Microstructure and thermal behavior of Sn-Zn-Ag solders

The microstructure and thermal behavior of the Sn-Zn-Ag solder were investigated for 8.73–9% Zn and 0–3.0% Ag. The scanning electron microscopy (SEM) analysis shows the Ag-Zn compound when the solder contains 0.1% Ag. X-ray diffraction (XRD) analysis results indicate that Ag₅Zn₈ and AgZn₃ become prominent when the Ag content is 0.3% and above. Meanwhile, the Zn-rich phase is refined, and the Zn orientations gradually diminish upon increase in Ag content. The morphology of the Ag-Zn compound varies from nodular to dendrite structure when the Ag content increases. The growth of the Ag-Zn compounds is accompanied by the diminishing of the eutectic structure of the Sn-9Zn solder. Differential scanning calorimetry (DSC) investigation reveals that the solidus temperature of these solders exists at around 198°C. A single, sharp exothermic peak was found for the solders with Ag content less than 0.5%. Liquidus temperatures were identified with the DSC analysis to vary from 206°C to 215°C when the Ag content ranges from 1.0% to 3.0%     

高温稀土永磁Sm2(Co,Cu,Fe,Zr)17 的制备和性能

制备了高温稀土永磁材料Sm(Coba1Fe0．26Cu0．05Zr0．026)7．0，研究了磁性能与工艺条件的关系．结果表明：提高烧结温度可使材料的Br和(BH)max增大，但是使Hci降低；适当提高真空预烧温度，可使材料在较低烧结温度下致密化，具有较高的Hci和(BH)max和温度稳定性．真空预烧温度过高使性能的急剧降低，其主要原因是Sm的析出．在最佳工艺条件下材料的磁性能参数分别为：Br1．08T3Hci2286kA／m，Hcb932kA／m，(BH)max220．8kJ／m^3；β20-200℃为-0．19％／℃．     

The Problem of Estimating the Uncertainty of the Fixed Point Temperature Due to the Presence of Impurities

The main problems in estimating the uncertainty due to the presence of impurities in the material: the absence in the documents of a unique definition of the quantity being measured – the fixed point temperature, the lack of agreed methods of realizing the fixed points and the insufficient justification of the equations used for the estimate, are analyzed. The results of a measurement of the melting point of gallium are presented, which differ in the conditions in which they were realized – with one and two liquid-solid interfaces and different solidification conditions, are presented. The reasons for the considerable difference between the values of the temperatures obtained in these experiments are discussed.     

Results of familiarization of and prospects for a procedure for the burning of wastes in a vortical fluidized bed

Problems that have arisen during tune-up of the production line for the thermal processing of solid household waste by the method of burning in a vortical fluidized bed (principally, a new technology for Russia), and means of their solution are presented. Investigative studies are cited. __________ Translated from élektricheskie Stantsii, No. 6, pp. 20–26, August, 2006.     

Study on ASTM E399 and ASTM E1921 standards

Costs of ASTM E399 and ASTM E1921 tests, which were developed to determine the fracture toughness (K_Ic) and the ductile–brittle transition temperature of ferritic steels, respectively, are considered high and the procedures are also very complicated. In this study, a method, which is more cost‐effective and easier to carry out, is proposed.     

Temperature–stress–strain trajectory modelling during thermo-mechanical fatigue

The isothermal strain‐life approach is the most commonly used approach for determining fatigue damage, particularly when yielding occurs. Computationally it is extremely fast and generally requires elastic finite element analyses only. Therefore, it has been adapted for variable temperatures. Local temperature—stress–strain behaviour is modelled with an operator of the Prandtl type. The hysteresis loops are supposed to be stabilized and no creep is considered. The consequences of reversal point filtering are analysed. The approach is finally compared to several thermo‐mechanical fatigue tests and the Skelton model.     

Phase Composition of Oxide Scales during Reheating in Hot Rolling of Low Carbon Steel

Low carbon steel was oxidized over the temperature range 1000‐1250°C in O₂‐CO₂‐H₂O‐N₂, O₂‐H₂O‐N₂, and O₂‐CO₂‐N₂ gas mixtures. Oxidation times were 12‐120 min. and the scales were 50‐2000 μm thick. The variations of these parameters were chosen to elucidate the phase composition of oxide scales under conditions similar to those of reheating furnaces in hot strip mills, using either thin slab casting or conventional casting and rolling technology. Two types of scales have been observed which are influenced by the furnace atmosphere, oxidation time, and temperature. The first type is a crystalline scale with an irregular outer surface, composed mostly of wustite (FeO), and a negligible amount of magnetite (Fe₃O₄). The second type is the classical three‐layer scale, composed of wustite (FeO), magnetite (Fe₃O₄), and hematite (Fe₂O₃). In general, the experiments showed that an increase in oxidation time decreased the percentage of wustite while the percentages of magnetite and hematite increased. A rise in oxygen concentration in the gas mixture increased the percentages of magnetite and hematite, confirming earlier experimental findings. In water vapour‐free atmospheres O₂‐CO₂‐N₂, the oxide scales had a low percentage of wustite, and high percentage of magnetite and hematite. Carbon dioxide showed a small influence at 1100°C, and a negligible one at 1250°C.     