共晶转变两者组成。     

Reactivity of steam in exhaust gas catalysis III. Steam and oxygen/steam conversions of propane on a Pd/Al2O3 catalyst

A 1% Pd catalyst (38% dispersion) was prepared by impregnating a γ-alumina with palladium acetylacetonate dissolved in acetone. The behaviour of this catalyst in oxidation and steam reforming (SR) of propane was investigated. Temperature-programmed reactions of C₃H₈ with O₂ or with O₂ + H₂O were carried out with different stoichiometric ratios S(S =[O₂]/5[C₃H₈]). The conversion profiles of C₃H₈ for the reaction carried out in substoichiometry of O₂ (S < 1) showed two discrete domains of conversion: oxidation at temperatures below 350°C and SR at temperatures above 350°C. The presence of steam in the inlet gases is not necessary for SR to occur: there is sufficient water produced in the oxidation to form H₂ and carbon oxides by this reaction. Contrary to what was observed with Pt, an apparent deactivation between 310 and 385°C could be observed with Pd in oxidation. This is due to a reduction of PdO_x into Pd⁰, which is much less active than the oxide in propane oxidation. Steam added to the reactants inhibits oxidation while it prevents the reduction of PdO_x into Pd⁰. Compared to Pt and to Rh, Pd has a higher thermal resistance: no deactivation occurred after treatment up to 700°C and limited deactivation after treatment up to 900°C, provided that the catalyst is maintained in an oxygen-rich atmosphere during the cooling.     

铁钴钒软磁合金损耗谱的分形结构

研究了铁钴钒软磁合金的铁芯损耗，发现铁芯损耗谱具有分形结构。讨论了带材厚度和磁感应强度对分形维数Ｄｆ的影响。     

变形温度和变形程度对Ti－31合金性能和组织的影响

通过高温和室温拉伸试验，研究了变形温度和变形程度对Ｔｉ－３１合金板材性能和组织的影响。结果表明，合金在７５０～８５０℃的温度下变形５％～２０％空冷后，其室温机械性能均能达到材料的技术指标要求。并发现了材料在９００℃的临界变形区。     

电沉积Ni-W合金镀层的X射线光电子能谱分析

采用X射线光电子能谱（XPS）对电沉积Ni-W合金镀层表面膜进行了分析。研究结果表明，Ni-W合金镀层表面存在一层薄的氧化膜，而钨的氧化作用远大于镍，Ni-W合金镀层中W含量的提高对耐蚀性起决定作用。     

脉冲化学沉积非晶态Ni—P合金原子分布函数研究

采用Ｘ射线衍射分析技术，研究了脉冲化学镀非晶态Ｎｉ－Ｐ合金的原子分布和函数，得出其短程有序原子集团的尺度为０．７５４ｎｍ，约为熔体激冷法获得的非晶态Ｎｉ－Ｐ合金短程有序畴的１／２。并利用脉冲化学沉积非晶态合金的微机制择这一结果进行了解释。     

含羧基的聚乙烯醇胺肟螯合纤维吸附钯的研究

研究了含羧基的聚乙烯醇胺肟（ＰＶＡＡＯ－ＡＡｃ）螯合纤维对钯的吸附，讨论了ｐＨ、温度、浓度、吸附时间对吸附率及回收率的影响。确定了最佳吸附条件，吸附钯的纤维用５％硫脲＋０．１０ｍｏｌ／Ｌ硝酸溶液可以解吸。     

GH2027铁基高温合金的第二相研究

运用电子显微分析和波谱分析等方法对ＧＨ２０２７合金的第二相进行了研究，结果表明，合金晶界相主要是片状Ｍ６Ｃ和薄膜状Ｍ２３Ｃ６，经波纹图样测得其错配度约为３％，晶内Ｍ６Ｃ和Ｍ２３